Improved Mechanical, Thermal, and Hydrophobic Properties of PLA Modified with Alkoxysilanes by Reactive Extrusion Process

Torres, Elena (författare)
AITEX Textile Industry Research Association, Spain
Gaona, Aide (författare)
AITEX Textile Industry Research Association, Spain
García-Bosch, Nadia (författare)
AITEX Textile Industry Research Association, Spain
visa fler...
Muñoz, Miguel (författare)
AITEX Textile Industry Research Association, Spain
Fombuena, Vicent (författare)
Universitat Politècnica de València, Spain
Moriana Torro, Rosana (författare)
RISE,Material- och ytdesign
Vallés-Lluch, Ana (författare)
Universitat Politècnica de València, Spain
visa färre...
 (creator_code:org_t)
MDPI, 2021
2021
Engelska.
Ingår i: Polymers. - : MDPI. - 2073-4360 .- 2073-4360. ; 13:15
  • Tidskriftsartikel (refereegranskat)
Abstract Ämnesord
Stäng  
  • An eco-friendly strategy for the modification of polylactic acid (PLA) surface properties, using a solvent-free process, is reported. Reactive extrusion (REX) allowed the formation of new covalent bonds between functional molecules and the PLA polymeric matrix, enhancing its mechanical properties and modifying surface hydrophobicity. To this end, the PLA backbone was modified using two alkoxysilanes, phenyltriethoxysilane and N-octyltriethoxysilane. The reactive extrusion process was carried out under mild conditions, using melting temperatures between 150 and 180 °C, 300 rpm as screw speed, and a feeding rate of 3 kg·h−1. To complete the study, flat tapes of neat and functionalized PLA were obtained through monofilament melt extrusion to quantify the enhancement of mechanical properties and hydrophobicity. The results verified that PLA modified with 3 wt% of N-octyltriethoxysilane improves mechanical and thermal properties, reaching Young’s modulus values of 4.8 GPa, and PLA hydrophobic behavior, with values of water contact angle shifting from 68.6° to 82.2°.

Ämnesord

ENGINEERING AND TECHNOLOGY  -- Industrial Biotechnology -- Bio Materials (hsv//eng)
TEKNIK OCH TEKNOLOGIER  -- Industriell bioteknik -- Biomaterial (hsv//swe)
TEKNIK OCH TEKNOLOGIER  -- Industriell bioteknik (hsv//swe)
ENGINEERING AND TECHNOLOGY  -- Industrial Biotechnology (hsv//eng)

Nyckelord

PLA
biopolymers
alkoxysilanes
hydrophobicity
grafting
monofilament melt extrusion
thermal properties
reactive extrusion

Publikations- och innehållstyp

ref (ämneskategori)
art (ämneskategori)

Hitta via bibliotek

  • Polymers (Sök värdpublikationen i LIBRIS)

Till lärosätets databas

Sök utanför SwePub

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy