The effects of voids in quasi-static indentation of resin-infused reinforced polymers

Sisodia, Sanjay (författare)
Uppsala universitet,Tillämpad mekanik,GKN Aerosp, SE-46181 Trollhattan, Sweden
Bull, D. J. (författare)
Univ Southampton, Fac Engn & Environm, Mat Res Grp, Southampton, Hants, England
George, A. R. (författare)
Brigham Young Univ, Mfg Engn Technol, Provo, UT 84602 USA
visa fler...
Gamstedt, E. Kristofer (författare)
Uppsala universitet,Tillämpad mekanik
Mavrogordato, M. N. (författare)
Univ Southampton, Fac Engn & Environm, Mat Res Grp, Southampton, Hants, England
Fullwood, D. T. (författare)
Brigham Young Univ, Mfg Engn Technol, Provo, UT 84602 USA
Spearing, S. M. (författare)
Univ Southampton, Fac Engn & Environm, Mat Res Grp, Southampton, Hants, England
visa färre...
 (creator_code:org_t)
2019
2019
Engelska.
Ingår i: Journal of composite materials. - 0021-9983 .- 1530-793X. ; 53:28-30, s. 4399-4410
  • Tidskriftsartikel (refereegranskat)
Abstract Ämnesord
Stäng  
  • The focus of this study is the influence of voids on the damage behaviour in quasi-static loading of resin-infused carbon fibre-reinforced polymers. Experimental results are presented for quasi-static loading in combination with high-resolution tomographic imaging and statistical analysis (homology of pores or voids and induced cracks). Three distinct mechanisms were observed to control delamination growth in the presence of sharp and blunt voids. Delamination cracks interact with the supporting yarns, especially in combination with air pockets trapped in the resin in the form of long, sharp voids. This resulted in crack growth that coalesces with delamination cracks from neighbouring yarn-voids during increased out-of-plane load-displacement, with almost no presence of intralaminar transverse cracks. This highlights the benefits and drawbacks of the supporting yarn during out-of-plane loading.

Ämnesord

ENGINEERING AND TECHNOLOGY  -- Mechanical Engineering -- Applied Mechanics (hsv//eng)
TEKNIK OCH TEKNOLOGIER  -- Maskinteknik -- Teknisk mekanik (hsv//swe)
TEKNIK OCH TEKNOLOGIER  -- Maskinteknik (hsv//swe)
ENGINEERING AND TECHNOLOGY  -- Mechanical Engineering (hsv//eng)

Nyckelord

Resin transfer moulding
CT analysis
porosity
damage mechanics

Publikations- och innehållstyp

ref (ämneskategori)
art (ämneskategori)

Hitta via bibliotek

Till lärosätets databas

Sök utanför SwePub

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy