Sökning: onr:"swepub:oai:research.chalmers.se:10af1c76-a3c3-41c8-a8d4-9c4c90402453" > Effect of Nitrogen ...

  • Calcagno, Giulio,1990Chalmers University of Technology,Chalmers tekniska högskola (författare)

Effect of Nitrogen Doping on the Performance of Mesoporous CMK-8 Carbon Anodes for Li-Ion Batteries

  • Artikel/kapitelEngelska2020

Förlag, utgivningsår, omfång ...

  • 2020
  • electronicrdacarrier

Nummerbeteckningar

  • LIBRIS-ID:oai:research.chalmers.se:10af1c76-a3c3-41c8-a8d4-9c4c90402453
  • https://research.chalmers.se/publication/520564URI
  • https://doi.org/10.3390/en13194998DOI

Kompletterande språkuppgifter

  • Språk:engelska
  • Sammanfattning på:engelska

Ingår i deldatabas

Klassifikation

  • Ämneskategori:ref swepub-contenttype
  • Ämneskategori:art swepub-publicationtype

Anmärkningar

  • Designing carbonaceous materials with heightened attention to the structural properties such as porosity, and to the functionalization of the surface, is a growing topic in the lithium-ion batteries (LIBs) field. Using a mesoporous silica KIT-6 hard template, mesoporous carbons belonging to the OMCs (ordered mesoporous carbons) family, namely 3D cubic CMK-8 and N-CMK-8 were synthesized and thoroughly structurally characterized. XPS analysis confirmed the successful introduction of nitrogen, highlighting the nature of the different nitrogen atoms incorporated in the structure. The work aims at evaluating the electrochemical performance of N-doped ordered mesoporous carbons as an anode in LIBs, underlining the effect of the nitrogen functionalization. The N-CMK-8 electrode reveals higher reversible capacity, better cycling stability, and rate capability, as compared to the CMK-8 electrode. Coupling the 3D channel network with the functional N-doping increased the reversible capacity to similar to 1000 mAh center dot g(-1) for the N-CMK-8 from similar to 450 mAh center dot g(-1) for the undoped CMK-8 electrode. A full Li-ion cell was built using N-CMK-8 as an anode, commercial LiFePO4, a cathode, and LP30 commercial electrolyte, showing stable performance for 100 cycles. The combination of nitrogen functionalization and ordered porosity is promising for the development of high performing functional anodes.

Ämnesord och genrebeteckningar

Biuppslag (personer, institutioner, konferenser, titlar ...)

  • Agostini, Marco,1987Chalmers University of Technology,Chalmers tekniska högskola(Swepub:cth)agostini (författare)
  • Xiong, Shizhao,1985Chalmers University of Technology,Chalmers tekniska högskola(Swepub:cth)xiongs (författare)
  • Matic, Aleksandar,1968Chalmers University of Technology,Chalmers tekniska högskola(Swepub:cth)matic (författare)
  • Palmqvist, Anders,1966Chalmers University of Technology,Chalmers tekniska högskola(Swepub:cth)adde (författare)
  • Cavallo, Carmen,1986University of Oslo, Norway,Chalmers University of Technology,Chalmers tekniska högskola(Swepub:cth)ccarmen (författare)
  • Chalmers University of TechnologyChalmers tekniska högskola (creator_code:org_t)

Sammanhörande titlar

  • Ingår i:Energies13:191996-1073

Internetlänk

Hitta via bibliotek

  • Energies (Sök värdpublikationen i LIBRIS)

Till lärosätets databas

Sök utanför SwePub

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy