| 1. |
- Broberg, Patrik, 1983-
(author)
-
Towards Automation of Non-Destructive Testing of Welds
- 2011
-
Licentiate thesis (other academic/artistic)abstract
- All welding processes can give rise to defects that will weaken the joint and can lead to failure of the welded structure. Because of this, non-destructive testing (NDT) of welds have become increasingly important to ensure the structural integrity when the material becomes thinner and stronger and welds become smaller; all to reduce weight in order to save material and reduce emissions due to lighter constructions.Several NDT methods exists for testing welds and they all have their advantages and disadvantages when it comes to the types and sizes of defects that are detectable, but also in the ability to automate the method. Several methods were compared using common weld defects to determine which method or methods were best suited for automated NDT of welds. The methods compared were radiography, phased array ultrasound, eddy current, thermography and shearography. Phased array ultrasound was deemed most suitable for detecting the weld defects used in the comparison and for automation and was therefore chosen to be used in the continuation of this work. Thermography was shown to be useful for detecting surface defects; something not easily detected using ultrasound. A combination of these techniques will be able to find most weld defects of interest.Automation of NDT can be split into two separate areas; mechanisation of the testing and automation of the analysis, both presenting their own difficulties. The problem of mechanising the testing has been solved for simple geometries but for more general welds it will require a more advance system using an industrial robot or similar. Automation of the analysis of phased array ultrasound data consists of detection, sizing, positioning and classification of defects. There are several problems to solve before a completely automatic analysis can be made, including positioning of the data, improving signal quality, segmenting the images and classifying the defects. As a step on the way towards positioning of the data, and thereby easing the analysis, the phase of the signal was studied. It was shown that the phase can be used for finding corners in the image and will also improve the ability to position the corner as compared to using the amplitude of the signal. Further work will have to be done to improve the signal in order to reliably analyse the data automatically.
|
|
| 2. |
- Hagqvist, Petter, 1986-
(author)
-
Instrumentation and estimation for high temperature control
- 2013
-
Licentiate thesis (other academic/artistic)abstract
- Within a variety of industrially relevant high temperature production processes such as welding, heat treatment and metal deposition, the quality of the manufactured component is largely affected by how well parameters can be controlled during processing. These parameters might be, in the case of metal deposition, power input, material feed, or a parameter which is common for all of the aforementioned processes: material temperature. The ability to correctly measure, or in other ways estimate process parameters is vital in order to successfully control high temperature processes such as above 700 degrees Celsius. In this work, instrumentation and estimation solutions adapted to high temperature control are proposed and implemented with a focus on the laser metal wire deposition process. Special attention is given to temperature measurements on specimens with varying emissivity as commonly found in high temperature processes. A calibration procedure for a single-wavelength pyrometer is also presented together with a general discussion on limitations of such a system for measurands with varying emissivity. A new method for non-contact emissivity compensated temperature estimations using a spectrometer is presented. Simulations and industrially relevant experiments have been carried out validating the method. The theoretical framework for the developed method will be further investigated in the future together with additional experimental validation. In addition to temperature measurements, a method for real-time process control of laser metal wire deposition has been developed and implemented with good results. This control scheme estimates and controls the tool-to-workpiece distance based on resistance measurements. Such measurements allow for placement of instruments outside of the processing chamber and easy integration into existing equipment. Future work will be directed towards incorporation of resistance measurements into an iterative learning control scheme. Also, improvement on the resistance-distance model and further investigation into suitable signal processing methods for the resistance signal will be pursued.
|
|