- Dou, S.X., et al.
(författare)
-
Improvement of critical current density in the Bi-Pb-Sr-Ca-Cu-O system through hot isostatic pressing
- 1990
-
Ingår i: Physica. C, Superconductivity. - 0921-4534 .- 1873-2143. ; 167:5-6, s. 525-528
-
Tidskriftsartikel (refereegranskat)abstract
- The effects of hot isostatic pressing (HIPing) on densification and the superconducting properties of the Bi-Pb-Sr-Ca-O system were investigated. A relative density up to 95% and a critical current density greater than 1100 A/cm2 at 77 K were achieved through HIPing at 650°C for 2 h under 200 MPa argon. Under these conditions, the product gave a value of Jc four times that without HIPing. To was unaffected by HIPing for samples encapsulated with a combination of glass and silver tubes. However, To was suppressed from 103 K to 86 K for samples encapsulated with stainless steel and silver tubes while Jc increased from 260 A/ cm2 to 1086 A/cm2 during HIPing, indicating that the weak links were significantly improved. A new minor phase, having a composition of Bi/Pb/Sr/Ca/Cu=0.58/2.8/3.0/2.1/1.1, was observed in HIPed samples but its effect on Jc is not clear
|
|
6. |
- Dou, S.X., et al.
(författare)
-
Microstructure and flux pinning in superconducting Bi-Pb-Sr-Ca-Cu-O wires
- 1990
-
Ingår i: Physica. C, Superconductivity. - 0921-4534 .- 1873-2143. ; 172:1-2, s. 63-70
-
Tidskriftsartikel (refereegranskat)abstract
- The critical current density (Jc) of Ag-clad Bi-Pb-Sr-Ca-Cu-O wire has been measured to be 1.2×104 A/cm2 at 77 K in zero field. The high Jc is attributed to a combination of elimination of the poisoning effect of Ag on superconductivity, grain alignment, and enhancement of flux pinning. Jc-H dependence was significantly improved in the Ag-clad tape, which has a Jc of 1.0×103 A /cm2 at 77 K and 4000 Oe, while the Jc of the sintered pellet drops two orders of magnitude at only 100 Oe. A pronounced anisotropy in Jc under high magnetic field is attributed to the grain alignment. Planar defects, such as heavy stacking faults parallel to the a-b plane in the rolled tape, are considered to be effective pinning centres.
|
|