| 1. |
- Jiang, Linhai, et al.
(författare)
-
Controlled Synthesis of CeO2/Graphene Nanocomposites with Highly Enhanced Optical and Catalytic Properties
- 2012
-
Ingår i: The Journal of Physical Chemistry C. - : American Chemical Society (ACS). - 1932-7447 .- 1932-7455. ; 116:21, s. 11741-11745
-
Tidskriftsartikel (refereegranskat)abstract
- In this paper, CeO2 nanocubes with the (200)-terminated surface/graphene sheet composites have been prepared successfully by a simple hydrothermal method. It is found that the CeO2 nanocubes with high crystallinity and specific exposed surface are well dispersed on well-exfoliated graphene surface. The (200)-terminated surface/graphene sheet composites modified electrode showed much higher sensitivity and excellent selectivity in its catalytic performance compared to a CeO2 nanoparticle-modified electrode. The photoluminescence intensity of the CeO2 anchored on graphene is about 30 times higher than that of pristine CeO2 crystals in air. The higher oxygen vacancy concentration in CeO2 is supposed to be an important cause for the higher photoluminescence and better electrochemical catalytic performance observed in the (200)-terminated surface/graphene sheet composites. Such ingenious design of supported well-dispersed catalysts in nanostructured ceria catalysts, synthesized in one step with an exposed high-activity surface, is important for technical applications and theoretical investigations.
|
|
| 2. |
- Liu, Dedi, et al.
(författare)
-
In situ Raman and photoluminescence study on pressure-induced phase transition in C60 nanotubes
- 2012
-
Ingår i: Journal of Raman Spectroscopy. - : Wiley. - 0377-0486 .- 1097-4555. ; 43:6, s. 737-740
-
Tidskriftsartikel (refereegranskat)abstract
- Single crystalline C60 nanotubes having face-centered-cubic structure with diameters in the nanometer range were synthesized by a solution method. In situ Raman and photoluminescence spectroscopy under high pressure were employed to study the structural stabilities and transitions of the pristine C60 nanotubes. A phase transition, probably because of the orientational ordering of C60 molecules, from face-centered-cubic structure to simple cubic structure occurred at the pressure between 1.46 and 2.26 GPa. At above 20.41 GPa, the Raman spectrum became very diffuse and lost its fine structure in all wavenumber regions, and only two broad and asymmetry peaks initially centered at 1469 and 1570cm-1 were observed, indicating an occurrence of amorphization. This amorphous phase remained to be reversible until 31.1 GPa, and it became irreversible to the ambient pressure after the pressure cycle of 34.3 GPa was applied.
|
|