| 1. |
- Hou, Yuanyuan, et al.
(författare)
-
Comparative study of pressure-induced polymerization of C60 nanorods and single crystals
- 2007
-
Ingår i: Journal of Physics Condensed Matter. - Bristol : Institute of Physics. - 0953-8984 .- 1361-648X. ; 19:42, s. 425207-
-
Tidskriftsartikel (refereegranskat)abstract
- In this paper, we report a comparative study of pressure-induced polymerization in C60 nanorods and bulk single crystals, treated simultaneously under various pressures and temperatures in the same experiment. For both materials, orthorhombic, tetragonal and rhombohedral phases have been produced under high pressure and high temperature. The structures have been identified and compared between the two sample types by Raman and photoluminescence spectroscopy. There are differences between the Raman and photoluminescence spectra from the two types of materials for all polymeric phases, but especially for the tetragonal phase. From the comparison between nanorods and bulk samples, we tentatively assign photoluminescence peaks for various polymeric phases.
|
|
| 2. |
- Liu, Dedi, et al.
(författare)
-
In situ Raman and photoluminescence study on pressure-induced phase transition in C60 nanotubes
- 2012
-
Ingår i: Journal of Raman Spectroscopy. - : Wiley. - 0377-0486 .- 1097-4555. ; 43:6, s. 737-740
-
Tidskriftsartikel (refereegranskat)abstract
- Single crystalline C60 nanotubes having face-centered-cubic structure with diameters in the nanometer range were synthesized by a solution method. In situ Raman and photoluminescence spectroscopy under high pressure were employed to study the structural stabilities and transitions of the pristine C60 nanotubes. A phase transition, probably because of the orientational ordering of C60 molecules, from face-centered-cubic structure to simple cubic structure occurred at the pressure between 1.46 and 2.26 GPa. At above 20.41 GPa, the Raman spectrum became very diffuse and lost its fine structure in all wavenumber regions, and only two broad and asymmetry peaks initially centered at 1469 and 1570cm-1 were observed, indicating an occurrence of amorphization. This amorphous phase remained to be reversible until 31.1 GPa, and it became irreversible to the ambient pressure after the pressure cycle of 34.3 GPa was applied.
|
|
| 3. |
- Liu, Dedi, et al.
(författare)
-
Synthesis and solid-state studies of self-assembled C60 microtubes
- 2011
-
Ingår i: Diamond and Related Materials, vol. 20 issue 2. - : Elsevier BV. ; , s. 178-182
-
Konferensbidrag (refereegranskat)abstract
- C60 microtubes were fabricated by a modified solution evaporation method, evaporating a solution of C60 in toluene in an atmosphere of m-xylene at room temperature. The C60 microtubes have outer diameters ranging from 2 to 8 μm. IR spectra, TG analysis and X-ray diffraction showed a solvated structure for the as-grown C60 microtubes. Through a gentle heat-treatment in vacuum, pure C60 microtubes with single crystalline fcc structure were obtained after the elimination of solvents. It is suggested that the C60 microtubes form through self-assembly from several individual C60 nanorods.
|
|