| 1. |
- Linderbäck, Paula, et al.
(författare)
-
Sol-gel derived titania coating with immobilized bisphosphonate enhances screw fixation in rat tibia.
- 2010
-
Ingår i: Journal of biomedical materials research. Part A. - : Wiley. - 1552-4965 .- 1549-3296. ; 94:2, s. 389-95
-
Tidskriftsartikel (refereegranskat)abstract
- A variety of surface modifications have been tested for the enhancement of screw fixation in bone, and locally delivered anti-osteoporosis drugs such as bisphosphonates (BP) are then of interest. In this in vivo study, the impact of surface immobilized BP was compared with systemic BP delivery and screws with no BP. After due in vitro characterization, differently treated stainless steel (SS) screws were divided into four groups with 10 rats each. Three of the groups received screws coated with sol-gel derived TiO(2) and calcium phosphate (SS+TiO(2)+CaP). One of these had no further treatment, one had alendronate (BP) adsorbed to calcium phosphate mineral, and one received systemic BP treatment. The fourth group received uncoated SS screws and no BP (control). The screw pullout force was measured after 4 weeks of implantation in rat tibiae. The immobilized amount and release rate of alendronate could be controlled by different immersion times. The SS+TiO(2)+CaP coating did not increase the pullout force compared to SS alone. Surface delivered alendronate enhanced the pullout force by 93% [p = 0.000; 95% Confidence Interval (CI): 67-118%] compared to SS, and by 39% (p = 0.044; 95% CI: 7-71%) compared to systemic alendronate delivery. Both surface immobilized and systemically delivered alendronate improved implant fixation. Also, locally delivered, that is, surface immobilized alendronate showed a better fixation than systemically delivered. Using sol-gel derived TiO(2) as a platform, it is possible to administer controllable amounts of a variety of BPs.
|
|
| 2. |
- Linderbäck, Paula, et al.
(författare)
-
The effect of heat- or ultra violet ozone-treatment of titanium on complement deposition from human blood plasma.
- 2010
-
Ingår i: Biomaterials. - : Elsevier BV. - 1878-5905 .- 0142-9612. ; 31:18, s. 4795-801
-
Tidskriftsartikel (refereegranskat)abstract
- Titanium (Ti) is a well known metallic biomaterial extensively used in dental, orthopaedic-, and occasionally also in blood contacting applications. It integrates well to bone and soft tissues, and is shown upon blood plasma contact to activate the intrinsic pathway of coagulation and bind complement factor 3b. The material properties depend largely on those of the nm-thick dense layer of TiO(2) that becomes rapidly formed upon contact with air and water. The spontaneously formed amorphous Ti-oxide has a pzc approximately 5-6 and its water solubility is at the order of 1-2 micromolar. It is often subjected to chemical- and heat treatments in order to increase the anatase- and rutile crystallinity, to modify the surface topography and to decrease the water solubility. In this work, we prepared sol-gel derived titanium and smooth PVD titanium surfaces, and analysed their oxide and protein deposition properties in human blood plasma before and after annealing at 100-500 degrees C or upon UVO-treatment for up to 96 hours. The blood plasma results show that complement deposition vanished irreversibly after heat treatment at 250-300 degrees C for 30 minutes or after UVO exposure for 24 hours or longer. XPS and infrared spectroscopy indicated change of surface water/hydroxyl binding upon the heat- and UVO treatments, and increased Ti oxidation. XRD analysis confirmed an increased crystallinity and both control (untreated) and annealed smooth titanium displayed low XRD-signals indicating some nanocrystallinity, with predominantly anatase phase. The current results show that the behaviour of titanium dioxide in blood contact can be controlled through relatively simple means, such as mild heating and illumination in UV-light, which both likely irreversibly change the stoichiometry and structure of the outmost layers of titanium dioxide and its OH/H(2)O binding characteristics.
|
|