| 1. |
- Hou, Yuanyuan, et al.
(författare)
-
Comparative study of pressure-induced polymerization of C60 nanorods and single crystals
- 2007
-
Ingår i: Journal of Physics Condensed Matter. - Bristol : Institute of Physics. - 0953-8984 .- 1361-648X. ; 19:42, s. 425207-
-
Tidskriftsartikel (refereegranskat)abstract
- In this paper, we report a comparative study of pressure-induced polymerization in C60 nanorods and bulk single crystals, treated simultaneously under various pressures and temperatures in the same experiment. For both materials, orthorhombic, tetragonal and rhombohedral phases have been produced under high pressure and high temperature. The structures have been identified and compared between the two sample types by Raman and photoluminescence spectroscopy. There are differences between the Raman and photoluminescence spectra from the two types of materials for all polymeric phases, but especially for the tetragonal phase. From the comparison between nanorods and bulk samples, we tentatively assign photoluminescence peaks for various polymeric phases.
|
|
| 2. |
- Zou, Yonggang, et al.
(författare)
-
Raman spectroscopy study of carbon nanotube peapods excited by near-IR laser under high pressure
- 2007
-
Ingår i: Physical Review B. - 0163-1829. ; 76:19, s. 195417-
-
Tidskriftsartikel (refereegranskat)abstract
- A resonant Raman spectroscopy study has been carried out under high pressure, using a diamond anvil cell,on carbon nanotube peapods (C60@SWNT) synthesized in high yield in our laboratory. The Raman signal wasexcited by a near IR laser (830 nm) to avoid photopolymerization of C60 and thus obtain the intrinsic vibrationalinformation on the C60 molecules in the nanotubes. It is found that the surrounding tubes create aneffective pressure on the encapsulated C60 due to tube-fullerene interactions, resulting in a shift of the intrinsicAg(2) vibrational mode to 1474 cm−1 at ambient pressure. High pressure Raman spectroscopy indicates that(C60)2 dimers form near 1 GPa, and that a further polymerization of C60 occurs near 23 GPa, creating linearchains of covalently linked C60 molecules in the tubes.
|
|
| 3. |
- Wang, Lin, et al.
(författare)
-
Synthesis and high pressure induced amorphization of C60 nanosheets
- 2007
-
Ingår i: Applied Physics Letters. - : AIP Publishing. - 0003-6951 .- 1077-3118. ; 91:10, s. 103112-
-
Tidskriftsartikel (refereegranskat)abstract
- C-60 nanosheets with thicknesses in the nanometer range were synthesized by a simple method. Compared to bulk C-60, the lattice of the nanosheets is expanded by about 0.4%. In situ Raman spectroscopy and energy-dispersive x-ray diffraction under high pressures have been employed to study the structure of the nanosheets. The studies indicate that the bulk modulus of the C-60 nanosheets is significantly larger than that of bulk C-60. The C-60 cages in nanosheets can persist at pressures over 30 GPa, 3 GPa higher than for bulk C-60. These results suggest that C-60 crystals in even small size will be a potential candidate of superhard materials.
|
|