- Bender, P., et al.
(författare)
-
Relating Magnetic Properties and High Hyperthermia Performance of Iron Oxide Nanoflowers
- 2018
-
Ingår i: Journal of Physical Chemistry C. - : American Chemical Society (ACS). - 1932-7447 .- 1932-7455. ; 122:5, s. 3068-3077
-
Tidskriftsartikel (refereegranskat)abstract
- We investigated, in depth, the interrelations among structure, magnetic properties, relaxation dynamics and magnetic hyperthermia performance of magnetic nanoflowers. The nanoflowers are about 39 nm in size, and consist of densely packed iron oxide cores. They display a remanent magnetization, which we explain by the exchange coupling between the cores, but we observe indications for internal spin disorder. By polarized small-angle neutron scattering, we unambiguously confirm that, on average, the nanoflowers are preferentially magnetized along one direction. The extracted discrete relaxation time distribution of the colloidally dispersed particles indicates the presence of three distinct relaxation contributions. We can explain the two slower processes by Brownian and classical Néel relaxation, respectively. The additionally observed very fast relaxation contributions are attributed by us to the relaxation of disordered spins within the nanoflowers. Finally, we show that the intrinsic loss power (ILP, magnetic hyperthermia performance) of the nanoflowers measured in colloidal dispersion at high frequency is comparatively large and independent of the viscosity of the surrounding medium. This concurs with our assumption that the observed relaxation in the high frequency range is primarily a result of internal spin relaxation, and possibly connected to the disordered spins within the individual nanoflowers.
|
|
| 2. |
- Gavilán, Helena, et al.
(författare)
-
Colloidal Flower-Shaped Iron Oxide Nanoparticles : Synthesis Strategies and Coatings
- 2017
-
Ingår i: Particle & particle systems characterization. - : Wiley. - 0934-0866 .- 1521-4117. ; 34:7
-
Tidskriftsartikel (refereegranskat)abstract
- The assembly of magnetic cores into regular structures may notably influence the properties displayed by a magnetic colloid. Here, key synthesis parameters driving the self-assembly process capable of organizing colloidal magnetic cores into highly regular and reproducible multi-core nanoparticles are determined. In addition, a self-consistent picture that explains the collective magnetic properties exhibited by these complex assemblies is achieved through structural, colloidal, and magnetic means. For this purpose, different strategies to obtain flower-shaped iron oxide assemblies in the size range 25–100 nm are examined. The routes are based on the partial oxidation of Fe(OH)2, polyol-mediated synthesis or the reduction of iron acetylacetonate. The nanoparticles are functionalized either with dextran, citric acid, or alternatively embedded in polystyrene and their long-term stability is assessed. The core size is measured, calculated, and modeled using both structural and magnetic means, while the Debye model and multi-core extended model are used to study interparticle interactions. This is the first step toward standardized protocols of synthesis and characterization of flower-shaped nanoparticles.
|
|
| 3. |
- Jonasson, Christian, et al.
(författare)
-
Modelling the effect of different core sizes and magnetic interactions inside magnetic nanoparticles on hyperthermia performance
- 2019
-
Ingår i: Journal of Magnetism and Magnetic Materials. - : Elsevier BV. - 0304-8853 .- 1873-4766. ; 477, s. 198-202
-
Tidskriftsartikel (refereegranskat)abstract
- We present experimental intrinsic loss power (ILP) values, measured at an excitation frequency of 1 MHz and at relatively low field amplitudes of 3.4–9.9 kA/m, as a function of the mean core diameter, for selected magnetic nanoparticles (MNPs). The mean core sizes ranged from ca. 8 nm to 31 nm. Transmission electron microscopy indicated that those with smaller core sizes (less than ca. 22 nm) were single-core MNPs, while those with larger core sizes (ca. 29 nm to 31 nm) were multi-core MNPs. The ILP data showed a peak at core sizes of ca. 20 nm. We show here that this behaviour correlates well with the predicted ILP values obtained using either a non-interacting Debye model, or via dynamic Monte-Carlo simulations, the latter including core-core magnetic interactions for the multi-core particles. This alignment of the models is a consequence of the low field amplitudes used. We also present interesting results showing that the core-core interactions affect the ILP value differently depending on the mean core size.
|
|