- Walia, Mandeep Singh, 1987, et al.
(författare)
-
Temperatures and wear at railway tread braking: Field experiments and simulation
- 2018
-
Ingår i: Proceedings of the 11th International Conference on Contact Mechanics and Wear of Rail/wheel Systems, CM 2018. - 9789461869630 ; , s. 1029-1036
-
Konferensbidrag (refereegranskat)abstract
- Field tests were carried out for a commuter train in revenue service equipped with cast iron and organic composite brake blocks. Temperatures for wheel tread, wheel web and brake blocks and wear of wheel treads and brake blocks were recorded. The measured temperatures are used for calibrating a thermal model for assessment of wheel and block temperatures. In addition, the results from thermal and wear simulations are presented. Comparisons are made between measured and simulated temperatures and wear. The wear of the cast iron brake blocks estimated using simulated temperatures and a temperature-dependent wear model calibrated from pin-on-disc experiments is in agreement with measured wear results from field tests.
|
|
| 2. |
- Walia, Mandeep Singh, 1987, et al.
(författare)
-
Thermomechanical capacity of wheel treads at stop braking: A parametric study
- 2018
-
Ingår i: International Journal of Fatigue. - : Elsevier BV. - 0142-1123. ; 113, s. 407-415
-
Tidskriftsartikel (refereegranskat)abstract
- During tread braking, the treads of railway wheels are subjected to a complex loading due to combined rolling contact and thermally induced stresses. In revenue traffic the running mode of the train varies and the operational parameters will influence the life of the wheels. To prevent excessive damage, it is therefore important to understand at which operational conditions wheel damage becomes unacceptable. The current study aims to find limits for tread braking with respect to the influence of thermal stresses on rolling contact fatigue (RCF) of the wheel tread when subjected to repeated stop braking. A parametric study, using 3D FE simulations and involving operational parameters such as axle load, maximum vehicle speed, deceleration, brake block material and initial wheel temperature, is carried out for a new wheel with an S-shaped web. Additional analyses investigate impact from wheel geometry by studying a wheel with a straight web and a wheel with a thin (worn) rim. The effects of simultaneous thermal loading from wheel–block frictional contact during braking and mechanical loading, due to the traversing wheel–rail rolling contact, are studied in an uncoupled thermomechanical analysis. In the wheel–rail contact simulations, frictional rolling contact stress distributions induced by braking are accounted for. Interfacial shear stresses and partial slip are also included in the model. A temperature-dependent elastoplastic model is utilised to characterise changes in material behaviour during braking. In the vicinity of the wheel tread, damage evolutions for the studied brake load cases are evaluated. The results show that high tread temperatures, in particular temperatures above 450 °C, have a strong detrimental influence on the RCF formation and, hence, also on the thermomechanical capacity of the wheel. On the other hand, it is found that for braking temperatures between 300 °C and 375 °C, the fatigue resistance is increased due to strain hardening effects. In addition, the parametric study points towards actual braking load cases that can give such temperatures in terms of initial speeds, axle loads, etcetera. Specifically, the study shows that the train axle load, that controls the normal wheel–rail contact force, has a substantial impact on the life of the wheel treads. Wheels having straight webs and S-shaped wheel web exhibit the same fatigue life of their treads, whereas a reduction in wheel rim thickness promotes ratchetting due to increased flexural stresses from the mechanical wheel–rail contact loading.
|
|