Diffusion bonding of CMSX-4 to UDIMET 720 using PVD-coated interfaces and HIP

Larker, Rickard (författare)
Luleå tekniska universitet
Ockborn, J. (författare)
Materials Technology, Volvo Aero Corporation, Trollhattan, S-461 81, Sweden
Selling, B. (författare)
Materials Technology, Volvo Aero Corporation, Trollhattan, S-461 81, Sweden
 (creator_code:org_t)
1999-07-01
1999
Engelska.
Ingår i: Journal of engineering for gas turbines and power. - : ASME International. - 0742-4795 .- 1528-8919. ; 121:3, s. 489-493
  • Tidskriftsartikel (refereegranskat)
Abstract Ämnesord
Stäng  
  • There is an increasing interest in development of manufacturing methods for Dual Property BLISKs, consisting of creep resistant airfoils and fatigue resistant disks bonded together by a durable joint. Optimum heat treatments are, however, very different for creep resistant single crystal CMSX-4 and fatigue resistant polycrystalline Udimet 720 selected in this study, but fortunately the first aging treatment for CMSX-4 (1140°C, 2-6 h, AC) is similar to the partial solution treatment of U 720 HS2 (1115°C, 4 h, OQ). Based on this, diffusion bonding was performed by HIP at 1120°C and 200 MPa argon pressure for 4 h, followed by cooling to 400°C. Subsequently, a shortened Udimet 720 HS2 two-step aging treatment was adopted by heating to 650°C for 6 h followed by cooling to 400°C, heating to 760°C for 2 h, and finally cooling to R.T. under remaining HIP pressure. Plasma etching followed by thin (80 nm) PVD coating with either nickel or titanium were used to clean and protect the polished surfaces before joining. The selection of coatings was governed by the possibility to reduce oxidized nickel by flushing with hydrogen at 330°C during evacuation of the HIP capsules, and by the large solubility of oxygen in titanium. Hot tensile testing was performed at 750°C on both joined and reference materials subjected to the modified heat treatment. Initially solution treated Udimet 720 and CMSX-4 comprised the reference materials. The testing showed that joints with Ni-PVD coatings were almost as strong as Udimet 720 (although with very limited elongation), while the joints with Ti-PVD coatings were weaker.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Annan materialteknik (hsv//swe)
ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Other Materials Engineering (hsv//eng)

Nyckelord

Material Mechanics
Materialmekanik

Publikations- och innehållstyp

ref (ämneskategori)
art (ämneskategori)

Hitta via bibliotek

Till lärosätets databas

Hitta mer i SwePub

Av författaren/redakt...
Larker, Rickard
Ockborn, J.
Selling, B.
Om ämnet
TEKNIK OCH TEKNOLOGIER
TEKNIK OCH TEKNO ...
och Materialteknik
och Annan materialte ...
Artiklar i publikationen
Journal of engin ...
Av lärosätet
Luleå tekniska universitet

Sök utanför SwePub

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy