Precipitate evolution in the early stages of ageing in Inconel 718 investigated using small-angle x-ray scattering

Fisk, Martin (författare)
Malmö högskola,Teknik och samhälle (TS),Materials Science and Applied Mathematics, Malmö University
Andersson, Joel Håkan, 1981 (författare)
Högskolan Väst,Avd för tillverkningsprocesser,GKN Aerospace Engine Systems, Trollhättan,PTW
du Rietz, Rickard (författare)
Malmö högskola,Teknik och samhälle (TS),Materials Science and Applied Mathematics, Malmö University
visa fler...
Haas, Sylvio (författare)
Lund University,Lunds universitet,MAX IV-laboratoriet,MAX IV Laboratory,MAX IV Laboratory, Lund University
Hall, Stephen (författare)
Lund University,Lunds universitet,Hållfasthetslära,Institutionen för byggvetenskaper,Institutioner vid LTH,Lunds Tekniska Högskola,Solid Mechanics,Department of Construction Sciences,Departments at LTH,Faculty of Engineering, LTH,European Spallation Source (ESS),Division of Solid Mechanics, Lund University
visa färre...
 (creator_code:org_t)
Elsevier BV, 2014
2014
Engelska.
Ingår i: Materials Science & Engineering: A. - : Elsevier BV. - 1873-4936 .- 0921-5093. ; 612, s. 202-207
  • Tidskriftsartikel (refereegranskat)
Abstract Ämnesord
Stäng  
  • Microstructural evolution during the early stages of ageing (less than one hour) in a Ni-Cr-Fe based superalloy Inconel 718 (IN718) has been investigated using Small-Angle X-ray Scattering (SAXS). The effects of precipitate kinetics on the precipitate size distribution are compared indirectly with SAXS measurements by using Vickers microhardness data. The microhardness increased after 4 min of ageing at a temperature of 760 degrees C, although the recorded SAXS data did not reveal the precipitate size distribution. This indicates that the precipitates had not evolved enough to be detected, but still a small number of precipitates increased the yield strength. After ageing the alloy for the shortest period for which data were available, 8 min, clear evidence of precipitates could be found from the SAXS data, showing that the gamma '' - precipitates are about 6 nm in width and 3 nm in height. (C) 2014 Elsevier B.V. All rights reserved.

Ämnesord

NATURVETENSKAP  -- Fysik (hsv//swe)
NATURAL SCIENCES  -- Physical Sciences (hsv//eng)
TEKNIK OCH TEKNOLOGIER  -- Maskinteknik (hsv//swe)
ENGINEERING AND TECHNOLOGY  -- Mechanical Engineering (hsv//eng)
TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

Nyckelord

Nucleation
SAXS
Vickers microhardness
Nickel based superalloys
Age
hardening
IN718
Vickers microhardness
Manufacturing and materials engineering

Publikations- och innehållstyp

art (ämneskategori)
ref (ämneskategori)

Hitta via bibliotek

Till lärosätets databas

Sök utanför SwePub

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy