| 1. |
- Rech, S, et al.
(författare)
-
Cold-spray deposition of Ti2AlC coatings
- 2013
-
Ingår i: Vacuum. - : Elsevier. - 0042-207X .- 1879-2715. ; 94, s. 69-73
-
Tidskriftsartikel (refereegranskat)abstract
- Ti2AlC coatings have been fabricated by cold-spray deposition. The microstructure evolution as a function of basic spray parameters temperature and pressure onto AA6060 aluminium alloy and 1.0037 steel substrates has been studied. Adherent and dense 50–80 μm thick Ti2AlC coatings were deposited on soft AA6060 substrates under gas temperature and pressure of 600 °C and 3.4 MPa, respectively, whilst comparable results were obtained on harder 1.0037 steel by using higher temperature (800 °C) and pressure (3.9 MPa).
|
|
| 2. |
- Lauridsen, Jonas, et al.
(författare)
-
Effects of A-elements (A=Si, Ge or Sn) on the structure and electrical contact properties of Ti-A-C-Ag nanocomposites
- 2012
-
Ingår i: Thin Solid Films. - : Elsevier BV. - 0040-6090 .- 1879-2731. ; 520:16, s. 5128-5136
-
Tidskriftsartikel (refereegranskat)abstract
- Ti-A-C-Ag (A is Si, Ge or Sn) nanocomposite coatings have been deposited by dc magnetron sputtering in an ultra high vacuum chamber. Electron microscopy, energy-dispersive x-ray spectroscopy, x-ray photoelectron spectroscopy, and x-ray diffraction show that all coatings contain nanocrystalline TiC and Ag grains in a matrix of mainly amorphous C. A C/Ti ratio above unity yields a homogenous distribution of Ag with a reduced grain size. From a chemical point of view. the addition of Ge and Sn to the Ti-C-Ag system should increase the conductivity of the coatings since the formation of more metallic phases than Si. We demonstrate that Si can be replaced with Ge and Sn and still yield a homogeneous distribution of Ag. The incorporation of Ge and Sn to the Ti-C-Ag system results in elemental precipitation and intermetallic phases, respectively. This gives improved electrical properties compared to Ti-Si-C-Ag coatings, and a contact resistance at loads of similar to 1 N against an Au probe (radius of 0.7 mm) that is comparable to that of Ag.
|
|
| 3. |
- Lauridsen, Jonas, et al.
(författare)
-
Microstructural and Chemical Analysis of AgI Coatings Used as a Solid Lubricant in Electrical Sliding Contacts
- 2012
-
Ingår i: Tribology letters. - : Springer Verlag (Germany). - 1023-8883 .- 1573-2711. ; 46:2, s. 187-193
-
Tidskriftsartikel (refereegranskat)abstract
- AgI coatings have been deposited by electroplating on Ag-plated Cu coupons. Electron microscopy shows that the coatings consist of weakly agglomerated AgI grains. X-ray diffraction, differential scanning calorimetry, thermogravimetry, and mass spectrometry show that the AgI exhibits a reversible transformation from hexagonal to cubic phase at 150 A degrees C. AgI starts to decompose at 150 A degrees C with an accelerating rate up to the AgI melting temperature (555 A degrees C), where a complex-bonded hydroxide evaporates. Ag pin-on-disk testing shows that the iodine addition to Ag decreases the friction coefficient from 1.2 to similar to 0.4. The contact resistance between AgI and Ag becomes less than 100 mu I (c) after similar to 500 operations as the AgI deagglomerates, and Ag is exposed on the surface and remains low during at least 10,000 reciprocating operations. This makes AgI suitable as a solid lubricant in electrical contacts.
|
|
| 4. |
- Lauridsen, Jonas, et al.
(författare)
-
Microstructure evolution of Ti-Si-C-Ag nanocomposite coatings deposited by DC magnetron sputtering
- 2010
-
Ingår i: Acta Materialia. - : Elsevier Ltd.. - 1359-6454 .- 1873-2453. ; 58:20, s. 6592-6599
-
Tidskriftsartikel (refereegranskat)abstract
- Nanocomposite coatings consisting of Ag and TiCx (x < 1) crystallites in a matrix of amorphous SiC were deposited by high-rate magnetron sputtering from Ti-Si-C-Ag compound targets. Different target compositions were used to achieve coatings with a Si content of similar to 13 at.%, while varying the C/Ti ratio and Ag content. Electron microscopy, helium ion microscopy, X-ray photoelectron spectroscopy and X-ray diffraction were employed to trace Ag segregation during deposition and possible decomposition of amorphous SiC. Eutectic interaction between Ag and Si is observed, and the Ag forms threading grains which coarsen with increased coating thickness. The coatings can be tailored for conductivity horizontally or vertically by controlling the shape and distribution of the Ag precipitates. Coatings were fabricated with hardness in the range 10-18 GPa and resistivity in the range 77-142 mu Omega cm.
|
|
| 5. |
- Singh, Niraj Kumar, et al.
(författare)
-
Electron-phonon coupling and quantum correction to topological magnetoconductivity in Bi2GeTe4
- 2022
-
Ingår i: Physical Review B. - : AMER PHYSICAL SOC. - 2469-9950 .- 2469-9969. ; 105:4
-
Tidskriftsartikel (refereegranskat)abstract
- We report structure, vibrational properties, and weak antilocalization-induced quantum correction to magnetoconductivity in single-crystal Bi2GeTe4. Surface band-structure calculations show a single Dirac cone corresponding to topological surface states in Bi2GeTe4. An estimated phase coherence length, lΦ ~ to 143 nm and prefactor α~-1.54 from Hikami-Larkin-Nagaoka fitting of magnetoconductivity describe the quantum correction to conductivity. An anomalous temperature dependence of A1g Raman modes confirms enhanced electron-phonon interactions. Our results establish that electrons of the topological state can interact with the phonons involving the vibrations of Bi-Te in Bi2GeTe4.
|
|
| 6. |
- Alijan Farzad Lahiji, Faezeh, et al.
(författare)
-
Growth and optical properties of NiO thin films deposited by pulsed dc reactive magnetron sputtering
- 2023
-
Ingår i: Journal of Vacuum Science & Technology. A. Vacuum, Surfaces, and Films. - : A V S AMER INST PHYSICS. - 0734-2101 .- 1520-8559. ; 41:6
-
Tidskriftsartikel (refereegranskat)abstract
- NiO thin films with varied oxygen contents are grown on Si(100) and c-Al2O3 at a substrate temperature of 300 degrees C using pulsed dc reactive magnetron sputtering. We characterize the structure and optical properties of NiO changes as functions of the oxygen content. NiO with the cubic structure, single phase, and predominant orientation along (111) is found on both substrates. X-ray diffraction and pole figure analysis further show that NiO on the Si(100) substrate exhibits fiber-textured growth, while twin domain epitaxy was achieved on c-Al2O3, with NiO(111) k Al2O3(0001) and NiO[1 (1) over bar0]k Al2O3[10 (1) over bar0] or NiO[(1) over bar 10]k Al2O3[2 (1) over bar(1) over bar0] epitaxial relationship. The oxygen content in NiO films did not have a significant effect on the refractive index, extinction coefficient, and absorption coefficient. This suggests that the optical properties of NiO films remained unaffected by changes in the oxygen content.
|
|
| 7. |
- Azina, Clio, et al.
(författare)
-
Deposition of MAX phase-containing thin films from a (Ti,Zr)(2)AlC compound target
- 2021
-
Ingår i: Applied Surface Science. - : Elsevier. - 0169-4332 .- 1873-5584. ; 551
-
Tidskriftsartikel (refereegranskat)abstract
- This work reports on sputter depositions carried out from a compound (Ti,Zr)(2)AlC target on Al2O3(0 0 0 1) substrates at temperatures ranging between 500 and 900 degrees C. Short deposition times yielded 30-40 nm-thick Al-containing (Ti,Zr)C films, whereas longer depositions yielded thicker films up to 90 nm which contained (Ti,Zr)C and intermetallics. At 900 degrees C, the longer depositions led to films that also consisted of solid solution MAX phases. Detailed transmission electron microscopy showed that both (Ti,Zr)(2)AlC and (Ti,Zr)(3)AlC2 solid solution MAX phases were formed. Moreover, this work discusses the growth mechanism of the thicker films, which started with the formation of the mixed (Ti,Zr)C carbide, followed by the nucleation and growth of aluminides, eventually leading to solid state diffusion of Al within the carbide, at the highest temperature (900 degrees C) to form the MAX phases.
|
|
| 8. |
- Ding, Haoming, et al.
(författare)
-
Chemical scissor-mediated structural editing of layered transition metal carbides
- 2023
-
Ingår i: Science. - : AMER ASSOC ADVANCEMENT SCIENCE. - 0036-8075 .- 1095-9203. ; 379:6637, s. 1130-1135
-
Tidskriftsartikel (refereegranskat)abstract
- Intercalated layered materials offer distinctive properties and serve as precursors for important two-dimensional (2D) materials. However, intercalation of non-van der Waals structures, which can expand the family of 2D materials, is difficult. We report a structural editing protocol for layered carbides (MAX phases) and their 2D derivatives (MXenes). Gap-opening and species-intercalating stages were respectively mediated by chemical scissors and intercalants, which created a large family of MAX phases with unconventional elements and structures, as well as MXenes with versatile terminals. The removal of terminals in MXenes with metal scissors and then the stitching of 2D carbide nanosheets with atom intercalation leads to the reconstruction of MAX phases and a family of metal-intercalated 2D carbides, both of which may drive advances in fields ranging from energy to printed electronics.
|
|
| 9. |
- Du, Hao, et al.
(författare)
-
Corundum-structured AlCrNbTi oxide film grown using high-energy early-arriving ion irradiation in high-power impulse magnetron sputtering
- 2023
-
Ingår i: Scripta Materialia. - : Elsevier. - 1359-6462 .- 1872-8456. ; 234
-
Tidskriftsartikel (refereegranskat)abstract
- Multicomponent or high-entropy oxide films are of interest due to their remarkable structure and properties. Here, energetic ion irradiation is utilized for controlling the phase formation and structure of AlCrNbTi oxide at growth temperature of 500 degrees C. The ion acceleration is achieved by using a high-power impulse magnetron sputtering (HiPIMS) discharge, accompanied by a 10 & mu;s-long synchronized substrate bias (Usync), to minimize the surface charging effect and accelerate early-arriving ions, mainly Al+, O+, Ar2+, and Al2+. By increasing the magnitude of Usync from-100 V to-500 V, the film structure changes from amorphous to single-phase corundum, followed by the formation of high-number-density stacking faults (or nanotwins) at Usync =-500 V. This approach paves the way to tailor the high-temperature-phase and defect formation of oxide films at low growth temperature, with prospects for use in protective-coating and dielectric applications.
|
|
| 10. |
- Eklund, Per, et al.
(författare)
-
Layered ternary M(n+1)AX(n) phases and their 2D derivative MXene: an overview from a thin-film perspective
- 2017
-
Ingår i: Journal of Physics D. - : IOP PUBLISHING LTD. - 0022-3727 .- 1361-6463. ; 50:11
-
Forskningsöversikt (refereegranskat)abstract
- Inherently and artificially layered materials are commonly investigated both for fundamental scientific purposes and for technological application. When a layered material is thinned or delaminated to its physical limits, a two-dimensional (2D) material is formed and exhibits novel properties compared to its bulk parent phase. The complex layered phases known as MAX phases (where M = early transition metal, A = A-group element, e.g. Al or Si, and X = C or N) are an exciting model system for materials design and the understanding of process-structure-property relationships. When the A layers are selectively etched from the MAX phases, a new type of 2D material is formed, named MXene to emphasize the relation to the MAX phases and the parallel with graphene. Since their discovery in 2011, MXenes have rapidly become established as a novel class of 2D materials with remarkable possibilities for composition variations and property tuning. This article gives a brief overview of MAX phases and MXene from a thin-film perspective, reviewing theory, characterization by electron microscopy, properties and how these are affected by the change in dimensionality, and outstanding challenges.
|
|