| 1. |
- Gustafsson, Oscar, et al.
(author)
-
Long-wavelength infrared quantum-dot based interband photodetectors
- 2011
-
In: Infrared physics & technology. - : Elsevier BV. - 1350-4495 .- 1879-0275. ; 54:3, s. 287-291
-
Journal article (peer-reviewed)abstract
- We report on the design and fabrication of (Al)GaAs(Sb)/InAs tensile strained quantum-dot (QD) based detector material for thermal infrared imaging applications in the long-wavelength infrared (LWIR) regime. The detection is based on transitions between confined dot states and continuum states in a type-II band lineup, and we therefore refer to it as a dot-to-bulk (D2B) infrared photodetector with expected benefits including long carrier lifetime due to the type-II band alignment, suppressed Shockley-Read-Hall generation-recombination due to the relatively large-bandgap matrix material, inhibited Auger recombination processes due to the tensile strain and epitaxial simplicity. Metal-organic vapor-phase epitaxy was used to grow multiple (Al)GaAs(Sb) QD layers on InAs substrates at different QD nominal thicknesses, compositions, doping conditions and multilayer periods, and the material was characterized using atomic force and transmission electron microscopy, and Fourier-transform infrared absorption spectroscopy. Dot densities up to 1 x 10(11) cm(-2), 1 x 10(12) cm(-2) and 3 x 10(10) cm(-2) were measured for GaAs, AlGaAs and GaAsSb QDs, respectively. Strong absorption in GaAs, AlGaAs and GaAsSb multilayer QD samples was observed in the wavelength range 6-12 mu m. From the wavelength shift in the spectral absorption for samples with varying QD thickness and composition it is believed that the absorption is due to an intra- valance band transition. From this it is possible to estimate the type-II inter-band transition wavelength, thereby suggesting that (Al)GaAs(Sb) QD/InAs heterostructures are suitable candidates for LWIR detection and imaging.
|
|
| 2. |
- Höglund, Linda, 1974-
(author)
-
Growth and characterisation of InGaAs-based quantum dots-in-a-well infrared photodetectors
- 2008
-
Doctoral thesis (other academic/artistic)abstract
- This thesis presents results from the development of quantum dot (QD) based infrared photodetectors (IPs). The studies include epitaxial growth of QDs, investigations of the structural, optical and electronic properties of QD-based material as well as characterisation of the resulting components.Metal-organic vapour phase epitaxy is used for growth of self-assembled indium arsenide (InAs) QDs on gallium arsenide (GaAs) substrates. Through characterisation by atomic force microscopy, the correlation between size distribution and density of quantum dots and different growth parameters, such as temperature, InAs deposition time and V/III-ratio (ratio between group V and group III species) is achieved. The V/III-ratio is identified as the most important parameter in finding the right growth conditions for QDs. A route towards optimisation of the dot size distribution through successive variations of the growth parameters is presented.The QD layers are inserted in In0.15Ga0.85As/GaAs quantum wells (QWs), forming so-called dots-in-a-well (DWELL) structures. These structures are used to fabricate IPs, primarily for detection in the long wavelength infrared region (LWIR, 8-14 μm).The electron energy level schemes of the DWELL structures are revealed by a combination of different experimental techniques. From Fourier transform photoluminescence (FTPL) and FTPL excitation (FTPLE) measurements the energy level schemes of the DWELL structures are deduced. Additional information on the energy level schemes is obtained from tunneling capacitance measurements and the polarization dependence studies of the interband transitions. From tunneling capacitance measurements, the QD electron energy level separation is confirmed to be 40-50 meV and from the polarization dependence measurements, the heavy hole character of the upper hole states are revealed.Further characterisation of the IPs, by interband and intersubband photocurrent measurements as well as dark current measurements, is performed. By comparing the deduced energy level scheme of the DWELL structure and the results of the intersubband photocurrent measurements, the origin of the photocurrent is determined. The main intersubband transition contributing to the photocurrent is identified as the QD ground state to a QW excited state transition. Optical pumping is employed to gain information on the origin of an additional photocurrent peak observed only at temperatures below 60 K. By pumping resonantly with transitions associated with certain quantum dot energy levels, this photocurrent peak is identified as an intersubband transition emanating from the quantum dot excited state. Furthermore, the detector response is increased by a factor of 10, when using simultaneous optical pumping into the quantum dots states, due to the increasing electron population created by the pumping. In this way, the potentially achievable responsivity of the detector is predicted to be 250 mA/W.Significant variations of photocurrent and dark currents are observed, when bias and temperature are used as variable parameters. The strong bias and temperature dependence of the photocurrent is attributed to the escape route from the final state in the QW, which is limited by tunneling through the triangular barrier. Also the significant bias and temperature dependence of the dark current could be explained in terms of the strong variation of the escape probability from different energy states in the DWELL structure, as revealed by interband photocurrent measurements. These results are important for the future optimisation of the DWELL IP.Tuning of the detection wavelength within the LWIR region is achieved by means of a varying bias across the DWELL structure. By positioning the InAs quantum dot layer asymmetrically in a 8 nm wide In0.15Ga0.85As/GaAs quantum well, a step-wise shift in the detection wavelength from 8.4 to 10.3 μm could be achieved by varying the magnitude and polarity of the applied bias. These tuning properties could be essential for applications such as odulators and dual-colour infrared detection.
|
|