- Gedefaw, Desta Antenehe, 1971, et al.
(författare)
-
Conjugated polymers with polar side chains in bulk heterojunction solar cell devices
- 2014
-
Ingår i: Polymer International. - : Wiley. - 1097-0126 .- 0959-8103. ; 63:1, s. 22-30
-
Tidskriftsartikel (refereegranskat)abstract
- Two polymers with polar side chains, namely poly[2,7-(9,9-dioctylfluorene)-alt-5,5-(5',8'-di-2-thienyl-(2',3'-bis(3''-(2-(2-methoxyethoxy)ethoxy)phenyl)quinoxaline))] (P1) and poly[2,7-(9,9-bis(2-(2-methoxyethoxy)ethyl)fluorene)-alt-5,5-(5',8'-di-2-thienyl-(2',3'-bis(3''-(2-(2-methoxyethoxy)-ethoxy)phenyl)quinoxaline))] (P2), were synthesized for solar cell application. A series of bulk heterojunction solar cells were systematically fabricated and characterized by varying the electron-acceptor materials, processing solvents and thickness of the active layer. The results show that P1, with a higher molecular weight and good film-forming properties, performed better. The best device showed an open circuit voltage of 0.87 V, a short circuit current of 6.81 mA cm(-2) and a power conversion efficiency of 2.74% with 1:4 polymer:[6,6]-phenyl-C71-butyric acid methyl ester (PCBM[70]) mixture using o-dichlorobenzene (o-DCB) as processing solvent. P2 on the other hand showed a poorer performance with chlorobenzene as processing solvent, but a much improved performance was obtained using o-DCB instead. Thus, an open circuit voltage of 0.80 V, short circuit current of 6.21 mA cm(-2) and an overall power conversion efficiency of 2.22% were recorded for a polymer:PCBM[70] mixing ratio of 1:4. This is presumably due to the improvement of the morphology of the active layer using o-DCB as processing solvent. (c) 2013 Society of Chemical Industry
|
|
| 3. |
- Zhou, Yi, et al.
(författare)
-
Black Polymers in Bulk-Heterojunction Solar Cells
- 2010
-
Ingår i: IEEE JOURNAL OF SELECTED TOPICS IN QUANTUM ELECTRONICS. - : Institute of Electrical and Electronics Engineers (IEEE). - 1077-260X .- 1558-4542. ; 16:6, s. 1565-1572
-
Tidskriftsartikel (refereegranskat)abstract
- The active materials in polymer solar cells have a decisive role on the performance of the cells. Polymers with extended absorption, i.e., black polymers with absorption covering the whole visible region are desired in order to capture the important parts of the solar irradiation. Different ways of achieving black active materials are discussed and two new alternating polyfluorene (APFO) copolymers with broad absorption, APFO-Black 1 and APFO-Black 2, using two different design strategies are described. The UV-Vis absorption spectra of the polymers extend to approximately 850 nm, and the polymers were used as donors and [6,6]-phenyl-C-61-butyric acid methyl ester (PCBM)[60] or PCBM[70] as acceptors in solar cell devices in various mixing ratios. The best combinations yielded an overall power conversion efficiency of 1.2% for APFO-Black 1 and 1.5% for APFO-Black 2.
|
|