| 1. |
- Bloch, J., et al.
(författare)
-
Reversible structural change and thermodynamic properties of hydrogen in thin vanadium films
- 2007
-
Ingår i: Physical Review B. Condensed Matter and Materials Physics. - 1098-0121 .- 1550-235X. ; 75:16, s. 165418-
-
Tidskriftsartikel (refereegranskat)abstract
- The absorption of H in 50nm V(001) films under pressures of 1–104Pa H2 and at temperatures between 310 and 530K was studied using in situ combined x-ray diffraction (XRD) and electrical resistivity measurements. The H-induced XRD peak shifts clearly indicate a fully reversible and nondeteriorating first-order phase transformation for the film. The H-induced residual resistivity changes in the V film demonstrate several extreme points (maxima and minima) apparently associated with some special points on the pressure isotherms of the film both below and above the critical temperature (Tc=460±20K) . Correlating these extreme points with the known V(bulk)-H phase diagram indicates that, in addition to the first-order transformation, two additional reversible second-order transitions exist in the film. The enthalpy and entropy of this transformation, obtained from the temperature dependence of the plateau pressures, are ‑39±1kJ/mol°K , and ‑60±2J/mol , respectively. The thermodynamic constants and the lattice parameters of the phases for the first-order transformation in the film closely correspond to the α→β phase transformation in bulk V.
|
|
| 2. |
- Bručas, Rimantas, et al.
(författare)
-
Magnetic and transport properties of Ni81Fe19/Al2O3 granular multilayers approaching the superparamagnetic limit
- 2007
-
Ingår i: Journal of Applied Physics. - : AIP Publishing. - 0021-8979 .- 1089-7550. ; 101:7, s. 073907-
-
Tidskriftsartikel (refereegranskat)abstract
- The magnetic and transport properties of Ni81Fe 19/Al2O3 granular multilayer films were studied in relation to their structural properties as the nominal thickness t of the permalloy (Ni81Fe19) layer was varied near the percolation limit: in the range of 8≤t≤ 16 Å while keeping the nominal thickness of the Al2O3 layers constant at 16 Å. A good structural quality of the multilayers was demonstrated by low angle x-ray reflectivity measurements, and transmission electron microscopy showed the transition from continuous permalloy layers separated by aluminium oxide layers for t= 16 Å to metal grains dispersed in the insulator at t=8 Å. Magnetization measurements showed the gradual transition from ferromagnetic layers to superparamagnetic clusters and grains that successively become blocked as the temperature decreases. A strong correlation between transport and structural properties was observed in the temperature (T) dependence of the electrical resistance measured with the current in the plane in the range of 2 ≤T≤300 K: a gradual change of behavior from continuous permalloy layers with conducting interlayer connections for t=16 Å. to isolated permalloy grains in a dielectric for the film with t= 10 Å. The percolation occurs between 12 and 10 Å, as deduced both from the magnetic and resistive properties. The discontinuous metal films were analyzed within models for thermally assisted tunneling, yielding estimates of the tunneling barrier for intralayer conduction of about 20 meV for t= 10 Å. A significant magnetic field dependence of the resistance increasing with decreasing temperature was observed in all samples.
|
|
| 3. |
|
|
| 4. |
|
|
| 5. |
- Brucas, Rimantas, 1965, et al.
(författare)
-
Tunneling and charging effects in discontinuous superparamagnetic Ni81Fe19/Al2O3 multilayers
- 2010
-
Ingår i: Physical Review B - Condensed Matter and Materials Physics. - : American Physical Society. - 2469-9950 .- 2469-9969 .- 1098-0121 .- 1550-235X. ; 81:22, s. 224437-
-
Tidskriftsartikel (refereegranskat)abstract
- The magnetic and transport properties of films based on discontinuous layers of Ni81Fe19 (Py) embedded in Al2O3 were investigated. In films with nominal Py thicknesses 6 and 8 angstrom superparamagnetic particles with median diameters D-med = 2.8 and 3.1 nm and distribution widths sigma(D)= 1.2 and 1.3 nm were formed. Current voltage (IU) curves were measured with the current perpendicular to the film plane. The analyses show that the charge transport occurs via tunneling; with the charging energy supplied by thermal fluctuations at high temperature, T >= 100 K, and by the electric field at low temperature, T
|
|
| 6. |
- Ciuciulkaite, Agne, et al.
(författare)
-
Collective magnetization dynamics in nanoarrays of thin FePd disks
- 2019
-
Ingår i: Physical Review B. - : AMER PHYSICAL SOC. - 2469-9950 .- 2469-9969. ; 99:18
-
Tidskriftsartikel (refereegranskat)abstract
- We report on the magnetization dynamics of a square array of mesoscopic disks, fabricated from an iron palladium alloy film. The dynamics properties were explored using ferromagnetic resonance measurements and micromagnetic simulations. The obtained spectra exhibit features resulting from the interactions between the disks, with a clear dependence on both temperature and the direction of the externally applied field. We demonstrate a qualitative agreement between the measured and calculated spectra. Furthermore, we calculated the mode profiles of the standing spin waves excited during time-dependent magnetic field excitations. The resulting maps confirm that the features appearing in the ferromagnetic resonance absorption spectra originate from the temperature- and directional-dependent interdisk interactions.
|
|
| 7. |
- Eastwood, D. S., et al.
(författare)
-
X-ray scattering from two-dimensionally patterned magnetic thin film nanoscale arrays
- 2007
-
Ingår i: Superlattices and Microstructures. - : Elsevier BV. - 0749-6036 .- 1096-3677. ; 41:2-3, s. 163-167
-
Tidskriftsartikel (refereegranskat)abstract
- Thin metallic films patterned into nanoscale periodic arrays give rise to coherent satellites on either side of the specular reflection when illuminated at grazing incidence with x-rays. We have used grazing incidence x-ray scattering to probe the crystallography of two-dimensional patterned arrays. Excellent agreement is obtained between experimental scattering profiles and those simulated using a fast Fourier transform method. The technique is appropriate to any shape of patterned element. It is shown that the symmetry of the satellites in an azimuthal rotation map of the scattered intensity provides a sensitive means of measuring symmetry of the two-dimensional order in patterned nanostructures. Furthermore, the in-plane coherence length of the array is found to determine the lineshape of the coherent satellite peaks. We find very good agreement between experimental and simulated rotation maps for the two dimensional array.
|
|
| 8. |
|
|
| 9. |
- Hanson, Maj, 1939, et al.
(författare)
-
Arrays of elliptical Fe(001) nanoparticles: Magnetization reversal, dipolar interactions, and effects of finite array sizes
- 2015
-
Ingår i: Physical Review B. Condensed Matter and Materials Physics. - 1098-0121 .- 2469-9950 .- 2469-9969 .- 1550-235X. ; 92:9
-
Tidskriftsartikel (refereegranskat)abstract
- The magnetic properties of arrays of nanoparticles are determined by the interplay between the individual particle properties and the dipolar interactions between them. Here we present a study of arrays of elliptical Fe(001) particles of thickness 10–50 nm. The aspect ratios of the ellipses are 1:3, their short axes a=50, 100, or 150 nm, and the periodicity of the rectangular arrays is either two or four times the corresponding axes of the ellipses. Magnetic measurements together with numerical and micromagnetic calculations yield a consistent picture of the arrays, comprising single-domain nanoparticles. We show that the magnetization reversal, occurring in the range 100–400 mT for fields applied along the long axis, is mainly determined by the properties of the corresponding single Fe ellipses. The interaction fields of the order of tens of mT can be tuned by the array configurations. For the actual arrays the interactions promote switching. For film thicknesses below the Bloch wall width parameter of Fe, lw=22 nm, magnetization reversal occurs without formation of domain walls or vortices. Within this range arrays may be tuned to obtain a well-defined switching field. Two general conclusions are drawn from the calculations: the character of the interaction, whether it promotes or delays magnetization reversal, is determined by the aspect ratio of the array grid, and the interaction strength saturates as the size of the array increases.
|
|
| 10. |
- Kravtsov, Evgeny, et al.
(författare)
-
Onset of spin-density-wave antiferromagnetism in Cr/V multilayers
- 2007
-
Ingår i: Physical Review B. Condensed Matter and Materials Physics. - 1098-0121 .- 1550-235X. ; 76:2, s. 024421-
-
Tidskriftsartikel (refereegranskat)abstract
- Spin-density-wave (SDW) magnetism in a series of Cr/V heterostructures with different Cr thicknesses was systematically investigated by combined resistivity, neutron, and synchrotron scattering measurements. We show that the onset of the bulklike SDW state comes through several necessary steps from a paramagnetic state through a commensurate SDW to an incommensurate SDW. The Néel temperature for the incommensurate SDW is found to scale with Cr thickness and reaches the bulk value at a Cr thickness of about 2000 Å. The proximity effect from Cr/V interfaces is found to lead to (i) the appearance of a 50-Å magnetically dead Cr layer near Cr/V interfaces and (ii) suppression of the spin-flip transition and stabilization of a single-domain SDW with out-of-plane spins and out-of-plane propagation wave vector. Finally, we show that the SDW period increases with decreasing Cr thickness and becomes temperature independent in sufficiently thin Cr layers.
|
|