| 1. |
- Agnarsson, Björn, 1977, et al.
(författare)
-
Rutile TiO 2 thin films grown by reactive high power impulse magnetron sputtering
- 2013
-
Ingår i: Thin Solid Films. - : Elsevier BV. - 0040-6090 .- 1879-2731. ; 545, s. 445-450
-
Tidskriftsartikel (refereegranskat)abstract
- Thin TiO 2 films were grown on Si(001) substrates by reactive dc magnetron sputtering (dcMS) and high power impulse magnetron sputtering (HiPIMS) at temperatures ranging from 300 to 700 C.Optical and structural properties of films were compared both before and after post-annealing using scanning electron microscopy, low angle X-ray reflection (XRR), grazing inc idence X-ray diffractometry and spectroscopic ellipsometry.Both dcMS- and HiPIMS-grown films reveal polycrystalline rutile TiO 2 , even prior to post-annealing.The HiPIMS-grown films exhibit significantly larger grains compared to that of dcMC-grown films, approaching 100% of the film thickness for films grown at 700 C.In addition, the XRR surface roughness of HiPIMS-grown films was significantly lower than that of dcMS-grown films over the whole temperature range 300-700 C.Dispersion curves could only be obtained for the HiPIMS-grown films, which were shown to have a refractive index in the range of 2.7-2.85 at 500 nm.The results show that thin, rutile TiO 2 films, with high refractive index, can be obtained by HiPIMS at relatively low growth temperatures, without post-annealing.Furthermore, these films are smoother and show better optical characteristics than their dcMS-grown counterparts.© 2013 Elsevier B.V.All rights reserved.
|
|
| 2. |
- Leosson, K., et al.
(författare)
-
Comparing resonant photon tunneling via cavity modes and Tamm plasmon polariton modes in metal-coated Bragg mirrors
- 2012
-
Ingår i: Optics Letters. - 0146-9592 .- 1539-4794. ; 37:19, s. 4026-4028
-
Tidskriftsartikel (refereegranskat)abstract
- Resonant photon tunneling was investigated experimentally in multilayer structures containing a high-contrast (TiO2/SiO2) Bragg mirror capped with a semitransparent gold film. Transmission via a fundamental cavity resonance was compared with transmission via the Tamm plasmon polariton resonance that appears at the interface between a metal film and a one-dimensional photonic bandgap structure. The Tamm-plasmon-mediated transmission exhibits a smaller dependence on the angle and polarization of the incident light for similar values of peak transmission, resonance wavelength, and finesse. Implications for transparent electrical contacts based on resonant tunneling structures are discussed.
|
|
| 3. |
- Magnus, Fridrik, et al.
(författare)
-
Nucleation and resistivity of ultrathin TiN films grown by high power impulse magnetron sputtering
- 2012
-
Ingår i: IEEE Electron Device Letters. - : IEEE. - 0741-3106 .- 1558-0563. ; 33:7, s. 1045-1047
-
Tidskriftsartikel (refereegranskat)abstract
- TiN films have been grown on SiO 2 by reactive high-power impulse magnetron sputtering (HiPIMS) at temperatures of 22°C-600°C. The film resistance is monitored in situ to determine the coalescence and continuity thicknesses that decrease with increasing growth temperature with a minimum of 0.38 ± 0.05 nm and 1.7 ± 0.2 nm, respectively, at 400°C. We find that HiPIMS-deposited films have significantly lower resistivity than dc magnetron sputtered (dcMS) films on SiO 2 at all growth temperatures due to reduced grain boundary scattering. Thus, ultrathin continuous TiN films with superior electrical characteristics can be obtained with HiPIMS at reduced temperatures compared to dcMS.
|
|
| 4. |
- Novoselova, Iuliia P., et al.
(författare)
-
Large uniaxial magnetostriction with sign inversion at the first order phase transition in the nanolaminated Mn2GaC MAX phase
- 2018
-
Ingår i: Scientific Reports. - London : NATURE PUBLISHING GROUP. - 2045-2322. ; 8
-
Tidskriftsartikel (refereegranskat)abstract
- In 2013, a new class of inherently nanolaminated magnetic materials, the so called magnetic MAX phases, was discovered. Following predictive material stability calculations, the hexagonal Mn2GaC compound was synthesized as hetero-epitaxial films containing Mn as the exclusive M-element. Recent theoretical and experimental studies suggested a high magnetic ordering temperature and non-collinear antiferromagnetic (AFM) spin states as a result of competitive ferromagnetic and antiferromagnetic exchange interactions. In order to assess the potential for practical applications of Mn2GaC, we have studied the temperature-dependent magnetization, and the magnetoresistive, magnetostrictive as well as magnetocaloric properties of the compound. The material exhibits two magnetic phase transitions. The Neel temperature is T-N similar to 507 K, at which the system changes from a collinear AFM state to the paramagnetic state. At T-t = 214 K the material undergoes a first order magnetic phase transition from AFM at higher temperature to a non-collinear AFM spin structure. Both states show large uniaxial c-axis magnetostriction of 450 ppm. Remarkably, the magnetostriction changes sign, being compressive (negative) above T-t and tensile (positive) below the T-t. The sign change of the magnetostriction is accompanied by a sign change in the magnetoresistance indicating a coupling among the spin, lattice and electrical transport properties.
|
|
| 5. |
- Petruhins, Andrejs, et al.
(författare)
-
Synthesis and characterization of magnetic (Cr0.5Mn0.5)2GaC thin films
- 2015
-
Ingår i: Journal of Materials Science. - : Springer Berlin/Heidelberg. - 0022-2461 .- 1573-4803. ; 50:13, s. 4495-4502
-
Tidskriftsartikel (refereegranskat)abstract
- Growth of (Cr0.5Mn0.5)2GaC thin films from C, Ga, and compound Cr0.5Mn0.5 targets is reported for depositions on MgO (111), 4H-SiC (0001), and Al2O3 (0001) with and without a NbN (111) seed layer. Structural quality is found to be highly dependent on the choice of substrate with MgO (111) giving the best results as confirmed by X-ray diffraction and transmission electron microscopy. Phase pure, high crystal quality MAX phase thin films are realized, with a Cr:Mn ratio of 1:1. Vibrating sample magnetometry shows a ferromagnetic component from 30 K up to 300 K, with a measured net magnetic moment of 0.67 μB per metal (Cr + Mn) atom at 30 K and 5 T. The temperature dependence of the magnetic response suggests competing magnetic interactions with a resulting non-collinear magnetic ordering.
|
|
| 6. |
- Magnus, Fridrik, et al.
(författare)
-
Current-voltage-time characteristics of the reactive Ar/O2 high power impulse magnetron sputtering discharge
- 2012
-
Ingår i: Journal of Vacuum Science & Technology. A. Vacuum, Surfaces, and Films. - : American Institute of Physics (AIP). - 0734-2101 .- 1520-8559. ; 30:5
-
Tidskriftsartikel (refereegranskat)abstract
- The discharge current–voltage–time waveforms are studied in the reactive Ar/O2 high power impulse magnetron sputtering discharge with a titanium target for 400 μs long pulses. The discharge current waveform is highly dependent on both the pulse repetition frequency and discharge voltage and the current increases with decreasing frequency or voltage. The authors attribute this to an increase in the secondary electron emission yield during the self-sputtering phase of the pulse, as an oxide forms on the target.
|
|
| 7. |
- Magnus, Fridrik, et al.
(författare)
-
Sequential magnetic switching in Fe/MgO(001) superlattices
- 2018
-
Ingår i: Physical Review B. Condensed Matter and Materials Physics. - : American Physical Society. - 1098-0121 .- 1550-235X. ; 97:17
-
Tidskriftsartikel (refereegranskat)abstract
- Polarized neutron reflectometry is used to determine the sequence of magnetic switching in interlayer exchangecoupled Fe/MgO(001) superlattices in an applied magnetic field. For 19.6 Å thick MgO layers we obtain a 90◦periodic magnetic alignment between adjacent Fe layers at remanence. In an increasing applied field the toplayer switches first followed by its second-nearest neighbor. For 16.4 Å MgO layers, a 180◦periodic alignment isobtained at remanence and with increasing applied field the layer switching starts from the two outermost layersand proceeds inwards. This sequential tuneable switching opens up the possibility of designing three-dimensionalmagnetic structures with a predefined discrete switching sequence
|
|
| 8. |
|
|
| 9. |
- Zubayer, Anton, et al.
(författare)
-
Reflective, polarizing, and magnetically soft amorphous neutron optics with 11B-enriched B4C
- 2024
-
Ingår i: Science Advances. - : AMER ASSOC ADVANCEMENT SCIENCE. - 2375-2548. ; 10:7
-
Tidskriftsartikel (refereegranskat)abstract
- The utilization of polarized neutrons is of great importance in scientific disciplines spanning materials science, physics, biology, and chemistry. However, state-of-the-art multilayer polarizing neutron optics have limitations, particularly low specular reflectivity and polarization at higher scattering vectors/angles, and the requirement of high external magnetic fields to saturate the polarizer magnetization. Here, we show that, by incorporating (B4C)-B-11 into Fe/Si multilayers, amorphization and smooth interfaces can be achieved, yielding higher neutron reflectivity, less diffuse scattering, and higher polarization. Magnetic coercivity is eliminated, and magnetic saturation can be reached at low external fields (>2 militesla). This approach offers prospects for substantial improvement in polarizing neutron optics with nonintrusive positioning of the polarizer, enhanced flux, increased data accuracy, and further polarizing/analyzing methods at neutron scattering facilities.
|
|
| 10. |
- Magnus, Fridrik, et al.
(författare)
-
Giant magnetic domains in amorphous SmCo thin films
- 2014
-
Ingår i: Physical Review B. Condensed Matter and Materials Physics. - 1098-0121 .- 1550-235X. ; 89:22, s. 224420-1-224420-5
-
Tidskriftsartikel (refereegranskat)abstract
- The potential for tuning of magnetic properties and the exceptional uniformity are among the features that make amorphous magnetic materials attractive for technology. Here it is shown that the magnetization reversal in amorphous SmCo thin films takes place through the formation of giant magnetic domains, over a centimeter across. The domain structure is found to be dictated by the direction of the imprinted in-plane easy axis and the film boundaries. This is a consequence of the size of the anisotropy and the structural uniformity of the films, which also allows the movement of millimeter-long domain walls over distances of several millimeters. The results demonstrate the possibility of tailoring the magnetic domain structure in amorphous magnets over a wide range of length scales, up to centimeters. Moreover, they highlight an important consequence of the structural perfection of amorphous films.
|
|