1.
  • Agnarsson, Björn, 1977, et al. (författare)
  • Rutile TiO 2 thin films grown by reactive high power impulse magnetron sputtering
  • 2013
  • Ingår i: Thin Solid Films. - : Elsevier BV. - 0040-6090 .- 1879-2731. ; 545, s. 445-450
  • Tidskriftsartikel (refereegranskat)abstract
    • Thin TiO 2 films were grown on Si(001) substrates by reactive dc magnetron sputtering (dcMS) and high power impulse magnetron sputtering (HiPIMS) at temperatures ranging from 300 to 700 C.Optical and structural properties of films were compared both before and after post-annealing using scanning electron microscopy, low angle X-ray reflection (XRR), grazing inc idence X-ray diffractometry and spectroscopic ellipsometry.Both dcMS- and HiPIMS-grown films reveal polycrystalline rutile TiO 2 , even prior to post-annealing.The HiPIMS-grown films exhibit significantly larger grains compared to that of dcMC-grown films, approaching 100% of the film thickness for films grown at 700 C.In addition, the XRR surface roughness of HiPIMS-grown films was significantly lower than that of dcMS-grown films over the whole temperature range 300-700 C.Dispersion curves could only be obtained for the HiPIMS-grown films, which were shown to have a refractive index in the range of 2.7-2.85 at 500 nm.The results show that thin, rutile TiO 2 films, with high refractive index, can be obtained by HiPIMS at relatively low growth temperatures, without post-annealing.Furthermore, these films are smoother and show better optical characteristics than their dcMS-grown counterparts.© 2013 Elsevier B.V.All rights reserved.
  •  
2.
  • Ingason, Arni Sigurdur, et al. (författare)
  • Magnetic Self-Organized Atomic Laminate from First Principles and Thin Film Synthesis
  • 2013
  • Ingår i: Physical Review Letters. - : American Physical Society. - 0031-9007 .- 1079-7114. ; 110
  • Tidskriftsartikel (refereegranskat)abstract
    • he first experimental realization of a magnetic Mn+1AXn (MAX) phase, (Cr0.75Mn0.25)2GeC, is presented, synthesized as a heteroepitaxial single crystal thin film, exhibiting excellent structural quality. This self-organized atomic laminate is based on the well-known Cr2GeC, with Mn, a new element in MAX phase research, substituting Cr. The compound was predicted using first-principles calculations, from which a variety of magnetic behavior is envisaged, depending on the Mn concentration and Cr/Mn atomic configuration within the sublattice. The analyzed thin films display a magnetic signal at room temperature.
  •  
3.
  • Leosson, K., et al. (författare)
  • Comparing resonant photon tunneling via cavity modes and Tamm plasmon polariton modes in metal-coated Bragg mirrors
  • 2012
  • Ingår i: Optics Letters. - 0146-9592 .- 1539-4794. ; 37:19, s. 4026-4028
  • Tidskriftsartikel (refereegranskat)abstract
    • Resonant photon tunneling was investigated experimentally in multilayer structures containing a high-contrast (TiO2/SiO2) Bragg mirror capped with a semitransparent gold film. Transmission via a fundamental cavity resonance was compared with transmission via the Tamm plasmon polariton resonance that appears at the interface between a metal film and a one-dimensional photonic bandgap structure. The Tamm-plasmon-mediated transmission exhibits a smaller dependence on the angle and polarization of the incident light for similar values of peak transmission, resonance wavelength, and finesse. Implications for transparent electrical contacts based on resonant tunneling structures are discussed.
  •  
4.
  • Mockuté, Aurelija, et al. (författare)
  • Structural and magnetic properties of (Cr1-xMnx)(5)Al-8 solid solution and structural relation to hexagonal nanolaminates
  • 2014
  • Ingår i: Journal of Materials Science. - : Springer Verlag (Germany). - 0022-2461 .- 1573-4803. ; 49:20, s. 7099-7104
  • Tidskriftsartikel (refereegranskat)abstract
    • Electron microscopy is used to reveal the competitive epitaxial growth of bcc structure (Cr1-x Mn (x) )(5)Al-8 and (Cr1-y Mn (y) )(2)AlC [M (n+1)AX (n) (MAX)] phase during both magnetron sputtering and arc deposition. X-ray diffraction theta-2 theta measurements display identical peak positions of (000n)-oriented MAX phase and (Cr1-x Mn (x) )(5)Al-8, due to the interplanar spacing of (Cr1-x Mn (x) )(5)Al-8 that matches exactly half a unit cell of (Cr1-y Mn (y) )(2)AlC. Vibrating sample magnetometry shows that a thin film exclusively consisting of (Cr1-x Mn (x) )(5)Al-8 exhibits a magnetic response, implying that the potential presence of this phase needs to be taken into consideration when evaluating the magnetic properties of (Cr, Mn)(2)AlC.
  •  
5.
  • Shayestehaminzadeh, S., et al. (författare)
  • Ultra-thin poly-crystalline TiN films grown by HiPIMS on MgO(100) - In-situ resistance study of the initial stage of growth
  • 2013
  • Ingår i: Thin Solid Films. - : Elsevier BV. - 0040-6090 .- 1879-2731. ; 549, s. 199-203
  • Tidskriftsartikel (refereegranskat)abstract
    • The growth of ultra-thin TiN films on single-crystalline MgO(100) substrates by high power impulse magnetron sputtering (HiPIMS) was studied for growth temperatures ranging from 35 degrees C to 600 degrees C. X-ray analysis showed that the films had a textured poly-crystalline structure. Films grown by dc magnetron sputtering (dcMS) were epitaxial at the higher growth temperatures. In-situ resistance measurements, during growth, revealed the coalescence thickness and film continuity thickness. The film grown by HiPIMS at room temperature coalesced at 1.2 +/- 0.1 nm and became structurally continuous at 2.67 +/- 0.15 nm. At 600 degrees C, the coalescence and continuity thicknesses decreased to 0.56 +/- 0.05 nm and 0.82 +/- 0.05 nm, respectively. X-ray reflectivity measurements revealed that the growth rate of the films was roughly constant for all growth temperatures. The film density increased slightly with growth temperature up to 5.3 g/cm(3) at 600 degrees C and the surface roughness of the films decreased from 1 nm to 0.3 nm while the growth temperature increased from 35 degrees C to 600 degrees C. Grazing incident X-ray diffraction measurements showed the presence of [111], [200] and [220] crystallites at all growth temperatures. The smallest [200] and [220] grain sizes appeared at 100 degrees C while the [200] grain size increased by increasing the growth temperature.
  •  
Skapa referenser, mejla, bekava och länka
  • Resultat 1-5 av 5

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy