Characterization of pack cemented Ni(2)Al(3 )coating exposed to KCl(s) induced corrosion at 600 degrees C
- 2018
-
Ingår i: Materials at High Temperatures. - : Informa UK Limited. - 0960-3409 .- 1878-6413. ; 35:1-3, s. 267-274
-
Tidskriftsartikel (refereegranskat)abstract
- Oxidation of Ni2Al3 produced by pack aluminizing of pure nickel was studied with and without 0.10 mg cm(-2) KCl(s) deposit in an environment containing 5% O-2, 40% H2O and 55% N-2 at 600 degrees C for up to 168 h. Oxide microstructure and composition was investigated by SEM/EDX, BIB, TEM and GDOES. Oxidised Ni2Al3 shows minimal weight gain, while adding KCl results in a small weight loss consistent with evaporation of KCl. On the surface of samples exposed to the gas environment only, a 30 nm oxide of Al oxide was present, but where KCl was present as deposit, 50-250 nm thick nodules form that are enriched in K, O and Al.
|
|