1.	Liang, Jie, et al. (författare) CHA-type zeolites with high boron content : Synthesis, structure and selective adsorption properties 2014 Ingår i: Microporous and Mesoporous Materials. - : Elsevier BV. - 1387-1811 .- 1873-3093. ; 194, s. 97-105 Tidskriftsartikel (refereegranskat)abstract Borosilicate zeolites with CHA-type framework are synthesized hydrothermally by using N,N,N-trimethylcyclohexylammonium hydroxide as structure directing agent. The use of this cation induces an increase of boron content in the CHA-type zeolites, and the Si/B ratios of the as-synthesized samples is in the range of 11.8-6.9. Rietveld refinements of the calcinated samples reveal a contraction of unit cells with the increase of boron content, and the 8-ring opening window of cha cavity becomes narrower. B-11 MAS NMR shows that all the boron atoms are incorporated into the framework as tetrahedral BO4 units in the as-synthesized samples. The thermal stability of these CHA-type borosilicates decreases with the increase of boron content, and the framework can retain up to 800 degrees C. These borosilicates, with the BET surfaces of 583-632 m(2)/g, show a high adsorption capacity for H-2 at 77 K, 900 mmHg and a preferential adsorption for CO2 at 273 K. This selective adsorption property enables CHA-type borosilicates to be potential materials as CO2 adsorbent.

Liang, Jie, et al. (författare)
CHA-type zeolites with high boron content : Synthesis, structure and selective adsorption properties
2014
Ingår i: Microporous and Mesoporous Materials. - : Elsevier BV. - 1387-1811 .- 1873-3093. ; 194, s. 97-105
Tidskriftsartikel (refereegranskat)abstract
- Borosilicate zeolites with CHA-type framework are synthesized hydrothermally by using N,N,N-trimethylcyclohexylammonium hydroxide as structure directing agent. The use of this cation induces an increase of boron content in the CHA-type zeolites, and the Si/B ratios of the as-synthesized samples is in the range of 11.8-6.9. Rietveld refinements of the calcinated samples reveal a contraction of unit cells with the increase of boron content, and the 8-ring opening window of cha cavity becomes narrower. B-11 MAS NMR shows that all the boron atoms are incorporated into the framework as tetrahedral BO4 units in the as-synthesized samples. The thermal stability of these CHA-type borosilicates decreases with the increase of boron content, and the framework can retain up to 800 degrees C. These borosilicates, with the BET surfaces of 583-632 m(2)/g, show a high adsorption capacity for H-2 at 77 K, 900 mmHg and a preferential adsorption for CO2 at 273 K. This selective adsorption property enables CHA-type borosilicates to be potential materials as CO2 adsorbent.

Träfflista för sökning "WFRF:(Mu Weijun) "