| 1. |
- Crowley, T.A., et al.
(författare)
-
Synthesis of metal and metal oxide nanowires and nanotube arrays within a mesoporous silica template
- 2003
-
Ingår i: Chemistry of Materials. - : American Chemical Society (ACS). - 0897-4756 .- 1520-5002. ; 15:18, s. 3518-3522
-
Tidskriftsartikel (refereegranskat)abstract
- Metallic nanowires of cobalt, copper, and iron oxide magnetite (Fe3O4) have been synthesized within the pores of mesoporous silica using a supercritical fluid inclusion technique. The mesoporous matrix provides a means of producing a high density of stable, hexagonally ordered arrays of highly crystalline nanowires. The formation of the metal and metal oxide nanowires within the silica mesopores was confirmed by transmission electron microscopy (TEM), N2 adsorption experiments, and powder X-ray diffraction (PXRD). The mechanism of nanowire formation within the mesopores appears to occur through the initial binding and coating of the pore walls with the metal atoms to form tubelike structures within the mesoporous template. The thickness of these tubes subsequently increases with further metal deposition until nanowires are formed. Additionally, the crystal structure of the cobalt nanowires formed within the mesoporous template can be readily changed by manipulating the density of the supercritical fluid phase.
|
|
| 2. |
|
|
| 3. |
|
|
| 4. |
|
|
| 5. |
- Pokropivny, A.V., et al.
(författare)
-
Study of Nanoscale Contacts with the Help of Combined TEM-AFM Technique and Theoretical MD-TM Calculations: In situ Transformations of Gold Nanowires
- 2004
-
Ingår i: Physics of low-Dimensional structures. - 0204-3467. ; 1-2, s. 83-90
-
Tidskriftsartikel (refereegranskat)abstract
- Nanoscale gold contacts were investigated both experimentally and theoretically. Simulations of in situ processes in a new combined TEM-AFM microscope were performed by molecular dynamics and theoretical mechanics methods. Atomistic transformations of gold nanometer-sized wires (nanowires) between Au-probe and Au-surface were studied in processes both of loading-unloading and in the normal, lateral, diagonal and zigzag directions of the probe motion. Molecular dynamics was used for studies of "adhesion avalanche", shear and strain deformations. Theoretical mechanics was used for studies of jump-to-contact and jump-off-contact phenomena. Reorientations from (100) to (111) planes with formation of extended zigzag, vacancy cavities, a double-neck creation and a slip along the (110) plane with formation of twins and steps were observed. Deformation mechanisms were shown to depend on schemes of motions and on the ratio between the relative velocity of the probe and surface motion and the velocity of the defect relaxation.
|
|
| 6. |
- Bogdanov, A. L., et al.
(författare)
-
Fabrication of arrays of nanometer size test structures for scanning probe microscope tips characterization
- 1994
-
Ingår i: Journal of Vacuum Science & Technology B: Microelectronics Processing and Phenomena. - : American Vacuum Society. - 0734-211X. ; 12:6, s. 3681-3684
-
Konferensbidrag (refereegranskat)abstract
- A problem in scanning probe microscopy (SPM) is the unknown shape of the probing tip. Generally, the image is a convolution between the shape of the tip and the surface. Information of the shape of the probe may be gained by imaging very sharp tips. Here we present a method for making two-dimensional arrays of very sharp tips. The tip arrays were made of silicon using electron beam lithography with subsequent ion-beam etching. To achieve the best possible resolution, ultrasonic excitation was used during development of the bilayered PMMA resist. Thus, openings in the resist with size nearly equal to the spot size of the writing e-beam have been obtained. A further decrease of the radius of the tips was obtained by the choice of appropriate thickness for the masking NiCr layer. The tips were conical with a height up to 100 nm with a radius of the tip down to 10 nm. The tips were suitable for study of the shape of AFM probe tips, under condition that the tip array samples were rinsed in water prior to the measurement. Without the rinsing procedure, strong sticking forces between the probe and the sample would have eroded both of them. The regularity of the array provided an easy way to calibrate the lateral motion of the scanner
|
|
| 7. |
- Erts, D, et al.
(författare)
-
Instrumentation of STM and AFM combined with transmission electron microscope
- 2001
-
Ingår i: Applied Physics A. - : Springer Science and Business Media LLC. - 0947-8396 .- 1432-0630. ; 72:7, s. 71-74
-
Tidskriftsartikel (refereegranskat)abstract
- A scanning tunneling microscope (STM) combined with a transmission electron microscope (TEM) is a powerful tool for direct investigation of structures, electronic properties, and interactions at the atomic scale. Here, we report on two different designs of such TEM-STM as well as an extension with an atomic force microscope (TEM-AFM). In the first TEM-STM design, a stepper motor, combined with a one-dimensional inertial slider, was used to perform the coarse approach. The advantage of this design was the strong pulling force that enabled notched metallic wires to be broken inside the TEM, which lead to clean sample surfaces. A second design, with a three-dimensional inertial slider, allowed lateral motion inside the TEM, which simplified the adjustment of tip location on the sample. By replacing the STM tip with a standard AFM-cantilever chip, a new combination was demonstrated: TEM-AFM. Here the force was simply measured by direct TEM imaging of the motion of the AFM tip. Some experimental results are included to illustrate the capabilities of TEM-STM and TEM-AFM.
|
|
| 8. |
|
|
| 9. |
- Hu, Q H, et al.
(författare)
-
Properties of Tl-2201 thin films
- 1997
-
Ingår i: Physica. C, Superconductivity. - 0921-4534 .- 1873-2143. ; 282-287:Part 2, s. 1075-1076
-
Tidskriftsartikel (refereegranskat)abstract
- Tl2Ba2CuO6 (Tl-2201) thin films were synthesised on single crystal LaAlO3 and SrTiO3 substrates and on bicrystal LaAlO3 by an ex-situ process. Depending on thallium content and processing conditions, the films were orthorhombic or tetragonal. Tc was in the range 30 – 92 K while Jc reached 4.106A/cm2 at 12 K. By oxygen depletion, Tc was increased by 15 – 20 K for some films.
|
|
| 10. |
|
|