| 1. |
- Bangolla, Hemanth Kumar, et al.
(författare)
-
Composition-dependent photoconductivities in indium aluminium nitride nanorods grown by magnetron sputter epitaxy
- 2022
-
Ingår i: Nanoscale Advances. - : Royal Society of Chemistry. - 2516-0230. ; 4:22, s. 4886-4894
-
Tidskriftsartikel (refereegranskat)abstract
- Photoconduction (PC) properties were investigated for ternary indium aluminium nitride (InxAl1-xN) nanorods (NRs) with different indium compositions (x) from 0.35 to 0.68, as grown by direct-current reactive magnetron sputter epitaxy. Cross-sectional scanning transmission electron microscopy (STEM) reveals single-crystal quality of the vertically aligned InxAl1-xN NRs. Single-rod photodetector devices with good ohmic contacts were fabricated using the focused-ion-beam technique (FIB), where the In-rich In0.68Al0.32N NR exhibits an optimal photocurrent responsivity of 1400 A W-1 and photoconductive gain of 3300. A transition from a positive photoresponse to a negative photoresponse was observed, while increasing the In composition x from 0.35 to 0.57. The negative PC was further enhanced by increasing x to 0.68. A model based on the coexistence and competition of deep electron trap states and recombination centers was proposed to explain the interesting composition-dependent PC in these ternary III-nitride 1D nanostructures.
|
|
| 2. |
- Chen, Yen-Ting, et al.
(författare)
-
Nucleation of single GaN nanorods with diameters smaller than 35 nm by molecular beam epitaxy
- 2013
-
Ingår i: Applied Physics Letters. - : American Institute of Physics (AIP). - 0003-6951 .- 1077-3118. ; 103:20, s. 203108-
-
Tidskriftsartikel (refereegranskat)abstract
- Nucleation mechanism of catalyst-free GaN nanorod grown on Si(111) is investigated by the fabrication of uniform and narrow (andlt; 35 nm) nanorods without a pre-defined mask by molecular beam epitaxy. Direct evidences show that the nucleation of GaN nanorods stems from the sidewall of the underlying islands down to the Si(111) substrate, different from commonly reported ones on top of the island directly. Accordingly, the growth and density control of the nanorods is exploited by a "narrow-pass" approach that only narrow nanorod can be grown. The optimal size of surrounding non-nucleation area around single nanorod is estimated as 88 nm.
|
|
| 3. |
- Dorri, Samira, et al.
(författare)
-
Effects of stoichiometry and individual layer thickness ratio on the quality of epitaxial CrBx/TiBy superlattice thin films
- 2023
-
Ingår i: Materials & design. - : ELSEVIER SCI LTD. - 0264-1275 .- 1873-4197. ; 228
-
Tidskriftsartikel (refereegranskat)abstract
- Studies of single crystal artificial superlattices (SLs) of transition-metal (TM) diborides, which is instru- mental to understand hardening mechanisms at nanoscale, is lacking. Here, CrBx/TiBy (0001) diboride SLs [x,y E 1.7-3.3] are grown epitaxially on Al2O3(0001) substrates by direct-current magnetron sputter epitaxy. Growth conditions for obtaining well-defined SLs with good interface quality are found at 4 mTorr Ar pressure and 600 degrees C. 1 -mu m-thick SL films deposited with modulation periods A between 1 and 10 nm, and A=6 nm SLs with TiBy-to-A layer thickness ratios F ranging from 0.2 to 0.8 are studied. SLs with A=6 nm and F in the range of 0.2-0.4, with a near stoichiometric B/TM ratio, exhibit the high- est structural quality. The effects of F and stoichiometries (B/TM ratio) on the distribution of B in the SL structures are discussed. By increasing the relative thickness of TiBy, the crystalline quality of SLs starts to deteriorate due to B segregation in over-stoichiometric TiBy, resulting in narrow epitaxial SL columnar growth with structurally-distorted B-rich boundaries. Moreover, increasing the relative thickness of under-stoichiometric CrBx enhances the SL quality and hinders formation of B-rich boundaries. The SLs are found to exhibit hardness values in the range of 29-34 GPa.(c) 2023 The Author(s). Published by Elsevier Ltd. This is an open access article under the CC BY license (http://creativecommons.org/licenses/by/4.0/).
|
|
| 4. |
- Dorri, Samira, 1988-, et al.
(författare)
-
Enhanced quality of single crystal CrBx/TiBy diboride superlattices by controlling boron stoichiometry during sputter deposition
- 2024
-
Ingår i: Applied Surface Science. - : Elsevier. - 0169-4332 .- 1873-5584.
-
Tidskriftsartikel (refereegranskat)abstract
- Single-crystal CrB2/TiB2 diboride superlattices with well-defined layers are promising candidates for neutron optics. However, excess B in sputter-deposited TiBy using a single TiB2 target deteriorates the structural quality of CrBx/TiBy (0001) superlattices. We study the influence of co-sputtering of TiB2 + Ti on the stoichiometry and crystalline quality of 300-nm-thick TiBy single layers and CrBx/TiBy (0001) superlattices on Al2O3(0001) substrates grown by DC magnetron sputter epitaxy at growth-temperatures TS ranging from 600 to 900 °C. By controlling the relative applied powers to the TiB2 and Ti magnetrons, y could be reduced from 3.3 to 0.9. TiB2.3 grown at 750 °C exhibited epitaxial domains about 10x larger than non-co-sputtered films. Close-to-stoichiometry CrB1.7/TiB2.3 superlattices with modulation periods Λ = 6 nm grown at 750 °C showed the highest single crystal quality and best layer definition. TiB2.3 layers display rough top interfaces indicating kinetically limited growth while CrB1.7 forms flat and abrupt top interfaces indicating epitaxial growth with high adatom mobility.
|
|
| 5. |
- Dorri, Samira, 1988-, et al.
(författare)
-
Oxidation kinetics of overstoichiometric TiB2 thin films grown by DC magnetron sputtering
- 2022
-
Ingår i: Corrosion Science. - : Pergamon-Elsevier Science Ltd. - 0010-938X .- 1879-0496. ; 206
-
Tidskriftsartikel (refereegranskat)abstract
- We systematically study the oxidation properties of sputter-deposited TiB2.5 coatings up to 700 °C. Oxide-scale thickness dox increases linearly with time ta for 300, 400, 500, and 700 °C, while an oxidation-protective behavior occurs with dox=250∙ta0.2 at 600 °C. Oxide-layer’s structure changes from amorphous to rutile/anatase-TiO2 at temperatures ≥ 500 °C. Abnormally low oxidation rate at 600 °C is attributed to a highly dense columnar TiO2-sublayer growing near oxide/film interface with a top-amorphous thin layer, suppressing oxygen diffusion. A model is proposed to explain the oxide-scale evolution at 600 °C. Decreasing heating rate to 1.0 °C/min plays a noticeable role in the TiB2.5 oxidation.
|
|
| 6. |
- Ghafoor, Naureen, et al.
(författare)
-
Phase separation paths in metastable Zr1-xAlxN monolithic layers compared to multilayers with TiN: Growth versus annealing temperatures
- 2023
-
Ingår i: Materialia. - : ELSEVIER SCI LTD. - 2589-1529. ; 28
-
Tidskriftsartikel (refereegranskat)abstract
- Metastable super-saturated Zr1_xAlxN alloys tend to phase separate into the equilibrium cubic (c) ZrN and wurtzite (w) AlN due to a deep miscibility gap. Transformation is shown here to follow distinctly different paths depending on if Zr1_xAlxN (x = 0.3 and 0.6) is sputter deposited as a single layer or multi-layered with TiN, and further varied by post-deposition annealing. Using in situ high-energy synchrotron wide-angle X-ray scattering and analytical transmission electron microscopy, surface segregation effects are compared to secondary phase transformations occurring in as-deposited layers during thermal annealing up to 1000 degrees C. For the primary phase transformation from the vapor phase, w-AlN nucleates and an AlN-ZrN labyrinthine structure evolves at elevated deposition temperature with semi-coherent interfaces over several nanometers, where the higher Al content narrows the structure in both single and multilayers. Transformation in thinner alloy layers is governed by epitaxial forces which stabilize single-phase c-Zr0.4Al0.6N, which enables c-Zr0.4Al0.6N/TiN superlattice growth at temperatures as low as 350 degrees C. Regardless of the decomposition route, the formation of c-AlN is impeded and w-AlN instantaneously forms during transformation. In contrast, isostructural decomposition into w-AlN and w-Zr (Al)N occurs in w-Zr0.4Al0.6N alloys during annealing.
|
|
| 7. |
- Ghafoor, Naureen, et al.
(författare)
-
Self-structuring in Zr1-xAlxN films as a function of composition and growth temperature
- 2018
-
Ingår i: Scientific Reports. - : NATURE PUBLISHING GROUP. - 2045-2322. ; 8
-
Tidskriftsartikel (refereegranskat)abstract
- Nanostructure formation via surface-diffusion-mediated segregation of ZrN and AIN in Zr1-xAlxN films during high mobility growth conditions is investigated for 0 amp;lt;= x amp;lt;= 1. The large immiscibility combined with interfacial surface and strain energy balance resulted in a hard nanolabyrinthine lamellar structure with well-defined (semi) coherent c-ZrN and w-AlN domains of sub-nm to similar to 4 nm in 0.2 amp;lt;= x amp;lt;= 0.4 films, as controlled by atom mobility. For high AlN contents (x amp;gt; 0.49) Al-rich ZrN domains attain wurtzite structure within fine equiaxed nanocomposite wurtzite lattice. Slow diffusion in wurtzite films points towards crystal structure dependent driving force for decomposition. The findings of unlikelihood of isostructural decomposition in c-Zr1-xAlxN, and stability of w-Zr1-xAlxN (in large x films) is complemented with first principles calculations.
|
|
| 8. |
- Hsiao, Ching-Lien, et al.
(författare)
-
Composition tunable Al1-xInxN nanorod arrays grown by ultra-high-vacuum magnetron sputter epitaxy
- 2011
-
Annan publikation (övrigt vetenskapligt/konstnärligt)abstract
- Self-assembled ternary Al1-xInxN nanorod arrays with variable In concentration, 0.10 ≤ x ≤ 0.32 have been realized onto c-plane sapphire substrates by ultra-high-vacuum magnetron sputter epitaxy with Ti0.21Zr0.79N or VN seed layers assistance. The formation of nanorods was very sensitive to the applied seed layer. Without proper seed layer assistance a continuous Al1-xInxN film was grown. The nanorods exhibit hexagonal crosssections with preferential growth along the c axis. A coaxial rod structure with higher In concentration in the core was observed by (scanning) transmission electron microscopy in combination with low-loss electron energy loss spectroscopy and energy dispersive xray spectroscopy. 5 K cathodoluminescence spectroscopy of Al0.86In0.14N nanorods revealed band edge emission at ~5.46 eV, which was accompanied by a strong defectrelated emission at ~ 3.38 eV.
|
|
| 9. |
- Hsiao, Ching-Lien, et al.
(författare)
-
Curved-lattice epitaxial growth of chiral AlInN twisted nanorods for optical applications
- 2012
-
Annan publikation (övrigt vetenskapligt/konstnärligt)abstract
- Despite of using chiral metamaterials to manipulate light polarization states has been demonstrated their great potential for applications such as invisible cloaks, broadband or wavelength-tunable circular polarizers, microreflectors, etc. in the past decade [1-6], operating wavelength in ultraviolet-visible range is still a challenge issue. Since these chiral structures often consist of metallic materials, their operation is designed for the infrared and microwave regions [2-4]. Here, we show how a controlled curved-lattice epitaxial growth (CLEG) of wide-bandgap AlInN semiconductor curved nanocrystals [7] can be exploited as a novel route for tailoring chiral nanostructures in the form of twisted nanorods (TNRs). The fabricated TNRs are shown to reflect light with a high degree of polarization as well as a high degree of circular polarization (that is, nearly circularly polarized light) in the ultravioletvisible region. The obtained polarization is shown to be dependent on the handedness of the TNRs.
|
|
| 10. |
- Hsiao, Ching-Lien, et al.
(författare)
-
Curved-Lattice Epitaxial Growth of InxAl1-xN Nanospirals with Tailored Chirality
- 2015
-
Ingår i: Nano letters (Print). - : American Chemical Society (ACS). - 1530-6984 .- 1530-6992. ; 15:1, s. 294-300
-
Tidskriftsartikel (refereegranskat)abstract
- Chirality, tailored by external morphology and internal composition, has been realized by controlled curved-lattice epitaxial growth (CLEG) of uniform coatings of single-crystalline InxAl1-xN nanospirals. The nanospirals are formed by sequentially stacking segments of curved nanorods on top of each other, where each segment is incrementally rotated around the spiral axis. By controlling the growth rate, segment length, rotation direction, and incremental rotation angle, spirals are tailored to predetermined handedness, pitch, and height. The curved morphology of the segments is a result of a lateral compositional gradient across the segments while maintaining a preferred crystallographic growth direction, implying a lateral gradient in optical properties as well. Left- and right-handed nanospirals, tailored with 5 periods of 200 nm pitch, as confirmed by scanning electron microscopy, exhibit uniform spiral diameters of ~80 nm (local segment diameters of ~60 nm) with tapered hexagonal tips. High resolution electron microscopy, in combination with nanoprobe energy dispersive X-ray spectroscopy and valence electron energy loss spectroscopy, show that individual nanospirals consist of an In-rich core with ~15 nm-diameter hexagonal cross-section, comprised of curved basal planes. The core is surrounded by an Al-rich shell with a thickness asymmetry spiraling along the core. The ensemble nanospirals, across the 1 cm2 wafers, show high in-plane ordering with respect to shape, crystalline orientation, and direction of compositional gradient. Mueller matrix spectroscopic ellipsometry shows that the tailored chirality is manifested in the polarization state of light reflected off the CLEG nanospiral-coated wafers. In that, the polarization state is shown to be dependent on the handedness of the nanospirals and the wavelength of the incident light in the ultraviolet-visible region.
|
|