| 1. |
- Lima, Raquel Bohn, et al.
(författare)
-
Direct lignin fuel cell for power generation
- 2013
-
Ingår i: RSC Advances. - : Royal Society of Chemistry (RSC). - 2046-2069. ; 3:15, s. 5083-5089
-
Tidskriftsartikel (refereegranskat)abstract
- Lignin, the second most abundant component after cellulose in biomass, has been examined in this study as a fuel for direct conversion into electricity using direct carbon fuel cells (DCFC). Two different types of industrial lignins were investigated: Lignosulfonate (LS) and Kraft lignin (KL), in their commercial forms, after their blending with commercial active carbon (AC) or after alteration of their structures by a pH adjustment to pH 10. It was found that the open circuit voltage (OCV) of the DCFC could reach around 0.7 V in most of the trials. Addition of active carbon increased the maximum current density from 43-57 to 83-101 mA cm(-2). The pH adjustment not only increased the maximum current density but also reduced the differences between the two types of lignins, resulting in an OCV of 0.68-0.69 V and a maximum current density of 74-79 mA cm(-2) from both lignins. Typical power density was 12 (for KL + AC) and 24 mW cm(-2) (for LS + AC). It is concluded that a direct lignin fuel cell is feasible and the lignin hydrophilicity is critical for the cell performance.
|
|
| 2. |
- Lima, Raquel B., et al.
(författare)
-
Direct lignin fuel cell for power generation
- 2011
-
Ingår i: 16th International Symposium on Wood, Fiber and Pulping Chemistry. ; , s. 257-262
-
Konferensbidrag (refereegranskat)abstract
- Lignin, the second most abundant component after cellulose in biomass, has been examined in this study as a fuel for a direct conversion into electricity using direct carbon fuel cell (DCFC). Two different types of industrial lignins were investigated: lignosulphonate (LS) and kraft lignin (KL), either directly in their commercial forms, after their blending with commercial active carbon (AC) or after alternation of their structures by a pH adjustment to pH 10. It has been found that the open circuit voltage (OCV) of the DCFC could reach around 0.7 V in most of the trials. Addition of active carbon increased the maximum current density from 43∼57 to 85∼101 mA/cm 2. The pH adjustment not only increased the maximum current density but also reduced the differences between the two types of lignins, resulting in an OCV of 0.680-0.699 V and a maximum current density of 74∼79 mA/cm 2 from both lignins. Typical power density was 12 (for KL +AC) and 24 mW cm -2 (for LS +AC). It has been concluded that a direct lignin fuel cell is feasible and the lignin hydrophilicity is critical for the cell performance.
|
|