| 1. |
- Ajmal Khan, Muhammad, et al.
(författare)
-
Comparative study of the nano-composite electrolytes based on samaria-doped ceria for low temperature solid oxide fuel cells (LT-SOFCs)
- 2013
-
Ingår i: International journal of hydrogen energy. - : Elsevier BV. - 0360-3199 .- 1879-3487. ; 38:36, s. 16524-16531
-
Tidskriftsartikel (refereegranskat)abstract
- Ceria-based electrolyte materials have great potential in low and intermediate temperature solid oxide fuel cell applications. In the present study, three types of ceria-based nanocomposite electrolytes (LNK-SDC, LN-SDC and NK-SDC) were synthesized. One-step co-precipitation method was adopted and different techniques were applied to characterize the obtained ceria-based nano-composite electrolyte materials. TGA, XRD and SEM were used to analyze the thermal effect, crystal structure and morphology of the materials. Cubic fluorite structures have been observed in all composite electrolytes. Furthermore, the crystallite sizes of the LN-SDC, NK-SDC, LNK-SDC were calculated by Scherrer formula and found to be in the range 20 nm, 21 nm and 19 nm, respectively. These values emphasize a good agreement with the SEM results. The ionic conductivities were measured using EIS (Electrochemical Impedance Spectroscopy) with two-probe method and the activation energies were also calculated using Arrhenius plot. The maximum power density was achieved 484 mW/cm(2) of LNK-SDC electrolyte at 570 degrees C using the LiCuZnNi oxide electrodes.
|
|
| 2. |
- Khan, M. Ajmal, et al.
(författare)
-
Effect of titania concentration on the grain boundary conductivity of calcium-doped ceria electrolyte
- 2014
-
Ingår i: Ceramics International. - : Elsevier BV. - 0272-8842 .- 1873-3956. ; 40:7, s. 9775-9781
-
Tidskriftsartikel (refereegranskat)abstract
- A solid-state technique was used to synthesize ceria-based (CDC-xT, in which x=0-1 mol%) solid electrolyte ceramics. The effects of doping the ceramic solid electrolyte (CDC) with titanium oxide were studied with regard to densification, crystal structure, morphology, electro-impedance spectroscopy and fuel cell performance. TiO2 doping afforded materials a 95% relative density at 940 degrees C, approximately 200 degrees C lower than the temperature required without titanium oxide. The addition of titanium oxide (TiO2) reduced the CDC sintering temperature and significantly improved the grain boundary conduction. The minimum grain boundary resistivity was obtained at 0.8 mol% TiO2. X-ray diffraction (XRD) results showed that the lattice parameters enhanced with increased titanium oxide concentrations up to 0.8 mol%, revealing the solubility limit for Caria's fluorite structure. The optimum doping level (0.8 mol%) is provided maximum conductivity. Conductivities were measured using EIS (Electrochemical Impedance Spectroscopy) with a two-probe method, and the activation energies were calculated using the Arrhenius plots. The maximum power density (660 mW/cm(2)) was achieved with CDC 0.8T electrolyte at 650 degrees C using LiCuZnNi oxide electrodes.
|
|