| 1. |
- Abbas, Ghazanfar, et al.
(författare)
-
Electrochemical investigation of mixed metal oxide nanocomposite electrode for low temperature solid oxide fuel cell
- 2017
-
Ingår i: International Journal of Modern Physics B. - : WORLD SCIENTIFIC PUBL CO PTE LTD. - 0217-9792. ; 31:27
-
Tidskriftsartikel (refereegranskat)abstract
- Zinc-based nanostructured nickel (Ni) free metal oxide electrode material Zn-0.60/CU0.20Mn0.20 oxide (CMZO) was synthesized by solid state reaction and investigated for low temperature solid oxide fuel cell (LTSOFC) applications. The crystal structure and surface morphology of the synthesized electrode material were examined by XRD and SEM techniques respectively. The particle size of ZnO phase estimated by Scherer's equation was 31.50 nm. The maximum electrical conductivity was found to be 12.567 S/cm and 5.846 S/cm in hydrogen and air atmosphere, respectively at 600 degrees C. The activation energy of the CMZO material was also calculated from the DC conductivity data using Arrhenius plots and it was found to be 0.060 and 0.075 eV in hydrogen and air atmosphere, respectively. The CMZO electrode-based fuel cell was tested using carbonated samarium doped ceria composite (NSDC) electrolyte. The three layers 13 mm in diameter and 1 mm thickness of the symmetric fuel cell were fabricated by dry pressing. The maximum power density of 728.86 mW/cm(2) was measured at 550 degrees C.
|
|
| 2. |
- Abbas, Ghazanfar, et al.
(författare)
-
Synthesize and characterization of nanocomposite anodes for low temperature solid oxide fuel cell
- 2015
-
Ingår i: International journal of hydrogen energy. - : Elsevier BV. - 0360-3199 .- 1879-3487. ; 40:1, s. 891-897
-
Tidskriftsartikel (refereegranskat)abstract
- Solid oxide fuel cells have much capability to become an economical alternative energy conversion technology having appropriate materials that can be operated at comparatively low temperature in the range of 400-600 degrees C. The nano-scale engineering has been incorporated to improve the catalytic activity of anode materials for solid oxide fuel cells. Nanostructured Al0.10NixZn0.90-xO oxides were prepared by solid state reaction, which were then mixed with the prepared Gadolinium doped Ceria GDC electrolyte. The crystal structure and surface morphology were characterized by XRD and SEM. The particle size was evaluated by XRD data and found in the range of 20-50 nm, which was then ensured by SEM pictures. The pellets of 13 mm diameter were pressed by dry press technique and electrical conductivities (DC and AC) were determined by four probe techniques and the values have been found to be 10.84 and 4.88 S/cm, respectively at hydrogen atmosphere in the temperature range of 300-600 degrees C. The Electrochemical Impedance Spectroscopy (EIS) analysis exhibits the pure electronic behavior at hydrogen atmosphere. The maximum power density of ANZ-GDC composite anode based solid oxide fuel cell has been achieved 705 mW/cm(2) at 550 degrees C.
|
|
| 3. |
- Ali, A., et al.
(författare)
-
Effect of Alkali Carbonates (Single, Binary, and Ternary) on Doped Ceria : A Composite Electrolyte for Low-Temperature Solid Oxide Fuel Cells
- 2018
-
Ingår i: ACS Applied Materials and Interfaces. - : American Chemical Society (ACS). - 1944-8244 .- 1944-8252. ; 10:1, s. 806-818
-
Tidskriftsartikel (refereegranskat)abstract
- Samarium-doped ceria (SDC) carbonate has become an attractive electrolyte for fuel cells because of its remarkable ion conductivity and high performance. Different doped ceria-carbonate (single-carbonate SDC, binary-carbonate SDC, and ternary-carbonate SDC) electrolytes were synthesized by the coprecipitation/oxalate method, to optimize the electrochemical performance. The structure; morphology; and thermal, optical, and surface properties have been studied using a variety of techniques. The X-ray diffraction results confirmed the successful incorporation of samarium into ceria as a crystalline structure and inclusion of carbonate, which is amorphous in nature. To analyze the conduction mechanism, direct current conductivity was measured in a H2/O2 atmosphere. Doped ceria-binary carbonate ((Li/Na)CO3-SDC) showed the best conductivity of 0.31 S cm-1 and power density of 617 mW cm-2, at 600 °C. The enhancement in the ionic conductivity and performance of the composites is due to the contribution of hybrid ions (O2-, H+). The crystallite size of the composites was in the range 21-41 nm. For the calculation of band gaps, optical absorption spectra of the synthesized powders were analyzed, and they showed a red shift with the band gap energy in the range 2.6-3.01 eV, when compared to that of pure ceria (3.20 eV).
|
|
| 4. |
- Hussain, Fida, et al.
(författare)
-
A modeling approach for low-temperature SOFC-based micro-combined heat and power systems
- 2019
-
Ingår i: International Journal of Modern Physics B. - : WORLD SCIENTIFIC PUBL CO PTE LTD. - 0217-9792. ; 33:4
-
Tidskriftsartikel (refereegranskat)abstract
- The world's challenge is to determine a more efficient, economical and environmental-friendly energy source to compete and replace the ongoing conventional energy resources. Solid oxide fuel cells (SOFCs) provide a highly efficient system to use divergent energy resources and have proved to provide the cleanest energy, least energy use, and lowest emissions. A techno-economic study is required to investigate the model design for SOFC-based micro-combined heat and power (m-CHP) systems for applications in terms of educational and commercial buildings. This work models and explores the optimized application of hydrogen gas-fueled SOFC-based m-CHP systems in educational buildings. Two educational departments' loads are presented and model of SOFC-based m-CHP system against the different electric power demands is performed, in order to provide a techno-economic assessment of the technology. For successful development of the technology, results are related to system rightsizing, operating strategies, thermal to electric ratios, and match between end-use, with an aim towards classifying the overall feasibility and essential application requirements.
|
|
| 5. |
- Khan, M. Ajmal, et al.
(författare)
-
Effect of titania concentration on the grain boundary conductivity of calcium-doped ceria electrolyte
- 2014
-
Ingår i: Ceramics International. - : Elsevier BV. - 0272-8842 .- 1873-3956. ; 40:7, s. 9775-9781
-
Tidskriftsartikel (refereegranskat)abstract
- A solid-state technique was used to synthesize ceria-based (CDC-xT, in which x=0-1 mol%) solid electrolyte ceramics. The effects of doping the ceramic solid electrolyte (CDC) with titanium oxide were studied with regard to densification, crystal structure, morphology, electro-impedance spectroscopy and fuel cell performance. TiO2 doping afforded materials a 95% relative density at 940 degrees C, approximately 200 degrees C lower than the temperature required without titanium oxide. The addition of titanium oxide (TiO2) reduced the CDC sintering temperature and significantly improved the grain boundary conduction. The minimum grain boundary resistivity was obtained at 0.8 mol% TiO2. X-ray diffraction (XRD) results showed that the lattice parameters enhanced with increased titanium oxide concentrations up to 0.8 mol%, revealing the solubility limit for Caria's fluorite structure. The optimum doping level (0.8 mol%) is provided maximum conductivity. Conductivities were measured using EIS (Electrochemical Impedance Spectroscopy) with a two-probe method, and the activation energies were calculated using the Arrhenius plots. The maximum power density (660 mW/cm(2)) was achieved with CDC 0.8T electrolyte at 650 degrees C using LiCuZnNi oxide electrodes.
|
|
| 6. |
- Khan, M. Ajmal, et al.
(författare)
-
Synthesize and characterization of ceria based nano-composite materials for low temperature solid oxide fuel cell
- 2018
-
Ingår i: International journal of hydrogen energy. - : PERGAMON-ELSEVIER SCIENCE LTD. - 0360-3199 .- 1879-3487. ; 43:12, s. 6310-6317
-
Tidskriftsartikel (refereegranskat)abstract
- The present study is focused on ceria based mixed (ionic and electronic conductor) composite Al0.05Ni0.1Ti0.05Zn0.80-SDC (ATZN-SDC) oxide material was prepared by solid state reaction, which can be used as anode materials for solid oxide fuel cell. The effect of Ti and Al oxides were analyzed on the NiZn-SDC composite with respect to its conductivity and catalytic activity in hydrogen atmosphere. The average crystallite size of the composite was found to be 40-100 nm by XRD and SEM. The DC conductivity was determined by 4-probe technique. The electrochemical impedance spectrum (EIS) was also examined in hydrogen atmosphere within a temperature range of 350-550 degrees C. The maximum power density 370 mW/cm(2) was achieved at 650 degrees C.
|
|
| 7. |
- Rafique, Asia, et al.
(författare)
-
Multioxide phase-based nanocomposite electrolyte (M@SDC where M = Zn2+ / Ba2+/ La2+/Zr-2/Al3+) materials
- 2020
-
Ingår i: Ceramics International. - : ELSEVIER SCI LTD. - 0272-8842 .- 1873-3956. ; 46:52, s. 6882-6888
-
Tidskriftsartikel (refereegranskat)abstract
- This paper deals with the development of a highly dense and stable electrolyte on the base of nanoionics oxide interface theory. This gives a comparative study of two-phase nanocomposite electrolytes that are developed for low temperature solid oxide fuel cells (LT-SOFCs). These nanocomposites are synthesised with different oxides, which are coated on the doped ceria that showed high oxide ion mobility for LT-SOFCs. These novel two-phase nanocomposite oxide ionic conductors (MCe0.8Sm0.2O2-MO2, where M = Zn2+/Ba2+/La3+/Zr2+/Al3+) were synthesised by a co-precipitation method. The interface study between these two phases was analysed by electrochemical impedance spectroscopy (EIS), while ionic conductivities were measured with DC conductivity (four probe method). The nanocomposite electrolytes exhibited higher conductivities with the increase of concentration of coated oxides but decreased at a certain level. The structural or morphological properties of the nanocomposite electrolytes were examined by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The thermal stability was investigated using thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The maximum performance of 590 mW/cm(2) at 550 degrees C was obtained for the Zn@SDC based cell, and the rest of the coated samples Ba@SDC, La@SDC, Zr@SDC and Al@SDC based cells showed values of 550 mW/cm(2), 540 mW/cm(2), 450 mW/cm(2), 340 mW/cm(2), respectively, with hydrogen as a fuel. Therefore, the coated-SDC based nanocomposite materials are a good approach for lowering the operating temperature to achieve the challenges of the solid oxide fuel cells (SOFC). These two-phase nanocomposite electrolytes satisfy the all requirements which one electrolyte should have, like high ionic conduction, thermodynamic stability and negligible electronic conduction.
|
|
| 8. |
- Rafique, Asia, et al.
(författare)
-
Significance enhancement in the conductivity of core shell nanocomposite electrolytes
- 2015
-
Ingår i: RSC Advances. - : Royal Society of Chemistry. - 2046-2069. ; 5:105, s. 86322-86329
-
Tidskriftsartikel (refereegranskat)abstract
- Today, there is great demand of electrolytes with high ionic conductivities at low operating temperatures for solid-oxide fuel cells. Therefore, a co-doped technique was used to synthesize a highly ionically conductive two phase nanocomposite electrolyte Sr/Sm-ceria-carbonate by a co-precipitation method. A significant increase in conductivity was measured in this co-doped Sr/Sm-ceria-carbonate electrolyte at 550 degrees C as compared to the more commonly studied samarium doped ceria. The fuel cell power density was 900 mW cm(-2) at low temperature (400-580 degrees C). The composite electrolyte was found to have homogenous morphology with a core-shell structure using SEM and TEM. The two phase core-shell structure was confirmed using XRD analysis. The crystallite size was found to be 30-60 nm and is in good agreement with the SEM analysis. The thermal analysis was determined with DSC. The enhancement in conductivity is due to two effects; co-doping of Sr in samarium doped ceria and it's composite with carbonate which is responsible for the core-shell structure. This co-doped approach with the second phase gives promise in addressing the challenge to lower the operating temperature of solid oxide fuel cells (SOFC).
|
|
| 9. |
- Raza, Rizwan, et al.
(författare)
-
Composite electrolyte with proton conductivity for low-temperature solid oxide fuel cell
- 2015
-
Ingår i: Applied Physics Letters. - : American Institute of Physics (AIP). - 0003-6951 .- 1077-3118. ; 107:18
-
Tidskriftsartikel (refereegranskat)abstract
- In the present work, cost-effective nanocomposite electrolyte (Ba-SDC) oxide is developed for efficient low-temperature solid oxide fuel cells (LTSOFCs). Analysis has shown that dual phase conduction of O-2 (oxygen ions) and H+ (protons) plays a significant role in the development of advanced LTSOFCs. Comparatively high proton ion conductivity (0.19 s/cm) for LTSOFCs was achieved at low temperature (460°C). In this article, the ionic conduction behaviour of LTSOFCs is explained by carrying out electrochemical impedance spectroscopy measurements. Further, the phase and structure analysis are investigated by X-ray diffraction and scanning electron microscopy techniques. Finally, we achieved an ionic transport number of the composite electrolyte for LTSOFCs as high as 0.95 and energy and power density of 90% and 550 mW/cm2, respectively, after sintering the composite electrolyte at 800°C for 4 h, which is promising. Our current effort toward the development of an efficient, green, low-temperature solid oxide fuel cell with the incorporation of high proton conductivity composite electrolyte may open frontiers in the fields of energy and fuel cell technology.
|
|
| 10. |
- Tariq, S., et al.
(författare)
-
Comparative study of Ce0.80Sm0.20 Ba0.80Y0.20O3-δ (YB-SDC) electrolyte by various chemical synthesis routes
- 2018
-
Ingår i: Results in Physics. - : Elsevier B.V.. - 2211-3797. ; 8, s. 780-784
-
Tidskriftsartikel (refereegranskat)abstract
- Solid Oxide Fuel Cells is received a significant attention in recent years due to higher efficiency and fuel flexibility. The one of the main challenge for SOFC is to lower the operating temperature of SOFCs. Therefore, different strategies are used in order to enhance the ionic conduction of electrolyte, which can lower the overall SOFC operating temperature. The present work is focused on this strategy to enhance the electrolytic conductivity. Therefore, the ceria based composite electrolytes Ce0.80Sm0.20B0.80Y0.20O3-δ (YBSDC) are synthesized using three different approaches i.e. co-precipitation (YBSDC-1), sol-gel (YBSDC-2) and ball milling (YBSDC-3). Their crystal structures and surface morphologies are characterized through X-ray Diffraction (XRD) and Scanning Electron Microscopy (SEM) techniques, respectively. The four-probe technique is employed to measure their dc conductivities in the temperature range (300–700) °C under air atmosphere. The open circuit voltage (OCV) and current are recorded with natural gas as fuel {flow rate kept at 100 ml min−1 at 1 atm pressure} over the temperature range (300–600) °C. The electrolyte (YBSDC-1) prepared by co-precipitation technique is shown better results as compare to other two electrolytes (YBSDC-2 and YBSDC-3). The electrolyte (YBSDC-1) having maximum dc conductivity (0.096 S/cm), peak power density 224 mW cm−2 and OCV 0.94 V at 600 °C. These results show that YBSDC-1electrolyte is potential candidate for low temperature SOFCs.
|
|