| 1. |
- Sul, Young-Taeg, 1960, et al.
(författare)
-
Characteristics of the surface oxides on turned and electrochemically oxidized pure titanium implants up to dielectric breakdown: the oxide thickness, micropore configurations, surface roughness, crystal structure and chemical composition.
- 2002
-
Ingår i: Biomaterials. - 0142-9612 .- 1878-5905. ; 23:2, s. 491-501
-
Tidskriftsartikel (refereegranskat)abstract
- Titanium implants have been used widely and successfully for various types of bone-anchored reconstructions. It is believed that properties of oxide films covering titanium implant surfaces are of crucial importance for a successful osseointegration, in particular at compromized bone sites. The aim of the present study is to investigate the surface properties of anodic oxides formed on commercially pure (c.p.) titanium screw implants as well as to study 'native' oxides on turned c.p. titanium implants. Anodic oxides were prepared by galvanostatic mode in CH3COOH up to the high forming voltage of dielectric breakdown and spark formation. The oxide thicknesses, measured with Auger electron spectroscopy (AES), were in the range of about 200-1000 nm. Barrier and porous structures dominated the surface morphology of the anodic film. Quantitative morphometric analyses of the micropore structures were performed using an image analysis system on scanning electron microscopy (SEM) negatives. The pore sizes were
|
|
| 2. |
- Sul, Young-Taeg, 1960, et al.
(författare)
-
Oxidized implants and their influence on the bone response.
- 2001
-
Ingår i: Journal of Materials Science: Materials in Medicine. - 0957-4530. ; 12:10-12, s. 1025-31
-
Tidskriftsartikel (refereegranskat)abstract
- Surface oxide properties are regarded to be of great importance in establishing successful osseointegration of titanium implants. Despite a large number of theoretical questions on the precise role of oxide properties of titanium implants, current knowledge obtained from in vivo studies is lacking. The present study is designed to address two aspects. The first is to verify whether oxide properties of titanium implants indeed influence the in vivo bone tissue responses. The second, is to investigate what oxide properties underline such bone tissue responses. For these purposes, screw-shaped/turned implants have been prepared by electrochemical oxidation methods, resulting in a wide range of oxide properties in terms of: (i) oxide thickness ranging from 200 to 1000 nm, (ii) the surface morphology of barrier and porous oxide film structures, (iii) micro pore configuration - pore sizes<8 microm by length, about 1.27 microm2 to 2.1 microm2 by area and porosity of about 12.7-24.4%, (iv) the crystal structures of amorphous, anatase and mixtures of anatase and rutile type, (v) the chemical compositions of TiO2 and finally, (vi) surface roughness of 0.96-1.03 microm (Sa). These implant oxide properties were divided into test implant samples of Group II, III, IV and V. Control samples (Group I) were turned commercially pure titanium implants. Quantitative bone tissue responses were evaluated biomechanically by resonance frequency analysis (RFA) and removal torque (RT) test. Quantitative histomorphometric analyses and qualitative enzyme histochemical detection of alkaline (ALP) and acidic phosphatase (ACP) activities were investigated on cut and ground sections after six weeks of implant insertion in rabbit tibia. In essence, from the biomechanical and quantitative histomorphometric measurements we concluded that oxide properties of titanium implants, i.e. the oxide thickness, the microporous structure, and the crystallinity significantly influence the bone tissue response. At this stage, however, it is not clear whether oxide properties influence the bone tissue response separately or synergistically. Copyright 2001 Kluwer Academic Publishers
|
|
| 3. |
- Sul, Young-Taeg, 1960, et al.
(författare)
-
Resonance frequency and removal torque analysis of implants with turned and anodized surface oxides.
- 2002
-
Ingår i: Clin Oral Implants Res. - 0905-7161. ; 13:3, s. 252-9
-
Tidskriftsartikel (refereegranskat)abstract
- The present experimental study was designed to address two issues. The first was to investigate whether oxide properties of titanium implants influenced bone tissue responses after an in vivo implantation time of six weeks. If such a result was found, the second aim was to investigate which oxide properties are involved in such bone tissue responses. Screw-shaped implants with a wide range of oxide properties were prepared by electrochemical oxidation methods, where the oxide thickness varied in the range of 200 nm to 1000 nm. The surface morphology was prepared in two substantially different ways, i.e. barrier and porous oxide film structures. The micropore structure revealed pore sizes of 8 microm in diameter, with a range in opening area from 1.27 microm 2 to 2.1 microm 2. Porosity ranged from 12.7% to 24.4%. The crystal structures of the titanium oxide were amorphous, anatase and a mixture of anatase and rutile type. The chemical compositions consisted mainly of TiO2. Surface roughness ranged from 0.96 microm to 1.03 microm (Sa). Each group of test samples showed its own, defined status with respect to these various parameters. The oxide properties of turned commercially pure titanium implants were used in the control group, which was characterized by an oxide thickness of 17.4 +/- 6.2 nm, amorphous type in crystallinity, TiO2 in chemical composition, and a surface roughness of 0.83 microm (Sa). Bone tissue responses were evaluated by resonance frequency measurements and removal torque tests that were undertaken six weeks after implant insertion in rabbit tibia. Implants that had an oxide thickness of approximately 600, 800 and 1000 nm demonstrated significantly stronger bone responses in the evaluation of removal torque values than did implants that had an oxide thickness of approximately 17 and 200 nm (P < 0.05). However, there were no difference between implants with oxide thicknesses of 17 and 200 nm (P = 0.99). It was concluded that oxide properties of titanium implants, which include oxide thickness, micropore configurations and crystal structures, greatly influence the bone tissue response in the evaluation of removal torque values. However, it is not fully understood whether these oxide properties influence the bone tissue response separately or synergistically.
|
|