| 1. |
- Zhang, L., et al.
(författare)
-
Study on the adhesion strength of new nano-structured polymer-metal composite for thermal interface material (Nano-TIM) under different pressures
- 2011
-
Ingår i: Proceedings - 12th International Conference on Electronic Packaging Technology and High Density Packaging, ICEPT-HDP 2011, Shanghai, 8-11 August 2011. - 9781457717680 ; , s. 426-429
-
Konferensbidrag (refereegranskat)abstract
- With the continual increase in cooling demand for microprocessors, the microelectronics industry has been increasingly focused on the development of thermal solutions. Thermal Interface Material (TIM) plays a key role in reducing the thermal resistance of packaging and the thermal resistance between the electronic device and the external cooling components. Nano-TIM, a new type of thermal interface material, was developed to improve the heat dissipation of electronic devices. This paper describes work undertaken to research the reliability of Nano-TIM. Pull tests were used to investigate the shear strength of samples with Nano-TIM of different thicknesses coalesced between two PCBs with Sn coating made under different pressure. Scanning Electron Microscopy (SEM) analysis techniques were used to determine the morphology of the shear fracture section after pull tests and observe the structure of the cross section of Nano-TIM coalesced between two PCBs with Sn coating.
|
|
| 2. |
- Zandira, Masoud, 1983, et al.
(författare)
-
Fracture Characteristics of Austempered Spheroidal Graphite Aluminum Cast Irons
- 2010
-
Ingår i: Journal of Iron and Steel Research International. - 1006-706X. ; 17:2, s. 31-35
-
Tidskriftsartikel (refereegranskat)abstract
- The fracture characteristics of austempered spheroidal graphite aluminum cast iron had been investigated. The chemical content of the alloy was C3.2, Al2.2, Ni0.8 and Mg0.05 (in mass percent, %). Impact test samples were produced from keel blocks cast in CO2 molding process. The oversized impact samples were austenitized at 850 and 950 degrees C for 2 h followed by austempering at 300 and 400 degrees C for 30, 60, 120 and 180 min. The austempered samples were machined and tested at room temperature. The impact strength values for those samples austempered at 400 degrees C varied between 90 and 110J. Lower bainitic structures showed impact strength values of 22 to 50J. The fractures of the samples were examined using SEM. The results showed that the upper bainitic fracture revealed a honey Comb-like topography, which confirmed the ductile fracture behavior. The lower bainitic fractures of those samples austempered for short times revealed brittle fracture.
|
|