| 1. |
- Jonnalagadda, Krishna Praveen, 1988-, et al.
(författare)
-
Failure of Multilayer Suspension Plasma Sprayed Thermal Barrier Coatings in the Presence of Na2SO4 and NaCl at 900 °C
- 2019
-
Ingår i: Journal of thermal spray technology (Print). - : Springer Science and Business Media LLC. - 1059-9630 .- 1544-1016. ; 28:1-2, s. 212-222
-
Tidskriftsartikel (refereegranskat)abstract
- The current investigation focuses on understanding the influence of a columnar microstructure and a sealing layer on the corrosion behavior of suspension plasma sprayed thermal barrier coatings (TBCs). Two different TBC systems were studied in this work. First is a double layer made of a composite of gadolinium zirconate + yttria stabilized zirconia (YSZ) deposited on top of YSZ. Second is a triple layer made of dense gadolinium zirconate deposited on top of gadolinium zirconate + YSZ over YSZ. Cyclic corrosion tests were conducted between 25 and 900 °C with an exposure time of 8 h at 900 °C. 75 wt.% Na2SO4 + 25 wt.% NaCl were used as the corrosive salts at a concentration of 6 mg/cm2. Scanning electron microscopy analysis of the samples’ cross sections showed that severe bond coat degradation had taken place for both the TBC systems, and the extent of bond coat degradation was relatively higher in the triple-layer system. It is believed that the sealing layer in the triple-layer system reduced the number of infiltration channels for the molten salts which resulted in overflowing of the salts to the sample edges and caused damage to develop relatively more from the edge.
|
|
| 2. |
- Jonnalagadda, Krishna Praveen, 1988-, et al.
(författare)
-
Hot gas corrosion and its influence on the thermal cycling performance of suspension plasma spray TBCs
- 2019
-
Ingår i: Proceedings of ASME Turbo Expo 2019. - New York, NY : American Society of Mechanical Engineers. - 9780791858677
-
Konferensbidrag (refereegranskat)abstract
- Thermal barrier coatings (TBCs) manufactured with suspension plasma spray (SPS) are promising candidates for use in gas turbines due to their high strain tolerance during thermal cyclic fatigue (TCF). However, corrosion often occurs alongside thermal fatigue and coating durability under these conditions is highly desirable. The current study focuses on understanding the corrosion behavior and its influence on the thermal cyclic fatigue life of SPS TBCs. Corrosion tests were conducted at 780 OC using a mixed-gas (1SO2-0.1CO-20CO2-N2(bal.) in vol. %) for 168h. They were later thermally cycled between 100-1100 ⁰C with a 1h hold time at 1100 ⁰C. Corrosion test results indicated that the damage predominantly started from the edges and a milder damage was observed at the center. Nickel sulfide was observed on top of the top coat and also in the columnar gaps of the top coat. Chromium oxides were observed inside the top coat columnar gaps but close to the bond coat/top coat interface. They were believed to reduce the strain tolerance of SPS TBCs to an extent and also amplify the thermal mismatch stresses during TCF tests. This, together with a fast growth of alumina during the TCF, resulted in a significant drop in the TCF life compared to the standard TCF tests.
|
|
| 3. |
- Zhang, Pimin, 1990-, et al.
(författare)
-
Effects of surface finish on the initial oxidation of HVAF-sprayed NiCoCrAlY coatings
- 2019
-
Ingår i: Surface & Coatings Technology. - Elsevier : Elsevier BV. - 0257-8972 .- 1879-3347. ; 364, s. 43-56
-
Tidskriftsartikel (refereegranskat)abstract
- Oxide scale formed on HVAF-sprayed NiCoCrAlY coatings and the effect of surface treatment were investigated by a multi-approach study combining photo-stimulated luminescence, microstructural observation and mass gain. The initial oxidationbehaviour of as-sprayed, polished and shot-peened coatings at 1000 °C is studied. Both polished and shot-peened coatings exhibited superior performance due to rapid formation of α-Al2O3 fully covering the coating and suppressing the growth of transient alumina, assisted by a high density of α-Al2O3 nuclei on surface treatment induced defects. Moreover, the fast development of a two-layer alumina scale consisting of an inward-grown inner α-Al2O3 layer and an outer layer transformed from outward-grown transient alumina resulted in a higher oxide growth rate of the as-sprayed coating.
|
|
| 4. |
- Zhang, Pimin, 1990-, et al.
(författare)
-
Isothermal oxidation behavior of HVAF-sprayed NiCoCrAlY coatings : Effect of surface treatment
- 2017
-
Ingår i: Proceedings of the International Thermal Spray Conference & Exposition (ITSC 2017). - New York : Curran Associates, Inc. - 9781510858220 ; , s. 456-461
-
Konferensbidrag (refereegranskat)abstract
- NiCoCrAlY coatings are widely used as bond coats for ceramic thermal barrier coatings (TBCs) andoxidation and corrosion protective overlay coatings in industrial gas turbines. High temperature oxidation behaviour of NiCoCrAlYs has a great influence on the coating performance and lifetime of TBCs. A promising route to decrease the oxidation rate of such coatings is post-coating surface modification which can facilitate formation of a uniform alumina scale with a considerably slower growth rate compared to the as-sprayed coatings. In this work, the effect of surface treatment by means of shot peening and laser surface melting (LSM) on the oxidation resistance of high velocity air-fuel (HVAF) sprayed NiCoCrAlY coatings was studied. Isothermal oxidation was carried out at 1000⁰C for 1000h. Results showed that the rough surface of as-sprayed HVAF sprayed coatings was significantly changed after shot peening and LSM treatment, with a compact and smooth appearance. After the exposure, the oxide scales formed on surface-treated NiCoCrAlY coatings showed different morphology and growth rate compared to those formed on as-sprayed coating surface. The oxidation behaviour of surface treated HVAF-sprayed NiCoCrAlY coatings were revealed and discussed.
|
|
| 5. |
- Zhang, Xun, et al.
(författare)
-
Determination of local residual stress in an air plasma spray thermal barrier coating (APS-TBC) by microscale ring coring using a picosecond laser
- 2019
-
Ingår i: Scripta Materialia. - : Elsevier BV. - 1359-6462 .- 1872-8456. ; 167, s. 126-130
-
Tidskriftsartikel (refereegranskat)abstract
- A picosecond laser for incremental annular trench cutting is combined with digital image correlation (DIC) to extend the incremental ring-core method to the profiling of residual stress in thick (>100 μm) coatings. In this case the local residual stress in a TBC is depth profiled after exposure to 1150 °C for 190 h. The topcoat was found to be in compression with an average compressive stress of −94 ± 8 MPa which is representative of the stresses that would be generated elastically on cooling from a stress-free temperature of ~970 °C. The stress profile measurements have been validated by high-energy synchrotron X-ray diffraction measurements. © 2019
|
|