- Andersson, Gabriella, et al.
(författare)
-
Influence of compressive biaxial strain on the hydrogen uptake of ultra-thin, single crystal vanadium layers
- 1997
-
Ingår i: Physical Review B. - 0163-1829. ; 55:3, s. 1774-1781
-
Tidskriftsartikel (refereegranskat)abstract
- We have investigated the influence of biaxial compressive strain on the thermodynamic propertied of hydrogen in thin, single-crystal vanadium layers (0.9, 1.6, and 2.0 nm). At H/V<0.1 (atomic ratio), the host-mediated H-H interaction was found to be attractive. For H/V>0.1, the interaction was found to be extremely weak in the 0.9-nm-thick layer and repulsive in the 1.6- and 2.0-nm-thick V layers. The repulsive interaction was found to increase with increasing layer thicknesses. These results are unexpected as the interaction is attractive in both bulk V and in thin vanadium layers under biaxial tensile strain for HV<0.5. Both the strained and unstrained vanadium lattices are found to have roughly the same hydrogen affinity at H/V=0.1 (0.3 eV/H). No ordered bulklike beta phase was observed at any concentration (0
|
|