- Arnalds, U. B., et al.
(författare)
-
A magnetron sputtering system for the preparation of patterned thin films and in situ thin film electrical resistance measurements
- 2007
-
Ingår i: Review of Scientific Instruments. - : AIP Publishing. - 0034-6748 .- 1089-7623. ; 78:10, s. 103901-
-
Tidskriftsartikel (refereegranskat)abstract
- We describe a versatile three gun magnetron sputtering system with a custom made sample holder for in situ electrical resistance measurements, both during film growth and ambient changes on film electrical properties. The sample holder allows for the preparation of patterned thin film structures, using up to five different shadow masks without breaking vacuum. We show how the system is used to monitor the electrical resistance of thin metallic films during growth and to study the thermodynamics of hydrogen uptake in metallic thin films. Furthermore, we demonstrate the growth of thin film capacitors, where patterned films are created using shadow masks.
|
|
| 3. |
- Thorgeirsson, Thorgeir E, et al.
(författare)
-
A variant associated with nicotine dependence, lung cancer and peripheral arterial disease
- 2008
-
Ingår i: Nature. - : Springer Science and Business Media LLC. - 0028-0836 .- 1476-4687. ; 452:7187, s. 9-638
-
Tidskriftsartikel (refereegranskat)abstract
- Smoking is a leading cause of preventable death, causing about 5 million premature deaths worldwide each year(1,2). Evidence for genetic influence on smoking behaviour and nicotine dependence (ND)(3-8) has prompted a search for susceptibility genes. Furthermore, assessing the impact of sequence variants on smoking-related diseases is important to public health(9,10). Smoking is the major risk factor for lung cancer (LC)(11-14) and is one of the main risk factors for peripheral arterial disease (PAD)(15-17). Here we identify a common variant in the nicotinic acetylcholine receptor gene cluster on chromosome 15q24 with an effect on smoking quantity, ND and the risk of two smoking- related diseases in populations of European descent. The variant has an effect on the number of cigarettes smoked per day in our sample of smokers. The same variant was associated with ND in a previous genomewide association study that used low- quantity smokers as controls(18,19), and with a similar approach we observe a highly significant association with ND. A comparison of cases of LC and PAD with population controls each showed that the variant confers risk of LC and PAD. The findings provide a case study of a gene - environment interaction(20), highlighting the role of nicotine addiction in the pathology of other serious diseases.
|
|
| 4. |
- Agustsson, J. S., et al.
(författare)
-
Electrical resistivity and morphology of ultra thin Pt films grown by dc magnetron sputtering on SiO(2)
- 2008
-
Ingår i: Journal of Physics Conference Series. - : IOP Science. - 1742-6596.
-
Konferensbidrag (refereegranskat)abstract
- Ultra thin platinum films were grown by dc magnetron sputtering on thermally oxidized Si (100) substrates. The electrical resistance of the films was monitored in-situ during growth. The coalescence thickness was determined for various growth temperatures and found to increase from 1.3 nm for films grown at room temperature to 1.8 nm for films grown at 250 degrees C, while a continuous film was formed at a thickness of 3.9 nm at room temperature and 3.5 nm at 250 degrees C. The electrical resistivity increases with increased growth temperature, as well as the morphological grain size, and the surface roughness, measured with a scanning tunneling microscope (STM).
|
|
| 5. |
- Agustsson, J. S., et al.
(författare)
-
Growth, coalescence, and electrical resistivity of thin Pt films grown by dc magnetron sputtering on SiO2
- 2008
-
Ingår i: Applied Surface Science. - : Elsevier BV. - 0169-4332 .- 1873-5584. ; 254:22, s. 7356-7360
-
Tidskriftsartikel (refereegranskat)abstract
- Ultra thin platinum films were grown by dc magnetron sputtering on thermally oxidized Si (100) substrates. The electrical resistance of the films was monitored in situ during growth. The coalescence thickness was determined for various growth temperatures and found to increase from 1.1 nm for films grown at room temperature to 3.3 nm for films grown at 400 degrees C. A continuous film was formed at a thickness of 2.9 nm at room temperature and 7.5 nm at 400 degrees C. The room temperature electrical resistivity decreases with increased growth temperature, while the in-plain grain size and the surface roughness, measured with a scanning tunneling microscope (STM), increase. Furthermore, the temperature dependence of the film electrical resistance was explored at various stages during growth.
|
|
| 6. |
- Gylfason, Kristinn B., 1978-, et al.
(författare)
-
In-situ resistivity measurements during growth of ultra-thin Cr_0.7Mo_0.3
- 2006
-
Ingår i: Thin Solid Films. - : Elsevier. - 0040-6090 .- 1879-2731. ; 515:2, s. 583-586
-
Tidskriftsartikel (refereegranskat)abstract
- The growth of ultra-thin, lattice matched, Cr0.7Mo0.3 films on an MgO substrate, in a dc magnetron discharge, was investigated by in situ measurements in order to determine the minimum thickness of a continuous layer. The thickness dependence of the resistivity shows a coalescence thickness of less than two monolayers indicating layer by layer growth of the films. We compare the resistivity of the films to a combination of the Fuchs- Sondheimer and the Mayadas-Shatzkes models, assuming a thickness dependence of grain size. The model indicates that grain size increases with increasing growth temperature.
|
|