| 1. |
- Halim, Joseph, 1985-, et al.
(författare)
-
Synthesis of Two-Dimensional Nb1.33C (MXene) with Randomly Distributed Vacancies by Etching of the Quaternary Solid Solution (Nb2/3Sc1/3)2AlC MAX Phase
- 2018
-
Ingår i: ACS Applied Nano Materials. - : American Chemical Society (ACS). - 2574-0970. ; 1:6, s. 2455-2460
-
Tidskriftsartikel (refereegranskat)abstract
- Introducing point defects in two-dimensional (2D) materials can alter or enhance their properties. Here, we demonstrate how etching a laminated (Nb2/3Sc1/3)2AlC MAX phase (solid solution) of both the Sc and Al atoms results in a 2D Nb1.33C material (MXene) with a large number of vacancies and vacancy clusters. This method is applicable to any quaternary, or higher, MAX phase, wherein one of the transition metals is more reactive than the other and could be of vital importance in applications such as catalysis and energy storage. We also report, for the first time, on the existence of solid solution (Nb2/3Sc1/3)3AlC2 and (Nb2/3Sc1/3)4AlC3 phases.
|
|
| 2. |
- Mockuté, Aurelija, et al.
(författare)
-
Age hardening in (Ti1-xAlx)B2+Delta thin films
- 2017
-
Ingår i: Scripta Materialia. - : Elsevier BV. - 1359-6462 .- 1872-8456. ; 127, s. 122-126
-
Tidskriftsartikel (refereegranskat)abstract
- Thin films of (Ti0.71Al0.29)B2+1.08 have been deposited by magnetron sputtering. Post-deposition annealing at 1000 degrees C for 1 h results in increased hardness and elastic modulus, from 32 to 37 GPa and from 436 to 461 GPa, respectively. In both as-deposited and annealed states the films adhere well to the substrate, indicating no considerable internal stress. The initial high hardness is attributed to a columnar microstructure consisting of crystalline (Ti,Al)B-2 columns separated by an amorphous B matrix. The observed age hardening corresponds to phase separation within the (Ti,Al)B-2 columns including the formation of Ti-deficient crystallites within the grain interior upon annealing.
|
|
| 3. |
- Mockuté, Aurelija, et al.
(författare)
-
Synthesis and characterization of (Ti1-xAlx)B2+Delta thin films from combinatorial magnetron sputtering
- 2019
-
Ingår i: Thin Solid Films. - : ELSEVIER SCIENCE SA. - 0040-6090 .- 1879-2731. ; 669, s. 181-187
-
Tidskriftsartikel (refereegranskat)abstract
- (Ti1-xAlx)B2+Delta films with a lateral composition gradient of x = [0.30-0.66] and Delta = [0.07-1.22] were deposited on an Al2O3 wafer by dual magnetron sputtering at 400 degrees C from sintered TiB2 and AlB2 targets. Composition analysis indicates that higher Ti:Al ratios favor overstoichiometry in B and a reduced incorporation of O. Transmission electron microscopy reveals distinctly different microstructures of Ti- and Al-rich compositions, with formation of characteristic conical growth features for the latter along with a lower degree of crystallinity and significantly less tissue phase from B segregation at the grain boundaries. For Al-rich films, phase separation into Ti- and Al-rich diboride nanometer-size domains is observed and interpreted as surface-initiated spinodal decomposition. The hardness of the films ranges from 14 to 28 GPa, where the higher values were obtained for the Ti-rich regions of the metal boride.
|
|