| 1. |
- Persson, Johanna, 1980-, et al.
(författare)
-
Birch xylan grafted with pla branches of predictable length
- 2012
-
Ingår i: BioResources. - 1930-2126. ; 7:3, s. 3640-3655
-
Tidskriftsartikel (refereegranskat)abstract
- Birch xylan (4-O-methylglucuronoxylan) isolated from a kraft cooking liquor was delignified and grafted with polylactide of predictable branch length. This graft copolymerization resulted in very high total yields, greater than 90%, and with less than 10% polylactide homopolymer byproducts. Mild reaction conditions (40 degrees C, 5 to 120 minutes) were used, which was believed to limit transesterification reactions and thus make it possible to reach good predictability of the polylactide branch length. The thermal properties of the polylactide-grafted xylan depended on the branch length. Short branches resulted in fully amorphous materials with a glass transition temperature of about 48 to 55 degrees C, whereas long polylactide branches resulted in semi-crystalline materials with melting points of about 130 degrees C. Using mixtures of L-lactide and D/L-lactide in the monomer feed further altered the thermal properties. The degradation temperatures of the polylactide-grafted xylans were higher than that of the unmodified xylan, with degradation temperatures of about 300 degrees C and 250 degrees C, respectively. Tensile testing showed increased elongation at break with increasing branch length. The proposed method thus enables tailor-making of copolymers with specific thermal and mechanical properties.
|
|
| 2. |
- Persson, Johanna, et al.
(författare)
-
Modification of birch xylan by lactide-grafting
- 2012
-
Ingår i: Nordic Pulp & Paper Research Journal. - : Walter de Gruyter GmbH. - 0283-2631 .- 2000-0669. ; 27:3, s. 518-524
-
Tidskriftsartikel (refereegranskat)abstract
- 4-O-methylglucuronoxylan, isolated by ultrafiltration from a birch kraft cooking liquor, was delignified and subsequently modified by grafting lactide-chains onto the hydroxyl groups via ring opening polymerization with L-lactide. The structures and average molar masses of the lactide-grafted xylan polymers were characterised by NMR and SEC respectively. By varying the lactide-to-xylan feed ratio, graft polymers with different graft levels were synthesized. The degree of substitution of the hydroxyls in the xylan back-bone ranged from 0.7 to 1.7 with lactide side-chains having an average length of 1.2 to 2.5 lactide units. The side-chain length and degree of substitution influenced the hydrophobicity, thermal properties and tensile strength properties. A glass transition could be detected for lactide-grafted xylan polymers with lactide chains longer than 1.8 lactide units. Solution-cast thin films prepared from lactide-grafted xylans exhibited strong tensile strength and high modulus with decreasing strength and increasing elongation at break as the lactide chain length was increased.
|
|
| 3. |
|
|
| 4. |
- Albertsson, Ann-Christine, et al.
(författare)
-
Wood hydrolysates turned valuable
- 2012
-
Ingår i: Abstracts of Papers of the American Chemical Society. - 0065-7727. ; 243
-
Tidskriftsartikel (övrigt vetenskapligt/konstnärligt)
|
|
| 5. |
|
|
| 6. |
- Edlund, Ulrica, et al.
(författare)
-
Positron Lifetime Reveals the Nano Level Packing in Complex Polysaccharide-Rich Hydrolysate Matrixes
- 2012
-
Ingår i: Analytical Chemistry. - : American Chemical Society (ACS). - 0003-2700 .- 1520-6882. ; 84:8, s. 3676-3681
-
Tidskriftsartikel (refereegranskat)abstract
- Positron annihilation lifetime spectroscopy (PALS) was used to quantify the free volume and molecular packing in hydrolysate and hemicellulose-based barriers films, derived from process streams during wood processing operations. These hydrolysate films, comprising a fair share of lignin coexisting with poly- and oligo-saccharides, have very low but variable oxygen permeability but differ among themselves with respect to barrier performance as well as molecular weight, degree of branching, and monosaccharide residue main chain composition. From PALS measurements on hydrolysates, the free volume hole radius (r(h)), radius distributions (n(r(h))), volume-weighted hole sizes ((v)), and hole volume distributions (g(v(h))) were calculated showing that the hydrolysate matrixes are very densely packed with small holes. The results show a clear relationship between hydrolysate molecular architecture and composition, the nanolevel molecular packing, and the ability of suppressing the diffusion of oxygen through the film.
|
|
| 7. |
|
|
| 8. |
|
|
| 9. |
- Agfors, Gunnar, et al.
(författare)
-
KEMI : den gränslösa vetenskapen
- 2011
-
Bok (populärvet., debatt m.m.)abstract
- Kemi – handlar inte det bara om farliga ämnen och onödiga tillsatser? Det är kanske bildenmånga har av kemi, men faktum är att utan kemi skulle vi inte ha det höga välstånd vi har i dag.Tack vare kemisk kunskap har vi tillgång till läkemedel som botar sjukdomar och lindrar smärta– med hjälp av syntetiska antibiotika kan infektionssjukdomar som tidigare var dödliga botas,magsår kan behandlas utan dyra och plågsamma operationer och många cancerformer kanframgångsrikt behandlas med syntetiska preparat. Konstgödsel och medel som hindrar skadeinsektergör att skördar kan ökas och svälten i världen därigenom begränsas. Tack vare kemin harvi även tillgång till alla de material vi behöver för att tillverka allt från kläder, rengöringsprodukteroch kosmetika till bilar, TV-apparater och reservdelar till kroppen. Det är genom kemisk syntes vikan framställa dessa och alla de övriga produkter vi behöver för vårt dagliga liv och det är keminsom visar vägen till hållbar produktion som utnyttjar förnybara råvaror och ger minimala mängderavfall. Kemisk kunskap är också oumbärlig för utveckling av nanoteknik och medicinskdiagnostik och andra till kemin angränsande områden. Kemin bidrar alltså till att finna lösningartill många av de komplexa globala problem vi står inför: hälsa, klimat, brist på råvaror, utnyttjandetav nya energikällor och tillgång till livsmedel för att föda jordens ökande befolkning. DET ÄR OM ALLT DETTA DEN HÄR BOKEN HANDLAR.
|
|
| 10. |
- Albertsson, Ann-Christine
(författare)
-
CELL 104-Renewable and/or degradable polymers
- 2007
-
Ingår i: Abstracts of Papers of the American Chemical Society. - : AMER CHEMICAL SOC. - 0065-7727. ; 233, s. 796-796
-
Tidskriftsartikel (övrigt vetenskapligt/konstnärligt)
|
|