| 1. |
- Mahade, Satyapal, 1987-, et al.
(författare)
-
Incorporation of graphene nano platelets in suspension plasma sprayed alumina coatings for improved tribological properties
- 2021
-
Ingår i: Applied Surface Science. - : Elsevier BV. - 0169-4332 .- 1873-5584. ; 570
-
Tidskriftsartikel (refereegranskat)abstract
- Graphene possesses high fracture toughness and excellent lubrication properties, which can be exploited to enhance tribological performance of coating systems utilized to combat wear. In this work, suspension plasma spray (SPS) process was employed to deposit a composite, graphene nano-platelets (GNP) incorporated alumina coating. For comparison, monolithic alumina was also deposited utilizing identical spray conditions. The as-deposited coatings were characterized in detail for their microstructure, porosity content, hardness, fracture toughness and phase composition. Raman analysis of the as-deposited composite coating confirmed retention of GNP. The composite coating also showed good microstructural integrity, comparable porosity, higher fracture toughness and similar alumina phase composition as the monolithic alumina coating. The as-deposited coatings were subjected to dry sliding wear tests. The GNP incorporated composite coating showed lower CoF and lower specific wear rate than the pure alumina coating. Additionally, the counter surface also showed a lower wear rate in case of the composite coating. Post-wear analysis performed by SEM/EDS showed differences in the coating wear track and in the ball wear track of monolithic and composite coatings. Furthermore, Raman analysis in the wear track of composite coating confirmed the presence of GNP. The micro-indentation and wear test results indicate that the presence of GNP in the composite coating aided in improving fracture toughness, lowering CoF and specific wear rate compared to the monolithic coating. Results from this work demonstrated retention of GNP in an SPS processed coating, which can be further exploited to design superior wear-resistant coatings.
|
|
| 2. |
- Åkerfeldt, Maria, 1982, et al.
(författare)
-
Textile piezoelectric sensors – melt spun bi-component poly(vinylidene fluoride) fibres with conductive cores and poly(3,4-ethylene dioxythiophene)-poly(styrene sulfonate) coating as the outer electrode
- 2014
-
Ingår i: Fashion and Textiles. - : Springer Science and Business Media LLC. - 2198-0802. ; 1:1
-
Tidskriftsartikel (refereegranskat)abstract
- The work presented here addresses the outer electroding of a fully textile piezoelectric strain sensor, consisting of bi-component fibre yarns of β-crystalline poly(vinylidene fluoride) (PVDF) sheath and conductive high density polyethylene (HDPE)/carbon black (CB) core as insertions in a woven textile, with conductive poly(3,4-ethylene dioxythiophene)-poly(styrene sulfonate) (PEDOT:PSS) coatings developed for textile applications. Two coatings, one with a polyurethane binder and one without, were compared for the application and evaluated as electrode material in piezoelectric testing, as well as tested for surface resistivity, tear strength, abrasion resistance and shear flexing. Both coatings served their function as the outer electrodes in the system and no difference in this regard was detected between them. Omission of the binder resulted in a surface resistivity one order of magnitude less, of 12.3 Ω/square, but the surface resistivity of these samples increased more upon abrasion than the samples coated with binder. The tear strength of the textile coated with binder decreased with one third compared to the uncoated substrate, whereas the tear strength of the coated textile without binder increased with the same amount. Surface resistivity measurements and scanning electron microscopy (SEM) images of the samples subjected to shear flexing showed that the coatings without the binder did not withstand this treatment, and that the samples with the binder managed this to a greater extent. In summary, both of the PEDOT:PSS coatings could be used as outer electrodes of the piezoelectric fibres, but inclusion of binder was found necessary for the durability of the coating.
|
|
| 3. |
- Xu, Jinghao, et al.
(författare)
-
Short-term creep behavior of an additive manufactured non-weldable Nickel-base superalloy evaluated by slow strain rate testing
- 2019
-
Ingår i: Acta Materialia. - : Elsevier BV. - 1359-6454 .- 1873-2453. ; 179, s. 142-157
-
Tidskriftsartikel (refereegranskat)abstract
- Additive manufacturing (AM) of high γ′ strengthened Nickel-base superalloys, such as IN738LC, is of high interest for applications in hot section components for gas turbines. The creep property acts as the critical indicator of component performance under load at elevated temperature. However, it has been widely suggested that the suitable service condition of AM processed IN738LC is not yet fully clear. In order to evaluate the short-term creep behavior, slow strain rate tensile (SSRT) tests were performed. IN738LC bars were built by laser powder-bed-fusion (L-PBF) and then subjected to hot isostatic pressing (HIP) followed by the standard two-step heat treatment. The samples were subjected to SSRT testing at 850 °C under strain rates of 1 × 10−5/s, 1 × 10−6/s, and 1 × 10−7/s. In this research, the underlying creep deformation mechanism of AM processed IN738LC is investigated using the serial sectioning technique, electron backscatter diffraction (EBSD), transmission electron microscopy (TEM). On the creep mechanism of AM polycrystalline IN738LC, grain boundary sliding is predominant. However, due to the interlock feature of grain boundaries in AM processed IN738LC, the grain structure retains its integrity after deformation. The dislocation motion acts as the major accommodation process of grain boundary sliding. Dislocations bypass the γ′ precipitates by Orowan looping and wavy slip. The rearrangement of screw dislocations is responsible for the formation of subgrains within the grain interior. This research elucidates the short-creep behavior of AM processed IN738LC. It also shed new light on the creep deformation mechanism of additive manufactured γ′ strengthened polycrystalline Nickel-base superalloys.
|
|
| 4. |
- Grolig, Jan Gustav, 1986
(författare)
-
Coated Ferritic Stainless Steels as Interconnects in Solid Oxide Fuel Cells - Material Development and Electrical Properties
- 2015
-
Doktorsavhandling (övrigt vetenskapligt/konstnärligt)abstract
- Solid oxide fuel cells (SOFCs) are attracting increasing interest as devices with potentialuses in decentralized and clean electricity and heat production. Several challengeswith respect to materials have to be overcome to achieve efficiencies and life-spansthat are sufficient for long-term applications.An important element of an SOFC stack is the interconnect component, which connectstwo adjacent fuel cell elements. Interconnects, which are commonly composedof ferritic stainless steels, have to be corrosion-resistant, mechanically stable and costoptimized.This work aimed to investigate economic solutions for interconnect materials and tounderstand the underlying mechanisms of degradation and electrical conduction ofthese materials. Mainly two substrates, a commercially available steel (AISI 441) anda ferritic stainless steel that was optimized for an SOFC application (Sandvik SanergyHT) were combined with different barrier coatings and exposed to a cathode-sideatmosphere. A method was developed that allows for the electrical characterizationof promising material systems and model alloys, thereby facilitating a fundamentalunderstanding of the dominant electrical conduction processes linked to the oxidescales that grow on interconnects. The AISI 441 steel coated with reactive elementsand cobalt showed good corrosion and chromium evaporation profiles, while AISI 441coated with cerium and cobalt also had promising electrical properties. The SanergyHT steel was examined with coatings of copper and iron and copper and manganese,respectively. The corrosion and chromium evaporation profiles of Sanergy HT wereimproved by coating with copper and iron. The copper and iron-coated Sanergy HTshowed lower area specific resistance values than cobalt-coated Sanergy HT. Chromia,which is the main constituent of oxide scales, was synthesized using differentmethods. The electrical properties of chromia were found to be sensitive to not onlyimpurities, but also heat treatment. Finally the electrical properties of cobalt- andcobalt cerium-coated Sanergy HT steels were investigated. It was revealed that theaddition of cerium improved the conductivity of the interconnect by both slowingdown chromia growth and preventing the outward diffusion of iron into the spinel.
|
|
| 5. |
- Duan, Shanghong, 1992, et al.
(författare)
-
Determination of transverse and shear moduli of single carbon fibres
- 2020
-
Ingår i: Carbon. - : Elsevier BV. - 0008-6223 .- 1873-3891. ; 158C, s. 772-782
-
Tidskriftsartikel (refereegranskat)abstract
- Carbon fibres are extensively used for their high specific mechanical properties. Exploiting their high axial stiffness and strength, they are employed to reinforce polymer matrix materials in advanced composites. However, carbon fibres are not isotropic. Data of the elastic properties in the other directions of the fibres are still largely unknown. Furthermore, standardised methods to characterise these properties are lacking. In the present work, we propose a methodology to determine the transverse and shear moduli of single carbon fibres. An experimental procedure is developed to fabricate high-quality, flat fibre cross-sections in both longitudinal and transverse directions using Focused Ion Beam, which gives full control of the specimen geometry. Indentation modulus on those surfaces are obtained using both Atomic Force Microscopy (AFM) and nanoindentation tests. Hysteresis was found to occur in the nanoindentation tests. The hysteresis response was due to nano-buckling and reversible shear deformation of the carbon crystals. For this reason, indentation tests using AFM is recommended. From the AFM indentation tests the transverse and shear moduli of three different carbon fibres (IMS65, T800 and M60J) are successfully determined.
|
|
| 6. |
- Johansen, Marcus, 1994, et al.
(författare)
-
Mapping nitrogen heteroatoms in carbon fibres using atom probe tomography and photoelectron spectroscopy
- 2021
-
Ingår i: Carbon. - : Elsevier BV. - 0008-6223. ; 179, s. 20-27
-
Tidskriftsartikel (refereegranskat)abstract
- Carbon fibres show great potential as multifunctional negative electrode for novel structural battery composites – a rechargeable electrochemical cell with structural function. The electrochemical performance of carbon materials can be enhanced with nitrogen heteroatoms, which conveniently are inherent in polyacrylonitrile (PAN)-based carbon fibres. However, it is not fully understood how the electrochemical performance is governed by microstructure and composition of the carbon fibres, particularly the distribution and chemical states of nitrogen heteroatoms. Here we reveal the atom-by-atom three-dimensional spatial distribution and the chemical states of nitrogen in three PAN-carbon fibre types (M60J, T800 and IMS65), using atom probe tomography (APT) and synchrotron hard X-ray photoelectron spectroscopy (HAXPES), and correlate the results to electrochemical performance. The findings pave the way for future tailoring of carbon fibre microstructure for multifunctional applications.
|
|
| 7. |
- Johansen, Marcus, 1994
(författare)
-
Microstructure of Carbon Fibres for Multifunctional Composites: 3D Distribution and Configuration of Atoms
- 2021
-
Licentiatavhandling (övrigt vetenskapligt/konstnärligt)abstract
- Lightweight energy storage is a must for increased driving range of electric vehicles. “Mass-less” energy storage can be achieved by directly storing energy in structural components. In such multifunctional devices called structural composite batteries, carbon fibres carry mechanical load and simultaneously act as negative battery electrode by hosting lithium ions in its microstructure. Little is known of how the microstructure of carbon fibres is optimised for multifunctionality, and deeper understanding of the configuration and the distribution of atoms in carbon fibres is needed. Here synchrotron hard X-ray photoelectron spectroscopy and atom probe tomography are used to reveal the chemical states and three-dimensional distribution of atoms in commercial carbon fibres. This thesis presents the first ever guide for how to perform atom probe tomography on carbon fibres, and the first ever three-dimensional atomic reconstruction of a carbon fibre. The results show that the chemical states and distribution of nitrogen heteroatoms in carbon fibres affect the electrochemical performance of the fibres. Carbon fibres performed electrochemically better with higher amount of nitrogen with pyridinic and pyrrolic configurations. Additionally, the nitrogen concentration varies throughout the carbon fibre, which may suggest that the electrochemical properties also vary throughout the carbon fibre. The knowledge provided by this thesis can lead to future carbon fibre designs with enhanced electrochemical performance for multifunctional applications.
|
|
| 8. |
- Chen, Zhe, et al.
(författare)
-
Nano-scale characterization of white layer in broached Inconel 718
- 2017
-
Ingår i: Materials Science & Engineering A: Structural Materials: Properties, Microstructure and Processing. - Amsterdam : Elsevier BV. - 0921-5093 .- 1873-4936. ; 684, s. 373-384
-
Tidskriftsartikel (refereegranskat)abstract
- The formation mechanism of white layers during broaching and their mechanical properties are not well investigated and understood to date. In the present study, multiple advanced characterization techniques with nano-scale resolution, including transmission electron microscopy (TEM), transmission Kikuchi diffraction (TKD), atom probe tomography (APT) as well as nano-indentation, have been used to systematically examine the microstructural evolution and corresponding mechanical properties of a surface white layer formed when broaching the nickel-based superalloy Inconel 718.TEM observations showed that the broached white layer consists of nano-sized grains, mostly in the range of 20–50 nm. The crystallographic texture detected by TKD further revealed that the refined microstructure is primarily caused by strong shear deformation. Co-located Al-rich and Nb-rich fine clusters have been identified by APT, which are most likely to be γ′ and γ′′ clusters in a form of co-precipitates, where the clusters showed elongated and aligned appearance associated with the severe shearing history. The microstructural characteristics and crystallography of the broached white layer suggest that it was essentially formed by adiabatic shear localization in which the dominant metallurgical process is rotational dynamic recrystallization based on mechanically-driven subgrain rotations. The grain refinement within the white layer led to an increase of the surface nano-hardness by 14% and a reduction in elastic modulus by nearly 10% compared to that of the bulk material. This is primarily due to the greatly increased volume fraction of grain boundaries, when the grain size was reduced down to the nanoscale.
|
|
| 9. |
- Dimitrios, Nikas, et al.
(författare)
-
Effect of annealing on microstructure in railway wheel steel
- 2022
-
Ingår i: 42Nd Riso International Symposium On Materials Science. - : Institute of Physics Publishing (IOPP). ; 1249
-
Konferensbidrag (refereegranskat)abstract
- Railway wheels are commonly made from medium carbon steels (similar to 0.55 wt.% C), heat treated to a near pearlitic microstructure with 5-10% pro-eutectoid ferrite. During the operation of freight trains, where block brakes are used, high thermal loads occur together with the high contact stresses, which combined can affect the mechanical properties of the material. In this study, the effects of annealing on local microstructure and mechanical properties in pearlitic railway wheel steel were investigated using electron microscopy and micro-hardness. It is found that after annealing at 650 degrees C, the room temperature hardness reduces about 25%, accompanied by significant spheroidization of cementite in the pearlitic colonies, though the size and the orientation gradients of the pearlitic colonies have not changed much. The relationship between the microstructural changes and the mechanical properties are discussed.
|
|
| 10. |
- Goel, Sneha, 1993-, et al.
(författare)
-
Effect of post-treatments under hot isostatic pressure on microstructural characteristics of EBM-built Alloy 718
- 2019
-
Ingår i: Additive Manufacturing. - : Elsevier BV. - 2214-8604 .- 2214-7810. ; 28, s. 727-737
-
Tidskriftsartikel (refereegranskat)abstract
- Electron beam melting (EBM) has emerged as an important additive manufacturing technique. In this study, Alloy 718 produced by EBM was investigated in as-built and post-treated conditions for microstructural characteristics and hardness. The post-treatments investigated were hot isostatic pressing (HIP) and combined HIP + heat treatment (HIP + HT) carried out as a single cycle inside the HIP vessel. Both the post-treatments resulted in significant decrease in defects inevitably present in the as-built material. The columnar grain structure of the as-built material was found to be maintained after post-treatment, with some sporadic localized grain coarsening noted. Although HIP led to complete dissolution of δ and γ′′ phase, stable NbC and TiN (occasionally present) particles were observed in the post-treated specimens. Significant precipitation of γ′′ phase was observed after HIP + HT, which was attributed to the two-step aging heat treatment carried out during HIP + HT. The presence of γ′′ phase or otherwise was correlated to the hardness of the material. While the HIP treatment resulted in drop in hardness, HIP + HT led to ‘recovery’ of the hardness to values exceeding those exhibited by the as-built material.
|
|