| 1. |
- Xu, Jinghao, et al.
(författare)
-
Short-term creep behavior of an additive manufactured non-weldable Nickel-base superalloy evaluated by slow strain rate testing
- 2019
-
Ingår i: Acta Materialia. - : Elsevier BV. - 1359-6454 .- 1873-2453. ; 179, s. 142-157
-
Tidskriftsartikel (refereegranskat)abstract
- Additive manufacturing (AM) of high γ′ strengthened Nickel-base superalloys, such as IN738LC, is of high interest for applications in hot section components for gas turbines. The creep property acts as the critical indicator of component performance under load at elevated temperature. However, it has been widely suggested that the suitable service condition of AM processed IN738LC is not yet fully clear. In order to evaluate the short-term creep behavior, slow strain rate tensile (SSRT) tests were performed. IN738LC bars were built by laser powder-bed-fusion (L-PBF) and then subjected to hot isostatic pressing (HIP) followed by the standard two-step heat treatment. The samples were subjected to SSRT testing at 850 °C under strain rates of 1 × 10−5/s, 1 × 10−6/s, and 1 × 10−7/s. In this research, the underlying creep deformation mechanism of AM processed IN738LC is investigated using the serial sectioning technique, electron backscatter diffraction (EBSD), transmission electron microscopy (TEM). On the creep mechanism of AM polycrystalline IN738LC, grain boundary sliding is predominant. However, due to the interlock feature of grain boundaries in AM processed IN738LC, the grain structure retains its integrity after deformation. The dislocation motion acts as the major accommodation process of grain boundary sliding. Dislocations bypass the γ′ precipitates by Orowan looping and wavy slip. The rearrangement of screw dislocations is responsible for the formation of subgrains within the grain interior. This research elucidates the short-creep behavior of AM processed IN738LC. It also shed new light on the creep deformation mechanism of additive manufactured γ′ strengthened polycrystalline Nickel-base superalloys.
|
|
| 2. |
- Chen, Zhe, et al.
(författare)
-
Nano-scale characterization of white layer in broached Inconel 718
- 2017
-
Ingår i: Materials Science & Engineering A: Structural Materials: Properties, Microstructure and Processing. - Amsterdam : Elsevier BV. - 0921-5093 .- 1873-4936. ; 684, s. 373-384
-
Tidskriftsartikel (refereegranskat)abstract
- The formation mechanism of white layers during broaching and their mechanical properties are not well investigated and understood to date. In the present study, multiple advanced characterization techniques with nano-scale resolution, including transmission electron microscopy (TEM), transmission Kikuchi diffraction (TKD), atom probe tomography (APT) as well as nano-indentation, have been used to systematically examine the microstructural evolution and corresponding mechanical properties of a surface white layer formed when broaching the nickel-based superalloy Inconel 718.TEM observations showed that the broached white layer consists of nano-sized grains, mostly in the range of 20–50 nm. The crystallographic texture detected by TKD further revealed that the refined microstructure is primarily caused by strong shear deformation. Co-located Al-rich and Nb-rich fine clusters have been identified by APT, which are most likely to be γ′ and γ′′ clusters in a form of co-precipitates, where the clusters showed elongated and aligned appearance associated with the severe shearing history. The microstructural characteristics and crystallography of the broached white layer suggest that it was essentially formed by adiabatic shear localization in which the dominant metallurgical process is rotational dynamic recrystallization based on mechanically-driven subgrain rotations. The grain refinement within the white layer led to an increase of the surface nano-hardness by 14% and a reduction in elastic modulus by nearly 10% compared to that of the bulk material. This is primarily due to the greatly increased volume fraction of grain boundaries, when the grain size was reduced down to the nanoscale.
|
|
| 3. |
- Xu, Jinghao, et al.
(författare)
-
On the strengthening and embrittlement mechanisms of an additively manufactured Nickel-base superalloy
- 2020
-
Ingår i: Materialia. - : Elsevier BV. - 2589-1529. ; 10
-
Tidskriftsartikel (refereegranskat)abstract
- The γ′ phase strengthened Nickel-base superalloy is one of the most significant dual-phase alloy systems for high-temperature engineering applications. The tensile properties of laser powder-bed-fused IN738LC superalloy in the as-built state have been shown to have both good strength and ductility compared with its post-thermal treated state. A microstructural hierarchy composed of weak texture, sub-micron cellular structures and dislocation cellular walls was promoted in the as-built sample. After post-thermal treatment, the secondary phase γ′ precipitated with various size and fraction depending on heat treatment process. For room-temperature tensile tests, the dominated deformation mechanism is planar slip of dislocations in the as-built sample while dislocations bypassing the precipitates via Orowan looping in the γ′ strengthened samples. The extraordinary strengthening effect due to the dislocation substructure in the as-built sample provides an addition of 372 MPa in yield strength. The results of our calculation are in agreement with experimental yield strength for all the three different conditions investigated. Strikingly, the γ′ strengthened samples have higher work hardening rate than as-built sample but encounter premature failure. Experimental evidence shows that the embrittlement mechanism in the γ′ strengthened samples is caused by the high dislocation hardening of the grain interior region, which reduces the ability to accommodate further plastic strain and leads to premature intergranular cracking. On the basis of these results, the strengthening micromechanism and double-edge effect of strength and ductility of Nickel-base superalloy is discussed in detail.
|
|
| 4. |
- Chen, Zhe, et al.
(författare)
-
Surface Integrity and Structural Stability of Broached Inconel 718 at High Temperatures
- 2016
-
Ingår i: Metallurgical and Materials Transactions. A. - : Springer. - 1073-5623 .- 1543-1940. ; 47A:7, s. 3664-3676
-
Tidskriftsartikel (refereegranskat)abstract
- The current study focused on the surface integrity issues associated with broaching of Inconel 718 and the structural stability of the broached specimen at high temperatures, mainly involving the microstructural changes and residual stress relaxation. The broaching operation was performed using similar cutting conditions as that used in turbo machinery industries for machining fir-tree root fixings on turbine disks. Thermal exposure was conducted at 723 K, 823 K, and 923 K (450 A degrees C, 550 A degrees C, and 650 A degrees C) for 30, 300, and 3000 hours, respectively. Surface cavities and debris dragging, sub-surface cracks, high intensity of plastic deformation, as well as the generation of tensile residual stresses were identified to be the main issues in surface integrity for the broached Inconel 718. When a subsequent heating was applied, surface recrystallization and alpha-Cr precipitation occurred beneath the broached surface depending on the applied temperature and exposure time. The plastic deformation induced by the broaching is responsible for these microstructural changes. The surface tension was completely relaxed in a short time at the temperature where surface recrystallization occurred. The tensile layer on the sub-surface, however, exhibited a much higher resistance to the stress relief annealing. Oxidation is inevitable at high temperatures. The study found that the surface recrystallization could promote the local Cr diffusion on the broached surface.
|
|
| 5. |
- Pant, Prabhat, 1990-, et al.
(författare)
-
Mapping of residual stresses in as-built Inconel 718 fabricated by laser powder bed fusion : A neutron diffraction study of build orientation influence on residual stresses
- 2020
-
Ingår i: Additive Manufacturing. - : Elsevier B.V.. - 2214-8604 .- 2214-7810. ; 36
-
Tidskriftsartikel (refereegranskat)abstract
- Manufacturing of functional (ready to use) parts with the powder bed fusion method has seen an increase in recent times in the field of aerospace and in the medical sector. Residual stresses (RS) induced due to the process itself can lead to defects like cracks and delamination in the part leading to the inferior quality of the part. These RS are one of the main reasons preventing the process from being adopted widely. The powder bed methods have several processing parameters that can be optimized for improving the quality of the component, among which, build orientation is one. In this current study, influence of the build orientation on the residual stress distribution for the Ni-based super-alloy Inconel 718 fabricated by laser-based powder bed fusion method is studied by non- destructive technique of neutron diffraction at selected cross-sections. Further, RS generated in the entire part was predicted using a simplified layer by layer approach using a finite element (FE) based thermo-mechanical numerical model. From the experiment, the part printed in horizontal orientation has shown the least amount of stress in all three directions and a general tendency of compressive RS at the center of the part and tensile RS near the surface was observed in all the samples. The build with vertical orientation has shown the highest amount of RS in both compression and tension. Simplified simulations results are in good agreement with the experimental value of the stresses. © 2020 The Authors
|
|
| 6. |
- Saarimäki, Jonas, et al.
(författare)
-
Anisotropy effects during dwell-fatigue caused by δ-phase orientation in forged Inconel 718
- 2017
-
Ingår i: Materials Science & Engineering A: Structural Materials: Properties, Microstructure and Processing. - : Elsevier BV. - 0921-5093 .- 1873-4936. ; 692, s. 174-181
-
Tidskriftsartikel (refereegranskat)abstract
- Inconel 718 is a commonly used superalloy for turbine discs in the gas turbine industry. Turbine discs are often subjected to dwell-fatigue as a result of long constant load cycles. The effect of anisotropy on dwell-fatigue cracking in forged turbine discs have not yet been thoroughly investigated. Crack propagation behaviour was characterised using compact tension (CT) samples cut in different orientations from a real turbine disc forging. Samples were also cut in two different thicknesses in order to investigate the influence of plane strain and plane stress condition on the crack propagation rates. The samples were subjected to dwell-fatigue tests at 550 °C with 90 s or 2160 s dwell-times at maximum load. Microstructure characterisation was done using scanning electron microscopy (SEM) techniques such as electron channelling contrast imaging (ECCI), electron backscatter diffraction (EBSD), and light optical microscopy (LOM). The forged alloy exhibits strong anisotropic behaviour caused by the non-random δ-phase orientation. When δ-phases were oriented perpendicular compared to parallel to the loading direction, the crack growth rates were approximately ten times faster. Crack growth occurred preferably in the interface between the γ-matrix and the δ-phase.
|
|
| 7. |
- Saarimäki, Jonas, et al.
(författare)
-
3D Residual Stresses in Selective Laser Melted Hastelloy X
- 2017
-
Ingår i: Residual Stresses 2016: ICRS-10, Materials Research Proceedings 2 (2016). - : Materials Research Forum LLC. ; , s. 73-78
-
Konferensbidrag (refereegranskat)abstract
- 3D residual stresses in as manufactured EOS NickelAlloy HX, produced by laser powder bed additive manufacturing, are analysed on the surface closest to the build-plate. Due to the severe thermal gradient produced during the melting and solidification process, profound amounts of thermal strains are generated. Which can result in unwanted geometrical distortion and effect the mechanical properties of the manufactured component. Measurements were performed using a four-circle goniometer Seifert X-ray machine, equipped with a linear sensitive detector and a Cr-tube. Evaluation of the residual stresses was conducted using sin2ψ method of the Ni {220} diffraction peak, together with material removal technique to obtain in-depth profiles. An analysis of the material is reported. The analysis reveals unwanted residual stresses, and a complicated non-uniform grain structure containing large grains with multiple low angle grain boundaries together with nano-sized grains. Grains are to a large extent, not equiaxed, but rather elongated.
|
|
| 8. |
- Chen, Zhe, et al.
(författare)
-
Surface Integrity and Fatigue Performance of Inconel 718 in Wire Electrical Discharge Machining
- 2016
-
Ingår i: 3RD CIRP CONFERENCE ON SURFACE INTEGRITY. - : Elsevier BV. ; , s. 307-310
-
Konferensbidrag (refereegranskat)abstract
- This paper presents a study to characterize the surface integrity in wire electrical discharge machining (EDM) of Inconel 718 and investigate its effect on the fatigue performance of the alloy in a four-point bending fatigue mode at room temperature. The EDM process generates a rough recast surface with multi-types of defects. Surface craters, micro-cracks and micro-voids within the recast layer have been found to be most detrimental from the point of view of fatigue as they could provide many preferential initiation sites for fatigue cracks. As a consequence, the specimens with an EDM cut surface show an approximately 30% decrease in fatigue life compared to those with a polished surface, and multiple crack origins were observed on the fracture surface. The high tensile residual stresses generated on the EDM cut surface, on the other hand, are also believed to be partly responsible for the loss in fatigue life of the alloy machined by EDM.
|
|
| 9. |
- Gustafsson, David, et al.
(författare)
-
Influence of high temperature hold times on the fatigue crack propagation in Inconel 718
- 2011
-
Ingår i: International Journal of Fatigue. - : Elsevier. - 0142-1123 .- 1879-3452. ; 33:11, s. 1461-1469
-
Tidskriftsartikel (refereegranskat)abstract
- High temperature fatigue crack growth in Inconel 718 has been studied at the temperatures 450 degrees C, 500 degrees C, 550 degrees C and 650 degrees C. The tests were conducted both without hold times and with hold times of different lengths and with a mix of both. Focus has been on quantifying the effect the hold time has upon the crack growth rate and how much it damages the material. Furthermore, it has been investigated how this damage influences the actual cracking behavior, i.e. where in the loading cycle the damage contributes most to the crack growth. This damage is related to the concept of a damaged zone in front of the crack tip. The size of the damaged zone has been derived from the tests and a microscopy study to confirm the findings has also been carried out. It is found that the concept of a damaged zone can be a successful explanatory model for the observed crack growth behavior under high temperature hold time.
|
|
| 10. |
- Saarimäki, Jonas, et al.
(författare)
-
Time- and Cycle-Dependent Crack Propagation in Haynes 282
- 2016
-
Ingår i: Journal of Materials Science and Engineering. - : Elsevier. - 2161-6213 .- 0921-5093. ; 658, s. 463-471
-
Tidskriftsartikel (refereegranskat)abstract
- Haynes 282 is a promising superalloy candidate for several high-temperature applications in both aero and land-based gas turbine engines. To study the crack growth behaviour under time-dependent conditions relevant to such applications, a test program was carried out at room temperature up to 700 °C with conditions ranging from pure cyclic to sustained tensile loading. At 650 °C and high stress intensity factors the crack growth was fully time-dependent for dwell-times of 90 s and longer. At lower stress intensities, the behaviour was mainly controlled by the cyclic loading, even under dwell conditions. The behaviour under dwell-fatigue conditions was well described by a liner superposition model.
|
|