Load effect on scratch micro-mechanisms of solution strengthened Compacted Graphite Irons

• This study investigates the scratch load effect, from 100 to 2000 mN, on micro-mechanisms involved during scratching. A pearlitic and three ferritic Compacted Graphite Irons (CGI) solution strengthened through addition of 3.66, 4.09, and 4.59 Si wt% were investigated. Good correlation was observed between hardness measurements, tensile testing, and scratch results explaining the influence of matrix characteristics on scratch behaviour for investigated alloys. A significant matrix deformation, change in frictional force and scratch coefficient of friction was observed by increase in scratch load. In all cases, microscratch depth and width increased significantly with load increasing, however pearlitic CGI showed most profound deformation, while the maximum and minimum scratch resistances were observed for high-Si ferritic and pearlitic CGI alloys, respectively.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Maskinteknik -- Tribologi (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Mechanical Engineering -- Tribology (hsv//eng)

Nyckelord

CGI

Si solution-strengthening

Scratch testing

Deformation micro-mechanisms during scratching