Influence of alloying additions on microstructure and thermal properties in compact graphite irons

• Nineteen compacted graphite cast irons were investigated in order to determine how alloying additions affect the thermal transport properties and microstructure. All melts were based on one chemical composition and alloying elements were added to obtain melts with variation in magnesium, silicon, carbon, copper, tin, chromium and molybdenum. Increasing amounts of magnesium resulted in a further compaction of the graphite particles, reducing the thermal conductivity. Large amounts of silicon resulted in a fully ferritic metal matrix. Silicon also formed solid solution with iron which had a deteriorating effect on the thermal conductivity, i.e. the larger amount of silicon the lower the thermal conductivity. Copper and tin promoted formation of pearlite that had worse thermal properties compared to ferrite. Increasing amount of ferrite generally had a positive influence of the thermal conductivity. Chromium and molybdenum were carbide forming elements and carbides had a negative influence on the thermal conductivity.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering (hsv//eng)

Nyckelord

CGI

Thermal Conductivity

Microstructure

Alloying Addition

Materials science

Teknisk materialvetenskap

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)