Weldability of wrought Haynes 282 repair welded using manual gas tungsten arc welding
-
- Hanning, Fabian, 1988 (författare)
- Chalmers University of Technology, Department of Industrial and Materials Science, Gothenburg, Sweden,Chalmers tekniska högskola
-
- Andersson, Joel, 1981- (författare)
- Högskolan Väst,Avdelningen för svetsteknologi (SV),PTW,University West
-
(creator_code:org_t)
- 2017-08-19
- 2018
- Engelska.
-
Ingår i: Welding in the World. - : Springer Science and Business Media LLC. - 0043-2288 .- 1878-6669. ; 62:1, s. 39-45
- Relaterad länk:
-
https://doi.org/10.1...
-
visa fler...
-
https://link.springe...
-
http://publications.... (primary) (free)
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
https://research.cha...
-
https://research.cha...
-
visa färre...
Abstract
Ämnesord
Stäng
- The ability of the precipitation hardening superalloy Haynes® 282® to be repaired by multi-pass gas tungsten arc welding is investigated in this study. The repair welding has been carried out on forged discs having four pre weld heat treatments, resulting in different grain sizes and precipitate structures of the base material. Another set of discs has additionally been put through a post weld heat treatment. The tendency to form cracks in the heat-affected zone and the fusion zone has been investigated metallographically. No cracks in the base metal heat-affected zone were found,whereas solidification cracks were present in the weld fusion zone of all tested conditions. While high heat input during welding increased cracking by a factor of 1.5, none of the heat treatments had a measurable influence on the cracking behaviour. Voids with solid state crack-like appearance turned out tobe aluminium-rich oxides being present from the deposition of previous weld deposit layers.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Kompositmaterial och -teknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Composite Science and Engineering (hsv//eng)
Nyckelord
- Nickel alloys
- weldability
- repair
- GTA welding
- cracking
- Manufacturing and materials engineering
- Produktions- och materialteknik
- Production Technology
- Produktionsteknik
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas