Effect of water vapor on the oxidation behavior of HVAF-sprayed NiCr and NiCrAlY coatings

• Isothermal oxidation behavior of NiCr and NiCrAlY coatings deposited onto low alloy 16Mo3 steel by high-velocity air fuel (HVAF) process was investigated in 5% O-2+20% H2O+N-2 at 600 degrees C for 168h. Whereas NiCrAlY showed lower mass gain compared to NiCr, both coatings succeeded in maintaining the integrity with the substrate during the exposure without any breakaway oxidation. A thin Cr-rich oxide scale (Cr2O3) formed on NiCr, and a thin mixed oxide scale (Al2O3 with NiCr2O4) formed on NiCrAlY significantly increasing the oxidation protection in the presence of water vapor.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Kemiteknik -- Korrosionsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Chemical Engineering -- Corrosion Engineering (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

Nyckelord

NiCr

NiCrAlY

oxidation protection

thermal spray coating

water vapor

Manufacturing and materials engineering

Produktions- och materialteknik

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)