Chlorine-induced high-temperature corrosion and erosion-corrosion of HVAF and HVOF-sprayed amorphous Fe-based coatings

• Chlorine-induced high-temperature corrosion and erosion-corrosion behavior of amorphous Fe-based coatings sprayed by high velocity air-fuel (HVAF) and high velocity oxy-fuel (HVOF) techniques were investigated. The coated specimens were first exposed to isothermal high-temperature corrosion at 600 °C in ambient air with and without KCl. The exposed specimens were then subjected to alumina erodent. The as-sprayed HVAF coating showed a more compact and uniform microstructure with a higher hardness leading to higher corrosion and erosion-corrosion resistance. After erosion, all the coatings similarly exhibited a combined brittle/ductile damage to surface oxide scale that previously formed in the corrosive environment. The corrosion and erosion-corrosion behavior of the coatings primarily relied on the uniformity of coatings’ microstructure and distribution of alloying elements to form the protective oxide scale in the corrosive environment, which can resist against erodent in the erosive media. © 2019 Elsevier B.V.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)

Nyckelord

Air

Alloying elements

Alumina

Aluminum oxide

Chlorine

Corrosion resistance

Corrosive effects

Erosion

Fuels

High temperature corrosion

HVOF thermal spraying

Microstructure

Potassium compounds

Scale (deposits)

Sprayed coatings

Thermal spraying

Amorphous coating

Chlorine-induced high-temperature corrosion

Erosion - corrosions

HVAF

HVOF

Corrosion resistant coatings

Manufacturing and materials engineering

Produktions- och materialteknik

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)