Effects of surface finish on the initial oxidation of HVAF-sprayed NiCoCrAlY coatings

• Oxide scale formed on HVAF-sprayed NiCoCrAlY coatings and the effect of surface treatment were investigated by a multi-approach study combining photo-stimulated luminescence, microstructural observation and mass gain. The initial oxidationbehaviour of as-sprayed, polished and shot-peened coatings at 1000 °C is studied. Both polished and shot-peened coatings exhibited superior performance due to rapid formation of α-Al2O3 fully covering the coating and suppressing the growth of transient alumina, assisted by a high density of α-Al2O3 nuclei on surface treatment induced defects. Moreover, the fast development of a two-layer alumina scale consisting of an inward-grown inner α-Al2O3 layer and an outer layer transformed from outward-grown transient alumina resulted in a higher oxide growth rate of the as-sprayed coating.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering (hsv//eng)

Nyckelord

Oxidation

Transient to alpha transformation

Surface treatment

Polishing

Shot-peening

Photo-stimulated luminescence spectroscopy

Manufacturing and materials engineering

Produktions- och materialteknik

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)