Effect of arc suppression on the physical properties of low temperature dc magnetron sputtered tantalum thin films

Subrahmanyam, A. (författare)
Valleti, K. (författare)
Joshi, S. V. (författare)
visa fler...
Sundararajan, G. (författare)
visa färre...
American Vacuum Society, 2007
2007
Engelska.
Ingår i: Journal of Vacuum Science and Technology A: Vacuum, Surfaces and Films. - : American Vacuum Society. - 0734-2101 .- 1520-8559. ; 25:2, s. 378-382
  • Tidskriftsartikel (refereegranskat)
Abstract Ämnesord
Stäng  
  • Arcing is a common phenomenon in the sputtering process. Arcs and glow discharges emit electrons which may influence the physical properties of films. This article reports the properties of tantalum (Ta) thin films prepared by continuous dc magnetron sputtering in normal and arc-suppression modes. The substrate temperature was varied in the range of 300-673 K. The tantalum films were ∌1.8 ÎŒm thick and have good adherence to 316 stainless steel and single-crystal silicon substrates. The phase of the Ta thin film determines the electrical and tribological properties. The films deposited at 300 K using both methods were crystallized in a tetragonal structure (Β phase) with a smooth surface (grain size of ∌10 nm) and exhibited an electrical resistivity of ∌194 ÎŒ cm and a hardness of ∌20 GPa. When the substrate temperature was 473 K and higher, the arc-suppression mode appears to influence the films to crystallize in the α phase with a grain size of ∌40 nm, whereas the normal power mode gave mixed phases Β and α beyond 473 K, the arc-suppression mode yields larger grain sizes in the Ta thin films and the hardness decreases. These changes in the physical properties in arc-suppression mode are attributed to either the change in plasma characteristics or the energetic particle bombardment onto the substrate, or both. © 2007 American Vacuum Society.

Nyckelord

Low temperature effects; Magnetron sputtering; Physical properties; Single crystals; Stainless steel; Tantalum compounds
Arc suppression; Arc-suppression modes
Thin films

Publikations- och innehållstyp

ref (ämneskategori)
art (ämneskategori)

Hitta via bibliotek

Till lärosätets databas

Hitta mer i SwePub

Av författaren/redakt...
Subrahmanyam, A.
Valleti, K.
Joshi, S. V.
Sundararajan, G.
Artiklar i publikationen
Journal of Vacuu ...
Av lärosätet
Högskolan Väst

Sök utanför SwePub

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy