• Electron beam welding of forged Allvac 718Plus superalloy has been carried out without any visible cracks in weld cross-sections. Healed cracks in the heat affected zone were, however, seen in most cross-sections with the healing as well as the cracking believed to be due to the constitutional liquation of the δ-phase. The δ-phase undergoes constitutional liquation in the Heat Affected Zone (HAZ) and consequently decreases the ductility of the material and renders cracks in the HAZ but due to the large amount of eutectic liquid produced at the same time the healing of the opened cracks takes place.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Annan materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Other Materials Engineering (hsv//eng)

Nyckelord

Electron beam welding

Allvac 718Plus

Production Technology

Produktionsteknik

Produktions- och materialteknik

Manufacturing and materials engineering

Publikations- och innehållstyp

ref (ämneskategori)

kon (ämneskategori)