Repair welding of wrought superalloys : Alloy 718, Allvac 718Plus and Waspaloy

• The ability to weld repair three precipitation hardening superalloys, i.e. Alloy 718, Allvac 718Plus and Waspaloy, with gas tungsten arc welding, is compared in this study. Four different solution heat treatment conditions for each material were examined: Alloy 718 and Allvac 718Plus heat treated at 954uC–1 h, 982uC–1 h, 954uC–15 h and 1020uC–1 h and Waspaloy for 4 h at 996uC, 1010uC, 1040uC and at 1080uC. By metallography, the total number of cracks was evaluated in both the heat affected zone and the fusion zone, which made it possible to consistently rate the repair weldability of these three materials. Alloy 718 was significantly the best one, with Allvac 718Plus slightly better than Waspaloy. As expected, the solution heat treatment conditions only affected the heat affected zone cracking behaviour.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

Nyckelord

Heat affected zone cracking

strain age cracking

Production Technology

Produktionsteknik

Manufacturing and materials engineering

Produktions- och materialteknik

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)