- Knudsen effusion mass spectrometry was used to study vaporization processes and thermodynamic properties of twenty samples of chromium-containing slags in the CaO-MgO-Al2O3-Cr2O3-FeO-SiO 2 system in the temperature range 1850-2750 K. Tungsten cells were used and Cr2O3 solid was used as a reference material. The system was calibrated using liquid gold. As FeO was the first emanating vapor species, monitoring of the chromium-containing species could be carried out only after the complete vaporization of FeO. This, however, was found to have very little impact on the concentration of the slags investigated. During the measurements, the ion current intensities of CrO+ and CrO +2 species in the mass spectra of the vapor over the CaO-MgO-Al2O3-Cr2O3-FeO-SiO 2 samples were monitored and compared with those corresponding to solid Cr2O3. Data on the partial pressures of vapor species as well as the activities of Cr2O3 as a function of temperature were obtained. The results are expected to be valuable in the optimization of slag composition in high alloy steelmaking processes.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Nyckelord
- THERMODYNAMIC PROPERTIES; OXIDE MELTS; LIQUID; MIXTURES; CHROMIUM; CR2O3; FEO
- Metallurgical process and manufacturing engineering
- Metallurgisk process- och produktionsteknik
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas