Effect of Tin on Microstructure and Mechanical Properties of Compacted Graphite Iron
-
- Lyu, Yezhe, 1987- (författare)
- KTH,Tribologi,School of Materials Science and Engineering, Zhengzhou University, Zhengzhou, PR China
-
- Sun, Yufu (författare)
- School of Materials Science and Engineering, Zhengzhou University, Zhengzhou, PR China
-
- Liu, Shengxin (författare)
- School of Materials Science and Engineering, Zhengzhou University, Zhengzhou, PR China
-
visa fler...
-
- Zhao, Jingyu (författare)
- School of Materials Science and Engineering, Zhengzhou University, Zhengzhou, PR China
-
visa färre...
-
(creator_code:org_t)
- Maney Publishing, 2015
- 2015
- Engelska.
-
Ingår i: International Journal of Cast Metals Research. - : Maney Publishing. - 1364-0461 .- 1743-1336. ; 28:5, s. 263-268
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- This experiment investigated the effect of tin in an amount up to 0.121 wt.% on the microstructure and mechanical properties of compacted graphite iron (CGI). Graphite and matrix evolution was emphasized with the help of scanning electron microscopy. The results indicate that Sn in experimental range reduces graphite size. Pearlite quantity would increase with the increasing Sn and reaches over 95% when Sn is greater than 0.057 wt.%. Sn helps to narrow the lamellar spacing of pearlite from sorbitic pearlite (320 nm) to troostitic pearlite (83 nm) when Sn increases from 0.003 wt.% to 0.057 wt.%. Appropriate Sn addition promotes the tensile strength and impact toughness and the samples containing 0.057 wt.% Sn perform the highest values of 410.7 MPa and 9.11 J/cm2, respectively. Elongation declines with increasing Sn content because of the emergence of more pearlite. Samples containing excessive Sn experience sharply deterioration in mechanical properties due brittle cementite.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Maskinteknik -- Tribologi (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Mechanical Engineering -- Tribology (hsv//eng)
Nyckelord
- Compacted graphite iron
- Electron Microscopy
- Pearlite; Microstructure
- Mechanical properties
- Cementite