CdSe quantum dots/molecular cobalt catalyst co-grafted open porous NiO film as a photocathode for visible light driven H-2 evolution from neutral water

• An active noble-metal-free photocathode was fabricated by co-grafting water-soluble thioglycolic acid-stabilized CdSe quantum dots and a molecular cobaloxime catalyst (CoP) through chemical linkage on a p-type open porous NiO film. This photocathode was used as a working electrode in a three-electrode cell, which displayed a photocurrent density up to 110 mu A cm(-2) at an applied potential of 0 V vs. NHE in 0.1 M Na2SO4 solution at pH 6.8 upon visible light illumination. The comparative studies showed that the open porous NiO/CdSe electrode did display a higher photocurrent density than that exhibited by an analogous planar NiO/CdSe electrode made by doctor-blading a NiO paste. Long-time photoelectrolysis experiments revealed that about 83% of the photocurrent density remained after 3.5 h illumination at 0.2 V vs. NHE. The open porous NiO/CdSe/CoP photocathode showed a considerably better current density and photocatalytic stability compared to the so-far reported dye-or QD-sensitized NiO cathodes with a cobaloxime catalyst chemically attached or physically adsorbed on the electrode surface under similar conditions.

Ämnesord

NATURVETENSKAP  -- Kemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences (hsv//eng)

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)