Ferromagnetism above room temperature in nickel-tetracyanoethylene thin films
-
- Bhatt, Pramod (författare)
- Linköpings universitet,Ytors Fysik och Kemi,Tekniska högskolan
-
- Kanciurzewska, Anna (författare)
- Linköpings universitet,Ytors Fysik och Kemi,Tekniska högskolan
-
- Carlegrim, Elin (författare)
- Linköpings universitet,Ytors Fysik och Kemi,Tekniska högskolan
-
visa fler...
-
- Kapilashrami, Mukes (författare)
- KTH,Teknisk materialfysik,Division of Engineering Material Physics, Royal Institute of Technology, Stockholm, Sweden
-
- Belova, Lyubov M. (författare)
- KTH,Teknisk materialfysik,Division of Engineering Material Physics, Royal Institute of Technology, Stockholm, Sweden
-
- Rao, K. V. (författare)
- KTH,Teknisk materialfysik,Division of Engineering Material Physics, Royal Institute of Technology, Stockholm, Sweden
-
- Fahlman, Mats (författare)
- Linköpings universitet,Ytors Fysik och Kemi,Tekniska högskolan
-
visa färre...
-
(creator_code:org_t)
- Royal Society of Chemistry (RSC), 2009
- 2009
- Engelska.
-
Ingår i: Journal of Materials Chemistry. - : Royal Society of Chemistry (RSC). - 0959-9428 .- 1364-5501. ; 19:36, s. 6610-6615
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
https://urn.kb.se/re...
-
visa färre...
Abstract
Ämnesord
Stäng
- Room temperature ferromagnetic ordering is reported in Ni-tetracyanoethylene (TCNE) thin films fabricated on Au substrates using physical vapor deposition (PVD) under ultra high vacuum conditions. This technique enables the preparation of very clean films without having any kind of contamination from oxygen-containing species, solvents or precursor molecules. Film stoichiometry was obtained from X-ray photoelectron spectroscopy (XPS) measurements. XPS derived stoichiometry points to a similar to 1 : 2 ratio between Ni and TCNE resulting in Ni(TCNE)(x), x approximate to 2. No evidence of pure Ni metal in the in situ grown films was present in the XPS or the ultraviolet photoelectron spectroscopy (UPS) measurements within the detection limits of the techniques.
Nyckelord
- designer magnets
- organic magnets
- solid-solution
- TECHNOLOGY
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas