Stability of Poly(3,4-ethylene dioxythiophene) Materials Intended for Implants

• This study presents experiments designed to study the stability of the conducting polymer poly(3,4-ethylene dioxythiophene) (PEDOT), under simulated physiological conditions using phosphate-buffered saline (PBS) and hydrogen peroxide (H2O2) (0 01M) at 37 degrees C over a 5- to 6-week period Voltage pulsing in PBS was used as an additional test environment The influence of switching the counter ion used in electropolymerization from polystyrene sulphonate (PSS) to heparin was investigated Absorbance spectroscopy and cyclic voltammetry were used to evaluate the material properties Most of the samples in H2O2 lost both electroactivity and optical absorbance within the study period, but PEDOT.PSS was found slightly more stable than PEDOT heparin. Polymers were relatively stable in PBS throughout the study period, with around 80% of electroactivity remaining after 5 weeks, disregarding delamination, which was a significant problem especially for polymer on indium tin oxide substrates Voltage pulsing in PBS did not increase degradation. The counter ion influenced the time course of degradation in Oxidizing agents.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Medicinteknik -- Medicinsk laboratorie- och mätteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Medical Engineering -- Medical Laboratory and Measurements Technologies (hsv//eng)

Nyckelord

PEDOT

stability

degradation

conjugated polymers

neural prosthesis

Medical engineering

Medicinsk teknik

TECHNOLOGY

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)