Synthesis and characterization of surfactant-coated superparamagnetic monodispersed iron oxide nanoparticles
-
Kim, D. K. (författare)
-
Zhang, Y. (författare)
-
Voit, W. (författare)
-
visa fler...
-
Rao, K. V. (författare)
-
- Muhammed, Mamoun (författare)
- KTH,Materialvetenskap
-
visa färre...
-
(creator_code:org_t)
- 2001
- 2001
- Engelska.
-
Ingår i: Journal of Magnetism and Magnetic Materials. - 0304-8853 .- 1873-4766. ; 225:02-jan, s. 30-36
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Synthesis and coating of superparamagnetic monodispersed iron oxide nanoparticles was carried out by chemical solution method. Controlled co-precipitation technique was used to prevent undesirable critical oxidation of Fe2+. The obtained Fe3O4 nanoparticles were coated with sodium oleate. Low-held AC susceptibility and SQUID measurement show superparamagnetism with a blocking temperature around 150K, and almost immeasurable remanence and coercivity.
Nyckelord
- nanoparticles
- superparamagnetism
- surfactant
- coprecipitation
- ferrofluid
- magnetite particles
- dispersions
- alkaline
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas